Golden-spot blue glaze

A technology of golden spot blue glaze and blue powder, which is applied in the field of glaze, can solve the problem of single glaze color of blue glaze, and achieve the effect of high yield and convenient firing temperature control

Inactive Publication Date: 2017-08-08
禹州市神器钧窑有限公司
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The "blue glaze" in Jun porcelain has a blue glaze color like the deep sea, and the glaze surface is uniform and stable in color. However, the glaze formula and firing process of the existing blue glaze firing blue glaze has a single glaze color and no gold on the glaze surface. spot

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Golden-spot blue glaze
  • Golden-spot blue glaze
  • Golden-spot blue glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A gold spot blue glaze, prepared from the following raw materials in parts by weight: 62-68 parts of feldspar, 10-16 parts of quartz, 12-18 parts of calcite, 1.5-2.5 parts of tin oxide, 0.5-1.5 parts of grouping, 0.5-1.5 parts of bovine bone powder, 1.5-2.5 parts of talc, and 0.5-1.5 parts of orchid powder.

[0020] The blue powder is composed of cobalt oxide and Datong soil, and the mass ratio of the cobalt oxide and Datong soil is 1:(9-11).

[0021] The blue powder is prepared by mixing cobalt oxide and Datong soil and calcining at 1150-1250° C. for 4-6 hours.

[0022] The preparation method of above-mentioned golden spot blue glaze, comprises the following steps:

[0023] (1) Take the raw materials in the above parts by weight, add water, put them into a ball mill, and pass through a 150-mesh sieve to obtain a glaze slurry;

[0024] (2) Glazing is applied on the biscuit body by dipping;

[0025] (3) Firing, the firing temperature is 1240-1280°C; specifically inclu...

Embodiment 2

[0027] A gold spot blue glaze prepared from the following raw materials in parts by weight: 65 parts of feldspar, 13 parts of quartz, 15 parts of calcite, 2 parts of tin oxide, 1 part of grouper, 1 part of bovine bone meal, 2 parts of talc, blue powder 1 serving.

[0028] The preparation method of above-mentioned golden spot blue glaze, comprises the following steps:

[0029] (1) Take the raw materials in the above parts by weight, add water, put them into a ball mill, and pass through a 150-mesh sieve to obtain a glaze slurry;

[0030] (2) Glazing is applied on the biscuit body by dipping;

[0031] (3) Firing, the firing temperature is 1260°C; specifically includes the following steps: put the body after glazing into the kiln, and make the temperature rise to 1260°C evenly in 2.5 hours; Cool down to 780°C at 7°C per minute; then cool naturally to room temperature. The firing atmosphere for the entire firing is an oxygen atmosphere.

[0032] The golden spot blue glaze glaz...

Embodiment 3

[0034] A gold spot blue glaze prepared from the following raw materials in parts by weight: 65 parts of feldspar, 13 parts of quartz, 15 parts of calcite, 2 parts of tin oxide, 1 part of grouper, 1 part of bovine bone meal, 2 parts of talc, blue powder 1 serving.

[0035] The preparation method of above-mentioned golden spot blue glaze, comprises the following steps:

[0036] (1) Take the raw materials in the above parts by weight, add water, put them into a ball mill, and pass through a 150-mesh sieve to obtain a glaze slurry;

[0037] (2) Glazing is applied on the biscuit body by dipping;

[0038] (3) Firing, the firing temperature is 1280°C; specifically includes the following steps: put the glazed green body into the kiln, and make the temperature rise to 1280°C evenly within 2 hours; Cool down to 800°C at 8°C per minute; then cool naturally to room temperature. The firing atmosphere for the entire firing is an oxygen atmosphere.

[0039] The glaze color of Jun porcela...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Golden-spot blue glaze is prepared from the following raw materials in parts by weight: 62 to 68 parts of melilite, 10 to 16 parts of quartz, 12 to 18 parts of calcite, 1.5 to 2.5 parts of stannic oxide, 0.5 to 1.5 parts of banhuashi (a kind of lean iron ore), 0.5 to 1.5 parts of bovine-derived power, 1.5 to 2.5 parts of talc and 0.5 to 1.5 parts of blue powder. Compared with the prior art, through scientific and reasonable raw material ratio and control on firing technique, the blue glaze with golden spots is prepared, the blank that the blue glaze has no golden spots is filled, and a new variety is provided for blue glaze jun porcelain; in addition, the golden-spot blue glaze prepared according to the invention is gorgeous, bright and smooth, the glaze surface has no pores and glaze missing, the firing temperature is convenient to control, and the rate of finished products is high, reaching 90% or above.

Description

technical field [0001] The invention relates to a glaze, in particular to a golden spot blue glaze. Background technique [0002] Jun Porcelain is one of the five famous kiln porcelains of the Song Dynasty in my country. It is a treasure in the traditional Chinese porcelain making process. It is famous all over the world for its unique kiln transformation art. The "blue glaze" in Jun porcelain has a blue glaze color like the deep sea, and the glaze surface is uniform and stable in color. However, the glaze formula and firing process of the existing blue glaze firing blue glaze has a single glaze color and no gold on the glaze surface. spot. Contents of the invention [0003] The purpose of the present invention is to provide a kind of golden spot blue glaze for solving the deficiencies of the prior art. [0004] The purpose of the present invention is achieved with the following technical solutions: [0005] A golden spot blue glaze, which is prepared from the following...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00
CPCC03C8/00C03C2204/04C03C2209/02
Inventor 张占领
Owner 禹州市神器钧窑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com