A kind of sprinkle blue glaze and its application method

An application method, the technology of blue glaze, applied in the field of sprinkled blue glaze, can solve the problems of not seeing related content, etc., achieve the effect of broad market space, lower firing temperature, and stable appearance and color development

Active Publication Date: 2019-03-29
JINGDEZHEN CERAMIC UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at present, there is still no relevant content related to the raw material formula and production process of the blue glaze, especially the research on process reproduction and restoration.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] (1) After the raw materials are mixed and ball-milled according to the following bottom glaze and top glaze material ratios, the bottom glaze passes through a 100-mesh sieve and the top glaze passes through a 250-mesh sieve, and the sieve residue is 0.2%;

[0019] (2) Glaze the bottom glaze and top glaze in stages on the surface of the porcelain body after high-temperature biscuit firing;

[0020] (3) Put the glazed porcelain body in a shuttle kiln for firing, use an oxidizing atmosphere from room temperature to 980°C, use a reducing atmosphere above 980°C, raise the temperature to the highest point of 1200°C, keep it for 20 minutes, and cool it down to room temperature naturally. kiln, obtaining a porcelain body decorated with blue glaze.

[0021] The bottom glaze material ratio is:

[0022] 15% wolfberry ash, 40% Yaoli glaze fruit, 5% pearl material, 1% tin oxide, 9% copper flower, 30% nitrate frit;

[0023] The ratio of glaze materials is:

[0024] Yaoli glaze fru...

Embodiment 2

[0028] (1) After the raw materials are mixed and ball-milled according to the following bottom glaze and top glaze material ratios, the bottom glaze passes through a 100-mesh sieve and the top glaze passes through a 250-mesh sieve, and the sieve residue is 0.2%;

[0029] (2) Glaze the bottom glaze and top glaze in stages on the surface of the porcelain body after high-temperature biscuit firing;

[0030] (3) Put the glazed porcelain body in a shuttle kiln for firing, use an oxidizing atmosphere from room temperature to 980°C, use a reducing atmosphere above 980°C, raise it to the highest temperature point of 1100°C, keep it for 20 minutes, and cool it down to room temperature naturally. kiln, obtaining a porcelain body decorated with blue glaze.

[0031] The bottom glaze material ratio is:

[0032] 5% wolfberry ash, 25% Yaoli glaze fruit, 2% pearl material, 3% tin oxide, 5% copper flower, 60% nitrate frit;

[0033] The ratio of glaze materials is:

[0034] Yaoli glaze fruit...

Embodiment 3

[0038] (1) After the raw materials are mixed and ball-milled according to the following bottom glaze and top glaze material ratios, the bottom glaze passes through a 100-mesh sieve and the top glaze passes through a 250-mesh sieve, and the sieve residue is 0.2%;

[0039] (2) Glaze the bottom glaze and top glaze in stages on the surface of the porcelain body after high-temperature biscuit firing;

[0040] (3) Put the glazed porcelain body in a shuttle kiln for firing, use an oxidizing atmosphere when the room temperature reaches 980°C, and use a reducing atmosphere when the temperature is above 980°C. Raise to the highest temperature point of 1150°C, keep it for 20 minutes, and cool it down to room temperature naturally. kiln, obtaining a porcelain body decorated with blue glaze.

[0041] The bottom glaze material ratio is:

[0042] 10% wolfberry grass ash, 30% Yaoli glaze fruit, 3% pearl material, 2% tin oxide, 7% copper flower, 48% nitrate frit;

[0043] The ratio of glaze ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a manufacturing method using reducing atmosphere to fire scattering-blue glaze. The ground glaze of the scattering-blue glaze comprises, by weight percentage, 5-15% of Dicranopteris linearis ash, 25-40% of Yaoli glaze stone, 2-5% of Zhuming material, 1-3% of tin oxide, 5-10% of copper scale and 30-60% of saltpeter frit. The surface glaze of the scattering-blue glaze comprises, by weight percentage, 30-40% of Yaoli glaze stone, 15-30% of Shouan lime-flyash and 30-55% of saltpeter frit. The manufacturing method includes: preparing raw materials, performing ball milling, sieving, performing unique twice glaze application on a high-temperature biscuit-firing body, and firing the scattering-blue glaze under the reducing atmosphere of 1100-1200 DEG C. The method has the advantages that the manufactured scattering-blue glaze is even in blue spot scattering, stable in appearance color, good in decoration effect and promising in application prospect.

Description

technical field [0001] The invention belongs to the field of inorganic non-metallic materials (ceramics), and in particular relates to a blue glaze and an application method thereof. Background technique [0002] Sprinkle blue glaze, also known as "snowflake blue glaze", was created and fired in Jingdezhen during the Xuande period of the Ming Dynasty, and then stopped firing. It was not until the Kangxi period of the Qing Dynasty that production resumed. The blue-glazed porcelain from the Kangxi, Yongzheng, and Qianlong periods of the Qing Dynasty was stable in color and fine in workmanship. Its characteristic is that the glaze layer is thicker in the dense part, and the white ground is exposed in the thin part, making the glazed surface seem to be covered with a layer of snowflakes, and the color is bright and elegant. Due to the complicated firing process and low success rate, blue-glazed porcelain was a relatively rare variety at that time. In the late Qing Dynasty, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/14C04B41/86
CPCC03C8/14C04B41/5022C04B41/86
Inventor 吴军明罗婷熊露张茂林李其江
Owner JINGDEZHEN CERAMIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com