High-strength thick glass substrate and preparation method thereof

A thick glass and high-strength technology, applied in the field of glass manufacturing, can solve problems such as increased processing difficulty, increased number of bubbles, and faster hardening speed, so as to improve bending strength, mechanical properties, and good bending strength Effect

Inactive Publication Date: 2018-02-23
株洲醴陵旗滨玻璃有限公司 +1
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the production of high-strength glass at home and abroad is mainly through the improvement of Al in glass. 2 o 3 content, however with Al 2 o 3 As the content increases, the viscosity of the glass increases, the clarification effect decreases, the number of bubbles in the glass increases, the volume increases, the melting effect of the glass becomes worse, and the hardening speed becomes faster, and it is easy to produce ribs and streaks on the surface of the glass , while increasing the annealing difficulty of the glass
In general, with the Al in the glass 2 o 3 As the content increases, the mechanical properties and optical properties of the glass will decrease, and the processing difficulty will increase

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength thick glass substrate and preparation method thereof
  • High-strength thick glass substrate and preparation method thereof
  • High-strength thick glass substrate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of high-strength thick glass substrate of the present invention, this high-strength thick glass substrate is made up of the raw material of following percentage by weight: SiO 2 : 63%; Al 2 o 3 : 6%; B 2 o 3 : 2%; CaO: 8%; MgO: 4%; Na 2 O: 14%; K 2 O: 2%; Sb 2 o 3 :1%.

[0031] The preparation method of this high-strength thick glass substrate is as follows:

[0032] (1) First heat the empty crucible, when the crucible is heated to 1350°C-1450°C, add the mixture of the above-mentioned raw materials into the crucible in 5 batches, control the feeding temperature at 1350°C-1450°C, and feed in batches before and after The interval time is 30 minutes, and the total feeding time is 2 hours. After the feeding is completed, the temperature is raised to 1590 ° C ~ 1600 ° C to melt the materials to obtain glass liquid;

[0033](2) Carry out the first heat preservation of the molten glass obtained in step (1), the temperature of the first heat preservation is 1590...

Embodiment 2

[0036] A kind of high-strength thick glass substrate of the present invention, this high-strength thick glass substrate is made up of the raw material of following percentage by weight: SiO 2 : 60%; Al 2 o 3 : 7%; B 2 o 3 : 4%; CaO: 8%; MgO: 4%; Na 2 O: 14%; K 2 O: 2%; Sb 2 o 3 :1%.

[0037] The preparation method of this high-strength thick glass substrate is as follows:

[0038] (1) First heat the empty crucible, when the crucible is heated to 1350°C-1450°C, add the mixture of the above-mentioned raw materials into the crucible in 5 batches, control the feeding temperature at 1350°C-1450°C, and feed in batches before and after The interval time is 35 minutes, and the total feeding time is 2.3 hours. After the feeding is completed, the temperature is raised to 1590 ° C ~ 1600 ° C to melt the materials to obtain molten glass;

[0039] (2) Carry out the first heat preservation of the molten glass obtained in step (1), the temperature of the first heat preservation is 1...

Embodiment 3

[0042] A kind of high-strength thick glass substrate of the present invention, this high-strength thick glass substrate is made up of the raw material of following percentage by weight: SiO 2 : 57%; Al 2 o 3 : 8%; B 2 o 3 : 6%; CaO: 8%; MgO: 4%; Na 2 O: 14%; K 2 O: 2%; Sb 2 o 3 :1%.

[0043] The preparation method of this high-strength thick glass substrate is as follows:

[0044] (1) First heat the empty crucible, when the crucible is heated to 1350°C-1450°C, add the mixture of the above-mentioned raw materials into the crucible in 5 batches, control the feeding temperature at 1350°C-1450°C, and feed in batches before and after The interval time is 30 minutes, and the total feeding time is 2 hours. After the feeding is completed, the temperature is raised to 1590 ° C ~ 1600 ° C to melt the materials to obtain glass liquid;

[0045] (2) Carry out the first heat preservation of the molten glass obtained in step (1), the temperature of the first heat preservation is 159...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-strength thick glass substrate which comprises the following raw materials in percentage by weight: 56-63 percent of SiO2, 6-8 percent of Al2O3, 2-6 percent of B2O3, 8-9percent of CaO, 3-5 percent of MgO, 13-15 percent of Na2O, 1-3 percent of K2O, 0-1 percent of Sb2O3 and 0.1-1 percent of a clarifying agent. The invention further discloses a preparation method of the high-strength thick glass substrate. The high-strength thick glass substrate prepared by the preparation method disclosed by the invention is high in mechanical and optical properties, good in melting effect and low in processing difficulty.

Description

technical field [0001] The invention relates to the technical field of glass manufacturing, in particular to a glass substrate and a preparation method thereof. Background technique [0002] With the continuous improvement of living standards, people's requirements for the surrounding environment are also getting higher and higher. The interior and exterior decoration of buildings must not only be safe and energy-saving, but also beautiful. Hard high-strength thick glass or hard high-strength colored glaze thick glass and its composite products (such as colored glaze laminated glass, etc.) can meet the above requirements. At the same time, because the glazed glass can not only realize various patterns through silk screen, but also realize different colors through pigment blending, and give dynamic beauty with the change of light, which provides inspiration and support for architectural designers. Therefore, glazed glass is widely used in the architectural decoration industr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/091C03C1/00C03B19/02C03B25/00
CPCC03B19/02C03B25/00C03C1/004C03C3/091
Inventor 陈立新戴海波谢伟陈民生龙首昂龙冬瑶袁斌刘屹赵利王巍卿艳黄毅斌苏峰荣林荣茂肖秋玉杨燕参许绣山欧栋良谢庆添姜志成张志强余继荣李渊宋茜匡卓珺刘福乾
Owner 株洲醴陵旗滨玻璃有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com