Glass polishing agent for automobiles and preparation method of glass polishing agent

A technology for glass and automobiles, applied to polishing compositions containing abrasives, etc., can solve the problems of increased probability of abrasive particles scraping scratches, decreased polishing effect, scratches of abrasive particles, etc., and achieves low cost, low toxicity, The effect of preventing large scratches

Inactive Publication Date: 2017-12-15
江苏云瀚股份有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, since the stripping agent is used to level the surface of the material by scraping, the problem that it inevitably brings is that as the surface flatness of the object to be polished increases, it is scraped off by the abrasive particles in the stripping agent. Chances of scratches are also on the rise
[0004] In addition, because the existing stripping agents all adopt a circular motion, the abrasive particles in the stripping agent tend to be displaced to the edge of the polishing machine grinding disc due to the centrifugal force, which will bring two problems. One is The polishing effect at the center of the grinding disc is reduced, and the second is that the surface of the object at the edge of the grinding disc is more likely to be scratched by dense abrasive particles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of glass stripping agent for automobiles provided by this implementation 1, including dibasic fatty carboxylic acid, alcohol compound, azole compound, inorganic salt compound, anticorrosion additive, descaling agent, lubricating penetrating agent, preservative, hindered Phenolic antioxidant, sugar lubricant, foaming additive, glass fiber, surfactant, palm wax, silica powder, Fe 3 o 4 Powder, carbon black, short carbon fibers, sodium hydroxide and water.

[0025] Further, in this embodiment 1, the glass stripping agent includes the following components by weight fraction: 1 part of dibasic fatty carboxylic acid, 15 parts of alcohol compounds, 0.4 parts of azole compounds, and 6 parts of inorganic salt compounds , 0.1 part of anti-corrosion additive, 0.3 part of descaling agent, 0.1 part of lubricating penetrating agent, 0.5 part of preservative, 0.2 part of hindered phenolic antioxidant, 0.1 part of sugar lubricant, 3 parts of foaming additive, 2 parts of glass f...

Embodiment 2

[0034] A kind of glass stripping agent for automobiles provided by this implementation 2, including dibasic fatty carboxylic acid, alcohol compound, azole compound, inorganic salt compound, anti-corrosion additive, descaling agent, lubricating penetrating agent, preservative, hindered Phenolic antioxidant, sugar lubricant, foaming additive, glass fiber, surfactant, palm wax, silica powder, Fe 3 o 4 Powder, carbon black, short carbon fibers, sodium hydroxide and water.

[0035] Further, in Example 2, the glass stripping agent includes the following components by weight fraction: 2 parts of dibasic fatty carboxylic acid, 20 parts of alcohol compound, 0.5 part of azole compound, and 8 parts of inorganic salt compound , 0.2 parts of anti-corrosion additives, 0.5 parts of descaling agents, 0.2 parts of lubricating penetrating agents, 0.7 parts of preservatives, 0.4 parts of hindered phenolic antioxidants, 0.2 parts of sugar lubricants, 5 parts of foaming additives, 3 parts of glas...

Embodiment 3

[0044] A kind of glass stripping agent for automobiles provided in this embodiment 3, including dibasic fatty carboxylic acid, alcohol compound, azole compound, inorganic salt compound, anticorrosion additive, descaling agent, lubricating penetrating agent, preservative, hindered Phenolic antioxidant, sugar lubricant, foaming additive, glass fiber, surfactant, palm wax, silica powder, Fe 3 o 4 Powder, carbon black, short carbon fibers, sodium hydroxide and water.

[0045] Further, in Example 3, the glass stripping agent includes the following components by weight fraction: 1 part of dibasic fatty carboxylic acid, 15 parts of alcohol compounds, 0.4 parts of azole compounds, and 6 parts of inorganic salt compounds , 0.1 part of anti-corrosion additive, 0.3 part of descaling agent, 0.1 part of lubricating penetrating agent, 0.5 part of preservative, 0.2 part of hindered phenolic antioxidant, 0.1 part of sugar lubricant, 3 parts of foaming additive, 2 parts of glass fiber, 0.5 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a glass polishing agent for automobiles and belongs to the technical field of glass polishing agents. The glass polishing agent is prepared from aliphatic dicarboxylic acid, alcohol compounds, azole compounds, inorganic salt compounds, an anticorrosive additive, an antiscaling agent, a lubricating penetrating agent, a preservative, hindered phenol antioxidants, a granulated sugar lubricant, a foaming additive, glass fiber, a surfactant, palm wax, silica powder, Fe3O4 powder, carbon black, short carbon fibers, sodium hydroxide and water. The invention further provides a preparation method of the glass polishing agent. The glass polishing agent is economical, reasonable, low in toxicity, environmentally friendly and non-toxic and adopts an excellent technique; the components perform a synergistic corrosion inhibiting function, and the polishing agent is low in cost, economical and practical; magnetic Fe3O4 is adopted, cannot be dispersed in the polishing process and is more uniformly distributed on the surface, the dispersity is improved through the short carbon fibers, and large scratches formed due to the fact that a single particle is fixed and stuck can be prevented.

Description

technical field [0001] The invention relates to a glass stripping agent and a preparation method thereof, in particular to a glass stripping agent for automobiles and a preparation method thereof, and belongs to the technical field of glass stripping agents. Background technique [0002] Stripping agent is a common reagent to improve the flatness of glass surface. Its basic principle is to reduce the roughness of glass surface through repeated scraping of fine polishing particles, so as to achieve a flat and smooth visual effect. Existing stripping agents are mostly used Tiny abrasive particles and various suspending agents are used together to perform polishing operations. [0003] However, since the stripping agent is used to level the surface of the material by scraping, the problem that it inevitably brings is that as the surface flatness of the object to be polished increases, it is scraped out by the abrasive particles in the stripping agent. The chances of scratches ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09G1/02
CPCC09G1/02
Inventor 郝国强
Owner 江苏云瀚股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products