Composite board containing moxa residue as well as preparation method and application thereof

A composite plate and composite additive technology, applied in the field of materials, can solve the problems of easy deformation, high price, poor bending strength, etc., and achieve the effects of not easy to crack, good bending strength, and improved anti-mildew effect

Active Publication Date: 2017-10-24
GUANGZHOU JINAN BIOMEDICINE RES & DEV CENT
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the existing composite boards have problems such as easy deformation and poor bending strength, and the boards used for pyrography are generally solid wood boards, and the price is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite board containing moxa residue as well as preparation method and application thereof
  • Composite board containing moxa residue as well as preparation method and application thereof
  • Composite board containing moxa residue as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Embodiment 1, a kind of composite sheet material containing moxa slag

[0043]The composite board containing moxa slag comprises a face plate, a core board, a back board and an adhesive layer, and the face plate, the core board and the back board are glued together by the adhesive layer, and the face board and the back board are poplar boards; the core board is composed of the following The raw material of weight ratio is made: mugwort slag 11, wood powder 63, bamboo charcoal powder 3, bamboo powder 15 and soybean meal adhesive 6; Described adhesive layer comprises compound additive and adhesive, the compound additive and adhesive The weight ratio is 1:16.

[0044] The composite additive is composed of hydroxyapatite, jade powder and attapulgite in a weight ratio of 1:7:11.

[0045] The adhesive is soybean meal adhesive.

[0046] The preparation method of described mugwort slag comprises the following steps:

[0047] Crush Artemisia argyi leaves, pass through an 80-m...

Embodiment 2

[0057] Embodiment 2, a kind of composite plate containing moxa slag

[0058] The composite plate containing moxa slag comprises a face plate, a core plate, a back plate and an adhesive layer, and the face plate, the core plate and the back plate are glued together by the adhesive layer, and the face plate and the back plate are birch boards; the core plate is composed of the following The raw material of weight ratio is made: moxa residue 15, wood powder 68, bamboo charcoal powder 6, bamboo powder 20 and soybean meal adhesive 12; Described adhesive layer comprises compound additive and adhesive, the compound additive and adhesive The weight ratio is 3:14.

[0059] The composite additive is composed of hydroxyapatite, jade powder and attapulgite in a weight ratio of 3:5:9.

[0060] The adhesive is soybean meal adhesive.

[0061] The preparation method of described mugwort slag comprises the following steps:

[0062] Crush Artemisia argyi leaves, pass through an 80-mesh sieve...

Embodiment 3

[0072] Embodiment 3, a kind of composite plate containing moxa slag

[0073] The composite plate containing moxa slag comprises a face plate, a core plate, a back plate and an adhesive layer, and the face plate, the core plate and the back plate are glued together by the adhesive layer, and the face plate and the back plate are basswood boards; the core plate is composed of the following The raw material of weight ratio is made: mugwort slag 13, wood powder 66, bamboo charcoal powder 5, bamboo powder 18 and soybean meal adhesive 11; Described adhesive layer comprises compound additive and adhesive, the compound additive and adhesive The weight ratio is 2:15.

[0074] The composite additive is composed of hydroxyapatite, jade powder and attapulgite in a weight ratio of 2:5:10.

[0075] The adhesive is soybean meal adhesive.

[0076] The preparation method of described mugwort slag comprises the following steps:

[0077] Crush Artemisia argyi leaves, pass through an 80-mesh s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of materials and in particular relates to a composite board containing moxa residues as well as a preparation method and application thereof. The provided composite board containing the moxa residues comprises a panel, a core board, a backing plate and adhesive layers, wherein the panel, the core board and the backing plate are glued by virtue of the adhesive layers, and the panel and the backing plate are a poplar plate, an eucalyptus plate, a birch plate or a basswood plate; the core board is prepared from the following raw materials in weight proportion: 11-15 parts of moxa residues, 63-68 parts of wood powder, 3-6 parts of bamboo charcoal powder, 15-20 parts of bamboo powder and 6-12 parts of soybean meal adhesive; each adhesive layer contains composite additives and an adhesive in a weight ratio of (1-3):(14-16). The provided composite board containing the moxa residues is flat, fine and smooth in surface, is not blistered when being scalded and ironed, does not discolor or deform and hardly cracks, is good in strength and has excellent insect-proof, anticorrosion and mildewproof properties. The provided composite board containing the moxa residues can be applied to pyrograph.

Description

technical field [0001] The invention belongs to the technical field of materials, and in particular relates to a composite plate containing moxa residue, a preparation method and application thereof. Background technique [0002] Composite panels refer to panels made of two or more materials. Generally, a single plate cannot meet the specific needs and conditions of use, and other methods will be used to enhance its own performance. The principle of composite materials is to greatly improve the shortcomings of their own performance on the basis of the original. Composite panels have the following advantages: (1) enhance their own performance, such as: wood-plastic composite panels can enhance their own bearing capacity and strength on the original basis; (2) improve the overall performance, such as: metal composite panels can greatly improve And overcome the shortcomings of its own poor corrosion resistance; (3) comprehensive performance (innovation) such as: it can combin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B21/02B32B21/13B32B21/14B32B7/10B44C1/02
CPCB32B7/10B32B21/02B32B21/13B32B21/14B32B2307/306B32B2307/546B32B2307/7145B32B2307/734B44C1/02
Inventor 王一飞马婧任哲利奕成
Owner GUANGZHOU JINAN BIOMEDICINE RES & DEV CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com