Organic and inorganic compound waterborne paint for exterior walls and preparation method thereof

A water-based paint, inorganic technology, applied in the direction of alkali metal silicate paint, coating, etc., can solve the problems of poor stability, poor decoration, aging, etc., and achieve excellent wear resistance and moisture resistance, good stability, The effect of appropriate flexibility

Active Publication Date: 2017-08-22
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most exterior wall paints are mainly organically synthesized emulsions, which are easy to construct, rich in decoration and color, but harmful substances volatilize during production and construction, and have excellent performance in weather resistance, heat and humidity resistance and adhesion. Poor, easy to be affected by ultraviolet rays and aging
Moreover, the dense coating seals the wall and prevents water vapor from penetrating, causing shedding.
However, pure inorganic coatings have disadvantages such as poor stability and poor decoration, which is not convenient for large-scale promotion and use.
[0003] CN101117477A discloses a preparation method of organic-inorganic composite waterproof paint, but there are many raw materials involved in the reaction, the content of components is not easy to control, and the process steps are relatively complicated
[0004] CN104559507A discloses an organic-inorganic composite coating and its preparation method, which has good water resistance, alkali resistance and stain resistance, but other performance needs to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic and inorganic compound waterborne paint for exterior walls and preparation method thereof
  • Organic and inorganic compound waterborne paint for exterior walls and preparation method thereof
  • Organic and inorganic compound waterborne paint for exterior walls and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Materials and contents used in the present embodiment are as follows:

[0050]

[0051] Preparation of inorganic bonding solution: Add silica sol into cylinder A according to the formula, stir at a speed of 500r / min and heat up to 35°C, then add stabilizer, stir at a speed of 500r / min for 20min, then add potassium silicate, Stir at a speed of 700r / min for 20min, and obtain an inorganic bonding solution in cylinder A for later use.

[0052] Preparation of paint slurry: Add pH adjuster, dispersant, wetting agent, defoamer, thickener and deionized water into cylinder B according to the formula amount, and stir at 1000r / min for 10min; then add pigments and fillers into cylinder B , disperse at 1400r / min for 30min, test the fineness of the millbase ≤ 50μm, and obtain the millbase,

[0053] Mixing steps: add the inorganic bonding solution in cylinder A to cylinder B, stir at a speed of 1100r / min for 10min, then add aqueous synthetic resin emulsion and leveling agent and s...

Embodiment 2

[0055] Materials and contents used in the present embodiment are as follows:

[0056]

[0057] Preparation of inorganic bonding solution: Add silica sol into cylinder A according to the formula, stir at a speed of 400r / min and heat up to 40°C, then add stabilizer, stir at a speed of 600r / min for 30min, then add potassium silicate, Stir at a speed of 600r / min for 10min, and obtain an inorganic bonding solution in cylinder A for later use.

[0058] Preparation of paint slurry: according to the formula, add pH regulator, dispersant, wetting agent, defoamer, thickener and deionized water into cylinder B, stir at 900r / min for 5min; then add pigments and fillers into cylinder B , disperse at 1300r / min for 40min, test the fineness of the millbase ≤ 50μm, and obtain the millbase,

[0059] Mixing steps: add the inorganic bonding solution in cylinder A to cylinder B, stir at a speed of 1000r / min for 5min, then add aqueous synthetic resin emulsion and leveling agent and stir at a spe...

Embodiment 3

[0061] Materials and contents used in the present embodiment are as follows:

[0062]

[0063] Preparation of inorganic bonding solution: Add silica sol into cylinder A according to the formula, stir at a speed of 600r / min and heat up to 30°C, then add stabilizer, stir at a speed of 400r / min for 10min, then add sodium silicate, Stir at a speed of 800r / min for 30min, and obtain an inorganic bonding solution in cylinder A for later use.

[0064] Prepare the paint slurry: add pH adjuster, dispersant, wetting agent, defoamer, thickener and deionized water into cylinder B according to the formula amount, stir at 1100r / min for 10min; then add pigments and fillers into cylinder B , disperse at 1500r / min for 20min, test the fineness of the millbase ≤ 50μm, and obtain the millbase,

[0065] Mixing steps: add the inorganic bonding solution in cylinder A to cylinder B, stir at a speed of 1000-1200r / min for 10min, then add water-based synthetic resin emulsion, leveling agent and stir ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention provides organic and inorganic compound waterborne paint for exterior walls and a preparation method thereof. The paint comprises waterborne synthetic resin, an inorganic cementitious material, a stabilizing agent, an auxiliary agent, a pigment and filler, and water, wherein the waterborne synthetic resin is pure acrylic emulsion modified by ultraviolet crosslinking, the inorganic cementitious material is a mixer of silicate and silica sol, and the stabilizing agent is siloxane. The organic and inorganic compound waterborne paint for exterior walls has good film forming effects, appropriate flexibility, extremely good adhesive force for surface of an object, good stability, as well as extremely good weatherability, wear resistance, and moisture and heat resistance; and the paint can satisfy demands of multiple respects.

Description

technical field [0001] The invention relates to the field of chemical materials, in particular to the field of coatings, in particular to an organic-inorganic composite exterior wall water-based coating and a preparation method thereof. Background technique [0002] At present, most exterior wall paints are mainly organically synthesized emulsions, which are easy to construct, rich in decoration and color, but harmful substances volatilize during production and construction, and have excellent performance in weather resistance, heat and humidity resistance and adhesion. Poor, easy to receive ultraviolet light and aging. Moreover, the dense coating seals the wall and prevents water vapor from penetrating, resulting in shedding. However, pure inorganic coatings have the disadvantages of poor stability and poor decoration, which are not convenient for large-scale promotion and use. [0003] CN101117477A discloses a method for preparing an organic-inorganic composite waterproo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D1/04C09D7/12
Inventor 陈向新胡中源郑毅崔晶晶赵娟崔佳慧
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap