A double metal hydroxide ceramic membrane for desalination of seawater and its preparation method

A hydroxide and ceramic membrane technology, applied in chemical instruments and methods, seawater treatment, general water supply conservation, etc., can solve problems such as low filtration efficiency, difficult seawater industrial desalination, and low efficiency of seawater desalination

Active Publication Date: 2020-12-01
湖州达立智能设备制造有限公司
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies in the prior art that filter and desalinate seawater have high requirements on membrane materials, low seawater desalination efficiency, and difficulty in realizing industrialized desalination of seawater, the present invention proposes a double metal hydroxide ceramic membrane and its The preparation method, it can directly desalinate seawater, and the ceramic membrane is repellent to salt ions, which can effectively prevent its accumulation and hinder the passage of water molecules, has high filtration efficiency and long service life, and overcomes the incomplete filtration and low filtration efficiency of current filtration membrane defect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A double metal hydroxide ceramic membrane for desalination of seawater and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A double metal hydroxide ceramic membrane for seawater desalination, comprising a porous ceramic substrate and a film covered on the porous ceramic substrate, the film is made of the following parts by weight: reduced graphene oxide 8 parts by weight , 20 parts by weight of magnesium sulfate, 30 parts by weight of aluminum nitrate, 5 parts by weight of sorbitan fatty acid ester, 5 parts by weight of n-decyltrimethoxysilane, 3 parts by weight of propylene glycol butyl ether, N,N-dimethylformaldehyde 60 parts by weight of amide, and 125 parts by weight of water.

[0028] The preparation method of the layered double metal hydroxide ceramic membrane used for seawater desalination comprises the following steps:

[0029] (1) Preparation of reduced graphene oxide: Weigh 200 mg of graphene oxide and add it to 100 ml of deionized water, and ultrasonically strip it for 0.5 h to form a graphene oxide mixture; add 600 mg of EDDS to the graphene oxide mixture, and mix evenly by ultr...

Embodiment 2

[0034] A double metal hydroxide ceramic membrane for seawater desalination, comprising a porous ceramic substrate and a film covered on the porous ceramic substrate, the film is made of the following parts by weight: 10 parts by weight of reduced graphene oxide , 15 parts by weight of magnesium chloride, 40 parts by weight of aluminum chloride, 7 parts by weight of polyoxyethylene fatty acid ester, 3 parts by weight of n-decyltrimethoxysilane, 5 parts by weight of ethylene glycol butyl ether acetate, N,N-di 75 parts by weight of methyl formamide, and 120 parts by weight of water.

[0035] The preparation method of the layered double metal hydroxide ceramic membrane used for seawater desalination comprises the following steps:

[0036] (1) Preparation of reduced graphene oxide: Weigh 200 mg of graphene oxide and add it to 100 ml of deionized water, and ultrasonically strip it for 0.5 h to form a graphene oxide mixture; add 600 mg of EDDS to the graphene oxide mixture, and mix e...

Embodiment 3

[0041] A double metal hydroxide ceramic membrane for seawater desalination, comprising a porous ceramic substrate and a film covered on the porous ceramic substrate, the film is made of the following parts by weight: reduced graphene oxide 5 parts by weight , 25 parts by weight of magnesium chloride, 20 parts by weight of aluminum sulfate, 3 parts by weight of polyoxyethylene fatty amine, 6 parts by weight of n-decyltrichlorosilane, 1 part by weight of propylene glycol butyl ether, 50 parts by weight of N-methylpyrrolidone, 150 parts by weight of water share.

[0042] The preparation method of the layered double metal hydroxide ceramic membrane for seawater desalination is characterized in that it comprises the following steps:

[0043] (1) Preparation of reduced graphene oxide: Weigh 200 mg of graphene oxide and add it to 100 ml of deionized water, and ultrasonically strip it for 0.5 h to form a graphene oxide mixture; add 600 mg of EDDS to the graphene oxide mixture, and mix...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
salt rejection rateaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of active carbon and preparation thereof, in particular to a bi-metal hydroxide ceramic film used for sea water desalination and a preparation method thereof. The bi-metal hydroxide ceramic film used for sea water desalination comprises porous ceramic substrate and a film which covers the porous ceramic substrate. The bi-metal hydroxide ceramic film ischaracterized by being prepared from the following substances in parts by weight: 3-12 parts of graphene, 10-30 parts of magnesium salts, 5-45 parts of aluminum salts, 2-8 parts of a surfactant, 3-6 parts of a silane coupling agent, 1-5 parts of a coalescing agent, 2-8 parts of an alkaline source, 40-80 parts of an organic solvent and 100-200 parts of water. According to the bi-metal hydroxide ceramic film used for sea water desalination and the preparation method thereof disclosed by the invention, sea water can be directly desalinated; the ceramic film has repellency on salt ions, effectively prevents the salt ions from stacking to block water molecules from passing, is high in filter efficiency, is long in service life, and overcomes the defects such as incomplete filtration and low filter efficiency of a current filter film.

Description

technical field [0001] The invention relates to the technical field of activated carbon and its preparation, in particular to a double metal hydroxide ceramic membrane used for seawater desalination and a preparation method thereof. Background technique [0002] Water resources are the material basis for human survival. However, with the growth of the world's population and the continuous development of industrialization, the crisis of water resources faced by mankind is becoming more and more serious, especially in my country with a large population, uneven distribution of water resources, and water shortages. increasingly serious. The crisis of fresh water resources on the earth is becoming more and more serious, and seawater desalination is one of the important ways to solve the crisis of water resources. Among them, the reverse osmosis seawater desalination method refers to the desalination of seawater by using the separation effect of the reverse osmosis membrane, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/02B01D67/00C04B41/87C02F1/44C02F103/08
CPCY02A20/131
Inventor 陈庆曾军堂
Owner 湖州达立智能设备制造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap