Expanded graphite and preparation method thereof
A technology of expanded graphite and graphite expansion, which is applied in the field of expanded graphite and its preparation, can solve the problems of reducing graphite expansion volume, uneven temperature, low reaction efficiency, etc., achieve controllable expansion multiple, avoid temperature difference, and improve reaction efficiency Effect
Inactive Publication Date: 2017-11-03
HUNAN GUOSHENG GRAPHITE TECH CO LTD
View PDF3 Cites 4 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The above scheme has the following problems: 1. Since the expansion process is affected by many aspects such as raw materials, feed speed, expansion temperature, time, wind speed, etc., the expansion multiple of the prepared expanded graphite cannot be controlled, and the expansion multiple of large-scale preparation cannot be stabilized. expanded graphite
2. Because the expansion temperature is too high, graphite will be oxidized at high temperature, thereby reducing the expansion volume of graphite. Therefore, on the one hand, it is necessary to control the reaction time and temperature, and at the same time, it is necessary to pass inert gas protection, resulting in complicated process and high cost.
3. The temperature in the furnace body is uneven, and the temperature of the inner wall of the furnace is obviously higher than that in the furnace, which leads to uneven heating of intercalated graphite during expansion and low reaction efficiency
4. After the reaction, due to the relatively small mesh number of expanded graphite, it is easy to get stuck in the equipment during transportation, which affects the product yield
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0032] The present invention will be further described below in conjunction with specific examples. The following examples are only illustrative examples and do not constitute improper limitations to the present invention. The present invention can be implemented in various ways defined and covered by the content of the invention. Unless otherwise specified, the reagents, compounds and equipment used in the present invention are conventional reagents, compounds and equipment in the technical field.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more
Abstract
The invention relates to an expanded graphite material, and discloses expanded graphite and a preparation method thereof. The traditional high-temperature expansion method is combined with a graphite expansion furnace; the optimal expansion temperature is used; the product stability can be effectively improved through controlling the raw materials and the process parameters at the expansion temperature, so that the large-scale preparation of stable expanded graphite with controllable expansion times is realized; the expansion times is 200 to 300; the bore diameter is 30 to 100nm; the carbon content is stable. The temperature region is formed by defining the temperature of a feeding opening and a discharging opening; the expansion time is controlled by setting the feeding speed and the wind speed; then, the separation and collection are realized through wind speed; the large-scale preparation is realized; the inert gas protection is not needed; the graphite high-temperature oxidation caused by too high expansion temperature can be prevented, so that the expansion volume of the graphite is reduced.
Description
technical field [0001] The present invention relates to expanded graphite materials, more specifically, to an expanded graphite and a preparation method thereof. Background technique [0002] Expanded graphite is a new type of composite material on the atomic and molecular scales formed by inserting foreign substances between graphite layers, and has become a new development direction in the graphite industry. It not only retains the excellent physical and chemical properties of graphite, but also produces a series of new physical and chemical properties due to the interaction between the carbon atom plane and the intercalated substance, such as high electrical conductivity, superconductivity, catalytic properties, hydrogen storage properties, etc. The expanded graphite obtained by high-temperature expansion looks like a worm, has stable thermodynamic properties, has a very large specific surface area and rich pore structure, and can be used as an adsorption material for org...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
IPC IPC(8): C01B32/225
Inventor 林前锋李丽萍
Owner HUNAN GUOSHENG GRAPHITE TECH CO LTD
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap