Environmentally friendly stone-like coating

A real stone paint and paint technology, applied in the paint field, can solve problems such as endangering life and property, and achieve the effects of strong anti-aging ability, bright colors, and good alkali resistance

Active Publication Date: 2018-01-05
山东卓威新型材料有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The use of dry-hanging stone on the exterior wall will add thousands of tons of additional burden, seriously endangering life and property

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] Environmentally friendly real stone paint, the specific raw materials are:

[0071] 0.1 parts by weight of hydroxyethyl cellulose;

[0072] 0.8 parts by weight of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate;

[0073] 0.5 parts by weight of ethylene glycol;

[0074] 0.1 parts by weight of 2-amino-2-methyl-1-propanol;

[0075] 20 parts by weight of silicone acrylic emulsion;

[0076] 90 parts by weight of natural colored sand;

[0077] 3 parts by weight of rock chips;

[0078] 0.2 parts by weight defoamer;

[0079] 0.2 parts by weight of water repellent;

[0080] 0.2 parts by weight of bactericide;

[0081] 8 parts by weight of water.

[0082] The above-mentioned raw materials are mixed, and stirred at a rotation speed of 600 rpm for 20 minutes at room temperature, and mixed evenly to obtain the environmentally friendly real stone paint coating of the present invention.

[0083] The environmental protection real stone paint coating of the present invention is sprayed on the mortar bloc...

Embodiment 2

[0087] Environmentally friendly real stone paint, the specific raw materials are:

[0088] 0.1 parts by weight of hydroxyethyl cellulose;

[0089] 0.8 parts by weight of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate;

[0090] 0.5 parts by weight of ethylene glycol;

[0091] 0.1 parts by weight of 2-amino-2-methyl-1-propanol;

[0092] 20 parts by weight of silicone acrylic emulsion;

[0093] 90 parts by weight of natural colored sand;

[0094] 3 parts by weight of rock chips;

[0095] 1 part by weight of ethylene glycol monomethyl ether;

[0096] 0.2 parts by weight defoamer;

[0097] 0.2 parts by weight of water repellent;

[0098] 0.2 parts by weight of bactericide;

[0099] 8 parts by weight of water.

[0100] The above-mentioned raw materials are mixed, and stirred at a rotation speed of 600 rpm for 20 minutes at room temperature, and mixed evenly to obtain the environmentally friendly real stone paint coating of the present invention.

[0101] The test method is the same as in Example 1.

...

Embodiment 3

[0104] Environmentally friendly real stone paint, the specific raw materials are:

[0105] 0.1 parts by weight of hydroxyethyl cellulose;

[0106] 0.8 parts by weight of 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate;

[0107] 0.5 parts by weight of ethylene glycol;

[0108] 0.1 parts by weight of 2-amino-2-methyl-1-propanol;

[0109] 20 parts by weight of silicone acrylic emulsion;

[0110] 90 parts by weight of natural colored sand;

[0111] 3 parts by weight of rock chips;

[0112] 1 part by weight of ethylene glycol monobutyl ether;

[0113] 0.2 parts by weight defoamer;

[0114] 0.2 parts by weight of water repellent;

[0115] 0.2 parts by weight of bactericide;

[0116] 8 parts by weight of water.

[0117] The above-mentioned raw materials are mixed, stirred at a rotation speed of 600 rpm for 20 minutes at room temperature, and mixed evenly to obtain the environmentally friendly real stone paint coating of the present invention.

[0118] The test method is the same as in Example 1.

[0119...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses environmentally friendly stone-like coating. The coating is prepared by the following raw materials in parts by weight: 0.05-0.15 parts of hydroxyethyl cellulose, 0.4-1.2 partsof 2,2,4-trimethyl-1,3-pentanediol mono(2-methylpropanoate), 0.2-0.8 parts of glycol, 0.05-0.15 parts of 2-amino-2-methyl-1-propanol, 15-30 parts of silicon acrylic emulsion, 50-100 parts of naturalcolor sand, 2-4 parts of rock sheets, 0.3-1.2 parts of 2-methoxyethanol, 0.3-1.2 parts of 2-butoxyethanol, and 5-10 parts of water. The stone-like coating has the advantages of gorgeous appearance color, water resistance, alkali resistance, good adhesion stress, and good ageing resistance; the product is suitable for a plurality of bases, and can be used for effectively protecting buildings from being eroded by severe environment, and prolonging usage life.

Description

Technical field [0001] The invention relates to a paint, in particular to an environmentally friendly real stone paint paint. Background technique [0002] Real stone paint is a kind of paint whose decorative effect resembles marble and granite. It is mainly made of natural stone powder of various colors and is applied to the imitation stone effect of building exterior walls, so it is also called liquid stone. [0003] Buildings decorated with real stone lacquer have natural and natural colors, giving people an elegant, harmonious and solemn beauty, and are suitable for indoor and outdoor decoration of various buildings. Especially the decoration on curved buildings is vivid and lifelike, and has a return to nature effect. Real stone paint is fireproof, waterproof, acid and alkali resistant, and pollution resistant. Non-toxic, odorless, strong adhesion, never fade, etc., can effectively prevent the harsh external environment from corroding the building and prolong the life of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/32C04B111/54
Inventor 储旭
Owner 山东卓威新型材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com