Conductive ink low-temperature curing composition and preparing method thereof

A conductive ink and composition technology, which is applied in the field of conductive ink low-temperature curing composition and its preparation, can solve the problems of complex process and high cost, and achieve the effects of simple operation, low cost and improved stability

Inactive Publication Date: 2017-11-07
XIAMEN UNIV
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Although the existing curing agent is very matur...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conductive ink low-temperature curing composition and preparing method thereof
  • Conductive ink low-temperature curing composition and preparing method thereof
  • Conductive ink low-temperature curing composition and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Weigh 4 parts of epoxy resin, 1 part of urea, 2 parts of ethylene glycol ether acetate, 1 part of terpineol, 1 part of additives, and 2 parts of graphene, and add them to a mixer and stir for 4 hours. Use a coating bar to coat on a smooth polyester film with a thickness of 0.2mm, and dry it in an oven at 100°C for 15 minutes to obtain a solid transparent resin film, and then measure it with tape according to the American Society for Testing and Materials standard ASTMD3359-74 Standard Method for Coating Film Adhesion "Test the adhesion of the sample, fix the sample, draw 11 horizontal and vertical lines with a cross-cutting knife, the line spacing is 1mm, and draw 100 small grids of 1mm x 1mm. Then use 3M#600 adhesive tape to cover the entire grid, and rub the rubber head on the cover, so that the color under the transparent tape is consistent and the adhesion is good. After sticking the tape and keeping it for 90±30s, pull off the tape quickly (not suddenly) in the opp...

Embodiment 2

[0039] Weigh 2 parts of epoxy resin and 3 parts of terpineol and mix evenly, then add 1 part of urea to the mixer. After it is completely dissolved, add 3 parts of conductive carbon black and 1 part of ethyl cellulose that pass through a 400 mesh screen, and stir evenly. A 300-mesh screen printing screen was selected, and the evenly stirred slurry to be tested was printed on a polyester film with a thickness of 0.1 mm. Dry in an oven at 120°C for 20 minutes. Bend the screen-printed pattern 180° outward according to the center line, then press it with a 2kg weight, keep it for 1min, and then open the diaphragm to flatten it. After repeated bending for 10 times in this way, the diaphragm was flattened, and the pattern did not fall off.

Embodiment 3

[0041] Weigh 2.5 parts of epoxy resin, 0.5 parts of urea, 2 parts of terpineol, 1 part of butyl acetate, 2 parts of graphite powder, 1 part of conductive carbon black, and 1 part of ethyl cellulose, and add them to a ball mill jar for ball milling for 6 hours. A 300-mesh screen printing screen was selected, and the evenly stirred slurry to be tested was printed on a polyester film with a thickness of 0.1 mm. Dry in an oven at 80°C for 30 minutes. Bend the screen-printed pattern 180° outward according to the center line, then press it with a 2kg weight, keep it for 1min, and then open the diaphragm to flatten it. After repeated bending for 10 times in this way, the diaphragm was flattened, and the pattern did not fall off.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a conductive ink low-temperature curing composition and a preparing method thereof, and relates to the low-temperature curing composition which contains a urea curing agent. The conductive ink low-temperature curing composition comprises, by mass, 1-6 of epoxy resin, 3-5 of solvent and 1-5 of urea. When the conductive ink low-temperature curing composition is prepared, firstly the epoxy resin and the solvent are mixed, and then urea is added to serve as the curing agent to conduct mixing curing, so that the conductive ink low-temperature curing composition is obtained. The conductive ink low-temperature curing composition includes epoxy resin and an epoxy curing agent. Regarding the epoxy curing agent, a simple compound, namely urea serves as the curing agent. The conductive ink low-temperature curing composition is applied to the field of conducting ink.

Description

technical field [0001] The invention relates to a low-temperature curing composition containing a urea curing agent, in particular to a low-temperature curing, low-cost conductive ink low-temperature curing composition suitable for industrialization and a preparation method thereof. Background technique [0002] As we all know, the excellent physical, mechanical and electrical insulation properties of epoxy resin, the bonding performance of various materials, and the flexibility of its use process are not available in other thermosetting plastics. Therefore, it can be made into coatings, adhesives, molding materials and injection molding materials, and is widely used in various fields of the national economy. The epoxy resin curing agent chemically reacts with the epoxy resin to form a network-like three-dimensional polymer, enveloping the composite material in the network. So far, there are a wide variety of curing agents for epoxy resins, which also provide users with a w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/03C09D11/102C09D11/52C08G59/40
CPCC09D11/102C08G59/4021C09D11/03C09D11/52
Inventor 郑南峰张鑫吴炳辉方晓亮曹昉
Owner XIAMEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap