Waterproof anti-oxidation insulating paint for power device

An anti-oxidation technology for power equipment, applied in anti-fouling/underwater coatings, primers, anti-corrosion coatings, etc., can solve the problems of poor waterproof and insulating properties, and achieve excellent protection effects, long protection time, and not easy yellowing effect

Inactive Publication Date: 2017-09-22
HEFEI ANLI ELECTRIC POWER ENG CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Conventional metal protective paints for equipment on the market can also be used, but these paints and coatings are not specially configured for the use scenarios of power equipment. They may have better properties such as oxidation resistance, wear resistance, and fire resistance, but they are not very waterproof and insulating. characteristic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof anti-oxidation insulating paint for power device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A waterproof and anti-oxidation insulating varnish for electric equipment, comprising a protective primer and a waterproof topcoat, the components of the protective primer are: 30 parts by mass of xylene, 30 parts of alkyd resin, 10 parts of aluminum powder slurry, china clay 10 parts, 3 parts of talcum powder, 2 parts of dibutyltin dilaurate, 1 part of silicon dioxide, 15 parts of glycol ether,

[0022] The composition of the waterproof topcoat in parts by mass is: 40 parts of polyether polyol, 30 parts of isocyanate, 25 parts of titanium dioxide, 11 parts of trimethylchlorosilane, 3 parts of fatty alcohol polyoxyethylene ether, polysiloxane 2 parts of leveling agent, 40 parts of No. 120 solvent naphtha.

[0023] The preparation method of the protective primer is as follows: mix alkyd resin, aluminum powder slurry, china clay, silicon dioxide and talc powder evenly, put them into a three-roll machine and grind them to a fineness of ≤45 μm, and then dissolve them in xyl...

Embodiment 2

[0027] A waterproof and oxidation-resistant insulating varnish for electric equipment, comprising a protective primer and a waterproof topcoat, the ingredients of the protective primer are: 40 parts by mass of xylene, 35 parts of alkyd resin, 15 parts of aluminum powder slurry, china clay 15 parts, 8 parts of talcum powder, 3 parts of dibutyltin dilaurate, 2 parts of silicon dioxide, 25 parts of glycol ether,

[0028] The composition of the waterproof topcoat in parts by mass is: 55 parts of polyether polyol, 40 parts of isocyanate, 30 parts of titanium dioxide, 15 parts of trimethylchlorosilane, 4 parts of fatty alcohol polyoxyethylene ether, polysiloxane 3 parts of leveling agent, 50 parts of No. 120 solvent naphtha.

[0029] The preparation method of the protective primer is as follows: mix alkyd resin, aluminum powder slurry, china clay, silicon dioxide and talc powder evenly, put them into a three-roll machine and grind them to a fineness of ≤45 μm, and then dissolve them...

Embodiment 3

[0033] A waterproof and oxidation-resistant insulating varnish for electric equipment, comprising a protective primer and a waterproof topcoat, the ingredients of the protective primer are: 35 parts by mass of xylene, 33 parts of alkyd resin, 12 parts of aluminum powder slurry, china clay 14 parts, 5 parts of talcum powder, 2 parts of dibutyltin dilaurate, 1 part of silicon dioxide, 20 parts of glycol ether,

[0034] The composition of the waterproof topcoat in parts by mass is: 50 parts of polyether polyol, 35 parts of isocyanate, 27 parts of titanium dioxide, 13 parts of trimethylchlorosilane, 3 parts of fatty alcohol polyoxyethylene ether, polysiloxane 2 parts of leveling agent, 45 parts of No. 120 solvent naphtha.

[0035] The preparation method of the protective primer is as follows: mix alkyd resin, aluminum powder slurry, china clay, silicon dioxide and talc powder evenly, put them into a three-roll machine and grind them to a fineness of ≤45 μm, and then dissolve them ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of coatings and particularly relates to a waterproof anti-oxidation insulating paint for a power device. The protective oil paint is prepared from priming paint and waterproof finish paint and contains dimethylbenzene, alkyd resin, aluminum powder slurry, porcelain clay, talcum powder, a plasticizer, silica and glycol ether. The waterproof finish paint contains polyether polyol, isocyanate, titanium dioxide powder, trimethyl monochlorosilane, fatty alcohol polyoxyethylene ether, a leveling agent and a cosolvent. When the waterproof anti-oxidation insulating paint is used, the priming paint is sprayed firstly, and then the finish paint is sprayed after the priming paint is dried. The protective paint has good oxidation-resistance, corrosion-resistance and waterproof properties, strong adhesive powder and uniform, fine and smooth paint surface and is very suitable for power device surfaces.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a waterproof and oxidation-resistant insulating varnish for electric equipment. Background technique [0002] Power equipment is used in the whole process from power generation, power transmission to power transformation, power distribution and power consumption to form a complete system of power production and consumption. These equipments have high technological content and high value; except for a few precision core equipments located indoors, most of the equipments are located outdoors, directly facing harsh natural conditions, so the requirements for equipment protection are relatively high. Painting the surface of some metal parts is part of the protective measures. [0003] Conventional metal protective paints for equipment on the market can also be used, but these paints and coatings are not specially configured for the use scenarios of power equipment. They...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D175/08C09D5/25C09D5/00C09D5/16C09D5/18C09D5/08C09D7/12C08G18/48
CPCC09D167/08C08G18/48C08K3/34C08K3/36C08K5/06C08K13/02C08K2003/0812C08K2003/2241C08K2201/014C08L2201/02C08L2201/08C08L2205/035C09D5/00C09D5/002C09D5/08C09D5/16C09D5/1687C09D5/18C09D175/08C08L71/02C08L83/04C08L91/00C08K3/22
Inventor 殷世尧
Owner HEFEI ANLI ELECTRIC POWER ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap