Cardiomyocyte detection method based on inverse opal hydrogel and its application

A technology of anti-opal structure and cardiomyocytes, applied in the field of biomedical material research, to achieve the effect of easy-to-obtain, low-cost, and intuitive materials

Active Publication Date: 2020-06-16
SOUTHEAST UNIV
View PDF14 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the research and development of sensing materials with high sensitivity to detect the contractility and beating frequency of cardiomyocytes and the construction of stable detection technologies for the contractility and beating frequency of cardiomyocytes still face severe challenges.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cardiomyocyte detection method based on inverse opal hydrogel and its application
  • Cardiomyocyte detection method based on inverse opal hydrogel and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1 A kind of cardiomyocyte detection and application based on gelatin methacrylate (GelMA) inverse opal structure hydrogel

[0039] 1. Preparation of GelMA inverse opal hydrogel:

[0040] 1) Disperse the purified monodisperse silicon dioxide particles with a particle size of 300nm in an ethanol solution to obtain a silicon dioxide ethanol dispersion with a concentration of silicon dioxide particles of 20wt%;

[0041] 2) Deposit the silicon dioxide ethanol dispersion on the glass sheet to form a silicon dioxide photonic crystal template, and finally perform high-temperature calcination (500° C.) on the obtained photonic crystal template to obtain a photonic crystal template with better mechanical strength;

[0042] 3) Soak the photonic crystal template with better mechanical strength in the GelMA hydrogel pre-poly solution (0.3g / ml) for 2 hours, and obtain the photonic crystal-hydrogel hybrid system through UV curing;

[0043] 4) Finally, HF (2wt%) was used to...

example 2

[0052] Example 2 A kind of cardiomyocyte detection based on bovine serum albumin (BSA) inverse opal hydrogel membrane and its application

[0053] 1. Preparation of BSA inverse opal structure hydrogel film:

[0054] 1) Dispersing the purified polystyrene particles monodispersed at 100 nm in an aqueous solution to obtain a polystyrene aqueous solution with a concentration of 1 wt %;

[0055] 2) Deposit polystyrene aqueous solution on the silicon wafer, self-assemble to form polystyrene photonic crystal template;

[0056] 3) Soak the polystyrene photonic crystal template in BSA hydrogel prepolymer solution (0.2g / ml) for 3 hours, and cross-link with glutaraldehyde to obtain a photonic crystal-hydrogel hybrid system;

[0057] 4) Finally, absolute ethanol was used to dissolve the polystyrene particles in the photonic crystal hydrogel hybrid system to obtain the BSA inverse opal hydrogel.

[0058] 2. BSA inverse opal hydrogel for the culture of cardiomyocytes

[0059] The cardiom...

example 3

[0066] Example 3 A kind of cardiomyocyte detection based on gelatin inverse opal structure hydrogel membrane and its application

[0067] 1. Preparation of gelatin stripe inverse opal structure hydrogel:

[0068] 1) Disperse the purified silicon dioxide particles monodispersed at 200nm in an ethanol solution to obtain a silicon dioxide ethanol dispersion with a concentration of silicon dioxide particles of 15% by weight;

[0069] 2) Deposit the silica ethanol dispersion on the striped silicon wafer (concave 40 μm, convex 30 μm) to form a striped silica photonic crystal template, and finally perform high-temperature calcination (600 ° C) on the obtained striped photonic crystal template to obtain mechanical strength Better stripe photonic crystal template;

[0070] 3) Soak the striped photonic crystal template with better mechanical strength in gelatin hydrogel prepolymer solution (0.25g / ml) for 5h, and cross-link with glutaraldehyde (3wt%) to obtain a photonic crystal hydroge...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
wavelengthaaaaaaaaaa
Login to View More

Abstract

A myocardial cell detection method based on hydrogel of an inverse opal structure, and applications thereof. The method comprises the following steps: (1) preparing hydrogel of an inverse opal structure, having biocompatibility; (2) culturing myocardial cells, based on the hydrogel of an inverse opal structure; (3) detecting the myocardial cells; and (4) analyzing data. The hydrogel of an inverse opal structure has good biocompatibility, cells have high activity and phenotype when growing on the surface of the hydrogel, the hydrogel of an inverse opal structure provides a carrier for the growth of the myocardial cells, and more importantly, provides stable optical sensing signals for detecting the shrinking force and the beat frequency of the myocardial cells. The detection method does not need a complicated detection system, and has the advantages of intuitiveness, high sensitivity and high efficiency and is not affected by external conditions; the method can be used for screening and evaluating heart drugs and can screen the drugs by means of the variation of the shrinking force and the beat frequency of the myocardial cells after the drugs are added.

Description

technical field [0001] The invention relates to a cardiomyocyte detection method based on an inverse opal structure hydrogel and an application thereof, belonging to the technical field of biomedical material research. Background technique [0002] At present, in the detection process of cardiomyocytes, we mainly rely on in vitro cell culture technology and the construction of in vivo animal models. In the process of new drug research and development, due to the lack of complexity of the body, simple two-dimensional cell culture has problems such as inability to truly simulate the microenvironment in vivo and the complex physiological processes between tissues and organs; in addition, due to the uncertainty of building animal models With its own complexity and some humanitarian factors, the construction of animal models in drug development also faces certain challenges. In order to truly simulate the microenvironment in the body and realize the real simulation of organs in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N15/10
CPCG01N15/10G01N2015/1006
Inventor 赵远锦付繁繁高崴商逸璇王月桐
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com