High-strength glass reinforced plastic

A glass fiber reinforced plastic, high-strength technology, applied in the field of glass fiber reinforced plastic, can solve the problems of reducing the high temperature resistance of epoxy glass fiber reinforced plastic composite materials, and achieve the effect of improving strength and suppressing the generation of smoke

Inactive Publication Date: 2018-03-09
成都双瑞暖通设备有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, there are low-molecular impurities such as free phenol in the epoxy FRP composite material prepared by the traditional method. The free low-molecular impurity will reduce the high temperature resistance of the epoxy FRP composite material. The long-term service temperature of epoxy polyester FRP composite materials in the field usually does not exceed 120°C

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A high-strength FRP, characterized in that: it consists of the following components in weight percent: 30 parts of unsaturated polyester resin, 10 parts of hydrogen peroxide, 1 part of potassium oxide, 1 part of phenol-modified tungsten hexachloride, 1 part of fuel, 2 parts of nano filler, 10 parts of glass fiber, 1 part of metal filler, 8 parts of magnesium hydroxide.

[0014] Preferably, the metal filler is one or more of copper powder, iron powder or tungsten powder with a fineness of 200 mesh.

[0015] Preferably, the nano-filler is at least one of nano-silicon dioxide or nano-calcium carbonate.

[0016] Preferably, the thickness of the FRP composite material is 13mm.

[0017] Preferably, the Shore hardness of the FRP composite material is 98D, the bending strength is 185MPa, and the impact strength is 260KJ / m2.

Embodiment 2

[0019] A high-strength FRP, characterized in that it consists of the following components in weight percentage: 40 parts of unsaturated polyester resin, 30 parts of hydrogen peroxide, 3 parts of potassium oxide, 3 parts of phenol-modified tungsten hexachloride, 5 parts of fuel, 4 parts of nano filler, 20 parts of glass fiber, 3 parts of metal filler, 10 parts of magnesium hydroxide.

[0020] Preferably, the metal filler is one or more of copper powder, iron powder or tungsten powder with a fineness between 500 mesh.

[0021] Preferably, the nano-filler is at least one of nano-silicon dioxide or nano-calcium carbonate.

[0022] Preferably, the thickness of the FRP composite material is 20mm.

[0023] Preferably, the Shore hardness of the FRP composite material is 108D, the bending strength is 195MPa, and the impact strength is 285KJ / m2.

Embodiment 3

[0025] A high-strength FRP, characterized in that it consists of the following components in weight percentage: 35 parts of unsaturated polyester resin, 20 parts of hydrogen peroxide, 2 parts of potassium oxide, 2 parts of phenol-modified tungsten hexachloride, 3 parts of fuel, 3 parts of nano filler, 15 parts of glass fiber, 2 parts of metal filler, 9 parts of magnesium hydroxide.

[0026] Preferably, the metal filler is one or more of copper powder, iron powder or tungsten powder with a fineness between 350 mesh.

[0027] Preferably, the nano-filler is at least one of nano-silicon dioxide or nano-calcium carbonate.

[0028] Preferably, the thickness of the FRP composite material is 17mm.

[0029] Preferably, the Shore hardness of the FRP composite material is 100D, the bending strength is 190MPa, and the impact strength is 275KJ / m2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Shore hardnessaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-strength FRP, which belongs to the technical field of FRP, and is characterized in that it consists of the following components in weight percent: 30-40 parts of unsaturated polyester resin, 10-30 parts of hydrogen peroxide, and 1-3 parts of potassium oxide 1-3 parts of phenol-modified tungsten hexachloride, 1-5 parts of flame retardant, 2-4 parts of nano filler, 10-20 parts of glass fiber, 1-3 parts of metal filler, 8-10 parts of magnesium hydroxide share. The beneficial effect of the present invention is: use unsaturated polyester resin and other auxiliary materials as curing system, use glass fiber yarn as reinforcing material, produce high-performance composite linear material, improve the strength of product through reasonable formula system; Magnesium is non-toxic and suppresses smoke production.

Description

technical field [0001] The invention relates to the technical field of glass fiber reinforced plastics, in particular to high-strength glass fiber reinforced plastics. Background technique [0002] Epoxy FRP composite materials are usually used in fields with high performance requirements, such as chemical industry, metallurgy and other fields. Traditional epoxy fiberglass composite materials usually mix epoxy resin with a certain proportion of ordinary phenolic resin as the body resin, and at the same time add some modifiers to the body resin to modify the body resin. Generally, there are low-molecular impurities such as free phenol in the epoxy FRP composite material prepared by the traditional method. The free low-molecular impurity will reduce the high temperature resistance of the epoxy FRP composite material. The long-term service temperature of epoxy polyester FRP composite materials in the field usually does not exceed 120 °C. SUMMARY OF THE INVENTION [0003] In...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/06C08K13/06C08K7/14C08K3/22C08K3/08C08K9/04C08K3/16C08K3/36C08K3/26
CPCC08K13/06C08K3/08C08K3/16C08K3/22C08K3/26C08K3/36C08K7/14C08K9/04C08K2003/085C08K2003/0856C08K2003/0887C08K2003/2224C08K2003/265C08K2201/011C08L67/06
Inventor 刘远明
Owner 成都双瑞暖通设备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap