Copper-red glaze for Jun porcelain and preparation method of copper-red glaze

A technology of red glaze and Jun porcelain, applied in the field of Jun porcelain manufacturing, can solve the problems of high production difficulty, high production cost, and low yield

Inactive Publication Date: 2018-01-16
禹州市大龙山钧瓷文化有限公司
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention provides Jun porcelain copper red glaze with scientific raw materials and proportioning an

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A Jun porcelain copper red glaze, prepared from the following raw materials in parts by weight: 26-34 parts of feldspar, 6-10 parts of white feldspar, 10-14 parts of kaolin, 6-10 parts of talc, 22-26 parts of quartz, Calcite 10-14 parts, copper oxide 0.9-1.1 parts, zinc oxide 1-3 parts, silicon carbide 1.1-1.3 parts, wood ash 1-3 parts.

[0023] The preparation method of above-mentioned Jun porcelain copper red glaze comprises the following steps:

[0024] (1) Grind the above raw materials and mix them into a ball mill for ball milling, add water to make the mass concentration of the glaze reach 52-53%, wet mill for 15-16 hours, pass the wet milled slurry through a 200-300 mesh sieve to obtain the glaze slurry ;

[0025] (2) The glaze is applied by dipping, and the thickness of the glaze is 0.8mm~1.2mm;

[0026] (3) Firing, the firing temperature is 1260-1300°C.

[0027] The firing process in step (3) specifically includes the following steps:

[0028] ①The body aft...

Embodiment 2

[0033] A Jun porcelain copper red glaze, prepared from the following raw materials in parts by weight: 30 parts of feldspar, 8 parts of white feldspar, 12 parts of kaolin, 8 parts of talc, 24 parts of quartz, 12 parts of calcite, 1 part of copper oxide, 2 parts of zinc, 1.2 parts of silicon carbide, and 2 parts of wood ash.

[0034] The preparation method of above-mentioned Jun porcelain copper red glaze comprises the following steps:

[0035] (1) Grind the above raw materials and put them into a ball mill for ball milling, add water to make the mass concentration of the glaze reach 53%, wet mill for 15 hours, pass the wet milled slurry through a 250-mesh sieve to obtain the glaze slurry;

[0036] (2) The glazing adopts the dipping method, and the thickness of glazing is 1mm;

[0037] (3) Firing, specifically including the following steps:

[0038] ①The body after glazing is put into a kiln and fired in an oxidizing atmosphere, so that the temperature rises to 950°C evenly w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses copper-red glaze for Jun porcelain. The copper-red glaze is prepared from raw materials in parts by weight as follows: 26-34 parts of melilite, 6-10 parts of white feldspar, 10-14 parts of kaolin, 6-10 parts of talc, 22-26 parts of quartz, 10-14 parts of calcite, 0.9-1.1 parts of copper oxide, 1-3 parts of zinc oxide, 1.1-1.3 parts of silicon carbide and 1-3 parts of wood ash. The preparation method of the copper-red glaze for the Jun porcelain comprises steps as follows: (1) the raw materials are crushed, mixed and put in a ball mill for ball milling, water is added, so that the mass concentration of the glaze reaches 52%-53%, wet grinding is performed for 15-16 h, slurry obtained through wet grinding is sieved by a 200-300-mesh sieve, and glaze slurry is obtained;(2) glazing is performed in a glaze dipping manner, wherein the glazing thickness is 0.8-1.2 mm; (3) firing at the temperature of 1,260-1,300 DEG C is performed.

Description

technical field [0001] The invention relates to the technical field of Jun porcelain manufacturing, in particular to a Jun porcelain copper red glaze and a preparation method thereof. Background technique [0002] Jun Porcelain is a unique national treasure porcelain in Shenhou Town, Yuzhou City, Xuchang City, Henan Province. With its simple shape, exquisite craftsmanship, complex glaze matching, and the magical kiln transformation of "one color in the kiln, thousands of colors in the kiln", the scenery of lakes and mountains, clouds and clouds Fog, human, animal, flower, bird, insect, fish, etc. are known as the first of the "Five Famous Porcelains" in China. [0003] Red is the most expensive ceramic decoration, and there are many types of red glaze, among which copper red glaze has the longest history. Copper red glaze is a precious product developed after celadon glaze. It matured in Henan Jun kiln in the Northern Song Dynasty, and was inherited and developed by Jingdez...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00C04B41/86
Inventor 王建伟
Owner 禹州市大龙山钧瓷文化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap