Jun red glaze

A red glaze, Jun red technology, applied in the field of glaze, can solve the problems of low yield and single glaze color, and achieve the effects of reducing firing temperature, increasing gloss and improving fluidity

Inactive Publication Date: 2017-08-08
禹州市神器钧窑有限公司
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The "copper red glaze" in Jun porcelain is famous for its crystal clear and even moisture. Jun red glaze is a kind of copper red glaze. , the glaze cloth has fine and dense cracks, bright and clean, but the existing glaze formula and firing process for firing Junhong glaze have a single glaze color and low yield

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Jun red glaze
  • Jun red glaze
  • Jun red glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A Junhong glaze prepared from the following raw materials in parts by weight: 37-43 parts of yellow feldspar, 13-19 parts of quartz, 10-16 parts of calcite, 4.5-5.5 parts of cyanine, 12-18 parts of frit, bovine bone 0.5-1.5 parts, 2.5-3.5 parts of tin oxide, 3.5-4.5 parts of zinc oxide, 2-3 parts of talc, 0.25-0.75 parts of copper oxide.

[0018] The preparation method of the above-mentioned Jun porcelain moon white glaze comprises the following steps:

[0019] (1) Take the raw materials in the above parts by weight, add water, put them into a ball mill, and pass through a 250-mesh sieve to obtain a glaze slurry;

[0020] (2) Glazing is applied on the biscuit body by dipping;

[0021] (3) Firing, the firing temperature is 1250-1280°C;

[0022] The firing process specifically includes the following steps: ①Pre-firing period: put the glazed green body into the kiln, and raise the temperature from room temperature to 540-580°C within 2-3 hours; ②Oxidation period: In an o...

Embodiment 2

[0025] A Junhong glaze prepared from the following raw materials in parts by weight: 40 parts of yellow feldspar, 16 parts of quartz, 13 parts of calcite, 5 parts of cyanine, 15 parts of frit, 1 part of bovine bone, 3 parts of tin oxide, and zinc oxide 4 parts, talc 2.5 parts, copper oxide 0.5 parts.

[0026] The preparation method of above-mentioned Junhong glaze comprises the following steps:

[0027] (1) Take the raw materials in the above parts by weight, add water, put them into a ball mill, and pass through a 250-mesh sieve to obtain a glaze slurry;

[0028] (2) Glazing is applied on the biscuit body by dipping;

[0029] (3) Firing, the firing temperature is 1270°C;

[0030] The firing process specifically includes the following steps: ①Pre-firing period: put the glazed body into the kiln, and raise the temperature from room temperature to 560°C within 2.5 hours; ②Oxidation period: in an oxidizing atmosphere, keep the temperature at 3.5 hours evenly rise to 1020°C; ③R...

Embodiment 3

[0033] A Junhong glaze prepared from the following raw materials in parts by weight: 40 parts of yellow feldspar, 16 parts of quartz, 13 parts of calcite, 5 parts of cyanine, 15 parts of frit, 1 part of bovine bone, 3 parts of tin oxide, and zinc oxide 4 parts, talc 2.5 parts, copper oxide 0.5 parts.

[0034] (1) Take the raw materials in the above parts by weight, add water, put them into a ball mill, and pass through a 250-mesh sieve to obtain a glaze slurry;

[0035] (2) Glazing is applied on the biscuit body by dipping;

[0036] (3) Firing, the firing temperature is 1250°C;

[0037] The firing process specifically includes the following steps: ①Pre-firing period: put the glazed green body into the kiln, and raise the temperature from room temperature to 540°C within 3 hours; ②Oxidation period: in an oxidizing atmosphere, keep the temperature at Evenly rise to 1030°C; ③Reduction period: When the temperature rises to 1030°C, open the damper of the kiln, let cold air flow i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Jun red glaze is prepared from the following raw materials in parts by weight: 37 to 43 parts of melilite, 13 to 19 parts of quartz, 10 to 16 parts of calcite, 4.5 to 5.5 parts of sodium metasilicate, 12 to 18 parts of frit, 0.5 to 1.5 parts of bovine-derived power, 2.5 to 3.5 parts of stannic oxide, 3.5 to 4.5 parts of zinc oxide, 2 to 3 parts of talc, and 0.25 to 0.75 part of copper oxide. Compared with the prior art, through scientific and reasonable raw material matching and control on the firing process, the prepared jun red glaze is bright in color, good in glossiness, and moderate in flowability, and has fine cracks, the glazing colors are rich, on the basis of jun red, the colors including yellow, blue, purple and the like exist, the color transition is clear, distinct and natural, the rate of finished products is high, reaching 75% or above, the blank of no colorful graze exists in jun red glaze is filled, and a new variety is provided for jun red glaze.

Description

technical field [0001] The invention relates to a glaze material, in particular to a Junhong glaze. Background technique [0002] Jun Porcelain is one of the five famous kiln porcelains of the Song Dynasty in my country. It is a treasure in the traditional Chinese porcelain making process. It is famous all over the world for its unique kiln transformation art. The "copper red glaze" in Jun porcelain is famous for its crystal clear and even moisture. Jun red glaze is a kind of copper red glaze. , the glaze cloth has fine and close cracks, bright and clean and translucent, but the glaze formula and firing process of the existing Junhong glaze fired Junhong glaze has a single glaze color and a low yield. Contents of the invention [0003] The objective of the present invention is just to provide a kind of Junhong glaze for solving the deficiencies in the prior art. [0004] The purpose of the present invention is achieved with the following technical solutions: [0005] A ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20
CPCC03C8/20C03C2204/04C03C2209/02
Inventor 张占领
Owner 禹州市神器钧窑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com