Production method of a soft-light glazed brick

A production method and technology for polishing glazed tiles, applied in the field of architectural ceramics, can solve the problems of reducing surface gloss, affecting decoration, easy to absorb dirt, etc., and achieving the effect of stable glaze gloss and delicate glaze

Inactive Publication Date: 2017-08-11
GUANGXI UNIV
View PDF5 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, although the surface gloss is reduced in this way, soft products can be obtained, but due to serious surface scratches, these scratches affect the decoration, and are particularly easy to absorb dirt
Not conducive to cleaning service after use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A method for producing soft-gloss polished glazed tiles, comprising the following steps: preparing a soft-gloss polished glazed tile body according to a conventional method, preparing a soft-gloss polished glazed tile base glaze and a top glaze, applying the base glaze, drying, applying the top glaze, and drying And firing, polishing, picking, packaging, storage.

[0016] Further, the material of the bottom glaze includes the following raw materials in mass percentage: 30% of potassium feldspar, 22% of albite, 10% of kaolin, 25% of quartz, 8% of talc, and 5% of alumina; The glaze material includes the following raw materials in mass percentage: 38% potassium feldspar, 27% wollastonite, 6% calcite, 8% quartz, 7% kaolin, 2% zinc oxide, 9% barium carbonate and 3% dolomite ;

[0017] Further, the specific method of the polishing treatment is as follows: (1) use the elastic grinding block as the polishing machine for the polishing mold, and use the resin-bonded emery abrasi...

Embodiment 2

[0019] A method for producing soft-gloss polished glazed tiles, comprising the following steps: preparing a soft-gloss polished glazed tile body according to a conventional method, preparing a soft-gloss polished glazed tile base glaze and a top glaze, applying the base glaze, drying, applying the top glaze, and drying And firing, polishing, picking, packaging, storage.

[0020] Further, the material of the bottom glaze includes the following raw materials in mass percentage: 32% of potassium feldspar, 20% of albite feldspar, 12% of kaolin, 23% of quartz, 9% of talc, and 4% of alumina; The material of the glaze includes the following raw materials in mass percentage: 40% potassium feldspar, 25% wollastonite, 7% calcite, 7% quartz, 5% kaolin, 2% zinc oxide, 9% barium carbonate and 5% dolomite , all the other are identical with embodiment 1.

Embodiment 3

[0022] A method for producing soft-gloss polished glazed tiles, comprising the following steps: preparing a soft-gloss polished glazed tile body according to a conventional method, preparing a soft-gloss polished glazed tile base glaze and a top glaze, applying the base glaze, drying, applying the top glaze, and drying And firing, polishing, picking, packaging, storage.

[0023] Further, the material of the bottom glaze includes the following raw materials in mass percentage: the bottom glaze formula is (parts by weight): 35% of potassium feldspar, 20% of albite feldspar, 10% of kaolin, 25% of quartz, and 5% of talc , alumina 5%; surface glaze formula (parts by weight): potassium feldspar 37%, wollastonite 26%, calcite 7%, quartz 5%, kaolin 7%, zinc oxide 2%, barium carbonate 9% and dolomite Stone 7%, all the other are identical with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of a soft-light glazed brick. The production method comprises steps as follows: (1), preparing a soft-light glazed brick green body with a conventional method; (2), preparing priming glaze and surface glaze of the soft-light glazed brick; (3), applying the priming glaze; (4), performing drying; (5), applying the surface glaze; (6), performing drying and sintering; (7), performing polish treatment; (8), performing selection, packaging and warehousing. The production method has the beneficial effects as follows: the problem of high probability of severe scratching and pollution absorption of soft-light treatment of an existing glazed brick is solved, and the production method of the soft-light glazed brick is better.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a production method of soft polished glazed tiles. Background technique [0002] With the continuous development of social economy, people's requirements for quality of life and living environment are also constantly improving, and decorative materials with natural stone imitation, simplicity and high grade have become the mainstream of consumption. Polished glazed tiles combine the advantages of polished tiles and antique tiles, which can realize the smooth and bright glazed surface like polished tiles, and can also achieve glazed decorative effects such as antique tiles with rich patterns and gorgeous colors. At present, glazed porcelain tiles, microcrystalline stones and antique porcelain tiles on the market have gradually become mainstream products in the market. Each series of products has its own advantages and disadvantages due to its different physical and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/89
CPCC04B41/52C03C8/02C04B41/89C04B41/504C04B41/0072C04B41/5022
Inventor 龚静
Owner GUANGXI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More