Long glass fiber reinforced polyketone material and preparation method thereof

A technology of long glass fiber and polyketone, which is applied in the field of long glass fiber reinforced polyketone material and its preparation, can solve the problems of few literature reports, and achieve the effects of excellent mechanical properties, high production capacity, and good rigidity

Inactive Publication Date: 2018-03-13
HEFEI GENIUS NEW MATERIALS
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there are developments for other types of thermoplastics, there are still few relevant literature reports

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Long glass fiber reinforced polyketone material and preparation method thereof
  • Long glass fiber reinforced polyketone material and preparation method thereof
  • Long glass fiber reinforced polyketone material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Polyketone 45 parts,

[0027] Continuous glass fiber 15 parts,

[0028] Among them, polyketone is selected from Hyosung's high-end mobile brand Shell DP R1000, the melt flow rate is 90g / 10min, the test condition is 240℃, 2.16kg;

[0029] The continuous glass fiber is selected from continuous non-alkali glass fiber with a fiber diameter of 10 μm and a linear density of 1000 tex.

[0030] ⑴ Mixing preparation: Add 45 parts of polyketone into the high mixer, control the mixing temperature at 40°C, stop mixing after 2 minutes, and then add the mixed material into the barrel of the extruder;

[0031] ⑵Preparation of polyketone composite materials: using impregnation equipment for continuous fiber reinforced thermoplastic materials, adding polyketone resin into the twin-screw extruder for heating and melting, and extruding the melt into the impregnation mold connected to the head of the twin-screw extruder In the process, the continuous glass fiber enters the impregnation...

Embodiment 2

[0039]

[0040]

[0041] Among them, the polyketone selected from Korea Hyosung’s advanced flow grade is M130A, the melt flow rate is 200g / 10min, and the test condition is 240°C, 2.16kg;

[0042] The continuous glass fiber is selected from continuous alkali-free glass fiber, the fiber diameter is 22μm, and the linear density is 4800tex;

[0043] The main antioxidant is selected from antioxidant 1076;

[0044] Auxiliary antioxidant is selected from the antioxidant 697 of BASF;

[0045] The lubricant is selected from a mixture of silicones, polyethylene waxes and pentaerythritol stearate;

[0046] The stabilizer is aluminum phosphate treated with 0.5% PEG-600.

[0047] ⑴ Mixing preparation: first add aluminum phosphate into a small high mixer, and add PEG-600 with 0.5% weight fraction of aluminum phosphate while stirring. After adding, stir for another 5 minutes and take it out for use; Propylene, 0.5 parts of primary antioxidant, 0.3 parts of auxiliary antioxidant, and...

Embodiment 3

[0052]

[0053]

[0054] Among them, the polyketone is selected from Korea Hyosung's medium and low flow grade M630A, the melt flow rate is 6g / 10min, and the test condition is 240°C, 2.16kg;

[0055] The continuous glass fiber is selected from continuous non-alkali glass fiber, the fiber diameter is 17μm, and the linear density is 2400tex;

[0056] The main antioxidant is selected from antioxidant 1098;

[0057] Auxiliary antioxidant is selected from MD1024 of BASF;

[0058] The lubricant is selected from a mixture of ethylene bisstearamide EBS, calcium stearate, silicone and polyethylene wax.

[0059] ⑴ Mixing preparation; add 69.1 parts of polypropylene, 0.2 parts of primary antioxidant, 0.2 parts of auxiliary antioxidant, and 0.5 parts of lubricant into the high-speed mixer in sequence. The mixing temperature is controlled at 50 ° C. After mixing for 3 minutes Stop, then add the mixed material to the extruder barrel;

[0060] ⑵Preparation of polyketone composite ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of polymer materials, and in particular, relates to a long glass fiber reinforced polyketone material prepared from the following components in parts by weight: 45-85 parts of polyketone resin, 15-50 parts of continuous glass fibers, 0-0.5 part of a main antioxidant, 0-0.3 part of an auxiliary antioxidant, 0-1 part of a lubricant, and 0-5 parts of a stabilizer. With adopting of the long glass fiber reinforced polyketone material, the grain-sized dicing length of grains is 10-15 mm, fibers in the grains are in ordered arrangement in the resin along the grain-sized dicing direction, and the fiber length is equal to the grain length; the material also has excellent rigidity, impact toughness and good heat-resistant temperature, especially has excellent low-temperature impact properties, and has the advantages of simple design, low cost and high productivity.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a long glass fiber reinforced polyketone material and a preparation method thereof. Background technique [0002] Long glass fiber reinforced thermoplastics are a class of materials that have developed rapidly in recent years. Their most prominent advantages are high rigidity and strength, excellent heat resistance, creep resistance, dimensional stability, and long service life. There are significant differences between long glass fiber reinforced plastic particles and short glass fiber reinforced plastic particles. In short glass fiber reinforced plastics, due to the damage caused by the shearing action of the screw, the length of glass fiber is generally kept to about 0.2-1mm, while in long glass fiber reinforced plastics, the length of glass fiber can be kept to 3-6mm, which is short glass fiber. 10 times that of fiber reinforced plastics. [0003] At p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L73/00C08L83/04C08L23/06C08K7/14C08K13/06C08K9/08C08K3/32B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704C08K3/32C08K7/14C08K9/08C08K13/06C08K2003/327C08K2201/003C08L73/00C08L2201/08C08L2205/03C08L83/04C08L23/06C08K13/04
Inventor 杨桂生范继贤费彬吴安琪
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com