High-toughness flame-retardant foamed PVC wood-plastic board and preparation method thereof

A foaming and high-toughness technology, which is applied in the field of high-toughness flame-retardant foamed PVC wood-plastic board and its preparation, can solve the problems of poor oxidation resistance, wear resistance and aging resistance, surface wear and tear of wood-plastic board furniture, and To achieve the flame retardant effect and other issues, to achieve the effect of easy operation, no influence on curing and molding speed, and ideal pore structure

Inactive Publication Date: 2017-08-29
程艳青
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, wood-plastic panels in the prior art also have many disadvantages, such as: in a colder environment, the impact resistance is poor, and the nails are easy to crack during winter construction; the oxidation resistance, wear resistance, and aging resistance are poor. During the process, there will be problems such as serious surface wear and oxidative fading of wood-plastic panel furniture; poor thermal stability, easy to deform during summer construction; poor flame retardancy, and effective flame retardant effect cannot be achieved in case of fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness flame-retardant foamed PVC wood-plastic board and preparation method thereof
  • High-toughness flame-retardant foamed PVC wood-plastic board and preparation method thereof
  • High-toughness flame-retardant foamed PVC wood-plastic board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A high-toughness flame-retardant foamed PVC wood-plastic board, comprising: 100 parts of PVC resin SG4, 20 parts of wood flour, 5 parts of nano-light calcium carbonate, 2 parts of rutile titanium dioxide, and mercaptan 2 parts of base tin, 0.5 parts of antimony trioxide, 0.5 parts of polyacrylonitrile-based carbon fiber, 2 parts of PVC toughening agent, 2 parts of siloxane coupling agent KH-792, 0.5 parts of liquid triphenyl phosphite, PVC modification 1 part of sex aid ACR401, 1 part of chlorinated paraffin, 2 parts of silicone oil, 0.5 part of AC foaming agent.

Embodiment 2

[0038] A high-toughness flame-retardant foamed PVC wood-plastic board, comprising: 100 parts of PVC resin SG4, 40 parts of wood flour, 10 parts of nano light calcium carbonate, 4 parts of rutile titanium dioxide, and mercaptan 4 parts of base tin, 2.5 parts of antimony trioxide, 2 parts of polyacrylonitrile-based carbon fiber, 4 parts of PVC toughening agent, 4 parts of siloxane coupling agent KH-792, 2.5 parts of liquid triphenyl phosphite, PVC modified 3 parts of sex aid ACR401, 3 parts of chlorinated paraffin, 4 parts of silicone oil, 1.5 parts of AC foaming agent.

Embodiment 3

[0040] A high-toughness flame-retardant foamed PVC wood-plastic board, comprising: 100 parts of PVC resin SG4, 60 parts of wood flour, 15 parts of nano-light calcium carbonate, 6 parts of rutile titanium dioxide, and mercaptan 6 parts of base tin, 5 parts of antimony trioxide, 4 parts of polyacrylonitrile-based carbon fiber, 6 parts of PVC toughening agent, 6 parts of siloxane coupling agent KH-792, 5 parts of liquid triphenyl phosphite, PVC modified 5 parts of sex aid ACR401, 5 parts of chlorinated paraffin, 6 parts of silicone oil, 3 parts of AC foaming agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-toughness flame-retardant foamed PVC wood-plastic board. The high-toughness flame-retardant foamed PVC wood-plastic board comprises PVC resin, fiber powder, nanometer light calcium carbonate, rutile titanium dioxide, methyltin mercaptide, antimony trioxide, polyacrylonitrile-based carbon fibers, a PVC flexibilizer, a coupling agent, liquid triphenyl phosphite, a PVC modification aid, chlorinated paraffin, silicone oil and an AC foaming agent. The invention also discloses a preparation method for the PVC wood-plastic board. The preparation method for PVC wood-plastic board in the invention is simple in process and easy to operate; and the prepared PVC wood-plastic board has a plurality of advantages like good thermal stability, good ageing resistance, good anti-oxidizability, good impact resistance, good wear resistance, good insulating properties and good flame resistance.

Description

technical field [0001] The invention relates to the technical field of building material wood-plastic panels, more specifically, to a high-toughness flame-retardant foamed PVC wood-plastic panel and a preparation method thereof. Background technique [0002] With the continuous growth of the building materials market, the market demand for wooden building materials is also rising sharply. Among them, the utilization rate of wooden formwork is very high, but wooden formwork consumes a lot of wood, and the reuse rate is low. The template must be surface treated, such as brushing the surface with anti-corrosion paint, etc. With the enhancement of people's awareness of environmental protection, people gradually pay more attention to the protection of trees. The traditional deforestation has gradually transformed into the current afforestation. Therefore, people urgently need a new type of material to replace wooden building materials. Wood-plastic formwork is a new type of form...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08L33/04C08L91/06C08L83/04C08K13/04C08K7/06C08K3/04C08K3/26C08K5/58C08K3/22C08K5/526C08J9/10
CPCC08L27/06C08J9/103C08J2203/04C08J2327/06C08J2497/02C08K2003/2241C08K2003/265C08K2201/011C08L2201/02C08L2203/14C08L2205/16C08L97/02C08L33/04C08L91/06C08L83/04C08K13/04C08K7/06C08K3/04C08K3/26C08K5/58C08K3/22C08K3/2279C08K5/526
Inventor 程艳青
Owner 程艳青
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com