A method for preparing YAG transparent ceramics by gel injection molding

A technology of gel injection molding and transparent ceramics, which is applied in the field of gel injection molding to prepare YAG transparent ceramics, which can solve the problems of slow gel molding and uneven dispersion

Active Publication Date: 2020-07-28
XUZHOU NORMAL UNIVERSITY
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In order to solve the problems of uneven dispersion and slow gel formation in the prior art, the present invention adopts a stirrer device powered by an electromechanical system, Isobam as a dispersant and a gelling agent, and a catalyst to control the gel rate. Stirring and mixing ceramic slurry under certain conditions to replace the common ball milling method can efficiently solve the heat generation in the ball milling process, and the equipment is simple and the process is controllable, which greatly improves the uniformity and dispersibility of the slurry, and the prepared high-quality The slurry is conducive to obtaining YAG transparent ceramics with good structure uniformity and high transmittance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing YAG transparent ceramics by gel injection molding
  • A method for preparing YAG transparent ceramics by gel injection molding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] A method for preparing YAG transparent ceramics by gel injection molding; the method includes the preparation of YAG ceramic slurry, vacuum defoaming, catalyst addition, injection into mold curing, demoulding, drying, debinding, and firing; specifically includes the following step:

[0027] Step 1. Follow Y 3 Al 5 o 12 The stoichiometric ratio of the molecular formula weighs Y 2 o 3 Powder, Al 2 o 3 The powder is used as a ceramic powder, and a sintering aid is added to obtain an oxide mixture;

[0028] Step 2: Premix the oxide mixture with balls and a solvent to form a premixed solution, and mix and ball mill for 15 to 24 hours to obtain a mixed slurry;

[0029] Step 3. After the mixed slurry is dried in an oven, calcined in a muffle furnace, and sieved to 100-200 mesh as raw material powder for gel injection molding;

[0030] Step 4, add raw material powder and defoamer to the Isobam solution, and stir with a stirrer at a constant temperature;

[0031] Step 5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of molding and manufacturing processes for transparent ceramic, and specifically relates to a method for preparing YAG transparent ceramic by gel casting.The method uses Isobam as a dispersing agent and a gelating agent, and adopts a system selected from the group consisting of a Ziegler-Natta catalyst system (a Ziegler-Natta catalyst), an ammonium persulfate-tetramethylethylenediamine (APS-TEMED) catalytic system and a 2,2-azo[2-(2-imidazoline-2-yl)propane]hydrochloride (AZIP.2HCl) catalytic system to control the rate of gelation and control the time of gel casting.

Description

technical field [0001] The invention belongs to the technical field of transparent ceramic molding and manufacturing technology, and in particular relates to a method for preparing YAG transparent ceramics by gel injection molding. Background technique [0002] Yttrium aluminum garnet (YAG for short) has a cubic structure, no birefringence effect, low high-temperature creep, excellent optical and mechanical properties, and is widely used in laser matrix gain materials, and can also be used to make high-temperature visible and infrared windows. Compared with YAG single crystal, YAG transparent ceramics can meet the large size and higher doping concentration required for the preparation of high-power lasers, so it has shown good application prospects in replacing YAG single crystal. The preparation of YAG transparent ceramics includes processes such as powder making, molding, sintering and machining. The purpose of the molding process is to obtain a compact green body with hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/505C04B35/622C04B35/638C04B35/64
CPCC04B35/505C04B35/622C04B35/638C04B35/64C04B2235/3206C04B2235/3217C04B2235/3418C04B2235/6022C04B2235/6562C04B2235/6567C04B2235/658C04B2235/6581C04B2235/662C04B2235/9653
Inventor 张乐姚庆蒋志刚魏帅高光珍王骋陈浩
Owner XUZHOU NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com