Bamboo cane anti-breakage treatment technology for plastic rattan seat

A treatment process and anti-fracture technology, which is applied in wood treatment, wood heat treatment, pressurized wood treatment, etc., can solve the problems of bamboo strips easy to break, low service life, and bamboo strips damage the skin, etc., to achieve tight connection of bamboo fibers, bright color effect

Inactive Publication Date: 2017-08-04
安徽持家汉家居工艺品有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now, many companies start to produce mixed weaving of plastic rattan and bamboo strips to enhance the artistic atmosphere of the woven products, but because the bamboo strips are easy to break, not only the service life is low, but also the bamboo strips will damage the skin.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] An anti-fracture treatment process for bamboo strips in a plastic rattan seat, comprising the following steps:

[0021] (1) felling the fresh bamboo between 5-6 months, then covering the bamboo with the pond silt that has been deposited for 2-3 years, and then covering the surface of the pond silt with yellow soil and burying it underground;

[0022] (2) Take out and clean the bamboo in February of the next year, then break the bamboo into bamboo strips, soak the bamboo strips in fresh bamboo leaf juice, and dry them with a dryer at 55°C after soaking for a week, then Send it into a 4MPa pressure vessel and pressurize it for 2 hours;

[0023] (3) handle finishes and bamboo stick is easily soaked with the ethyl acetate of 3.5% concentration;

[0024] (4) After soaking for 1 hour, the bamboo strips were pulled out and then soaked in dilute sulfuric acid solution with a concentration of 3.2%, and the bamboo strips were fumigated with ethanol steam for 10 minutes after soa...

Embodiment 2

[0032] An anti-fracture treatment process for bamboo strips in a plastic rattan seat, comprising the following steps:

[0033] (1) felling the fresh bamboo between 5-6 months, then covering the bamboo with the pond silt that has been deposited for 2-3 years, and then covering the surface of the pond silt with yellow soil and burying it underground;

[0034] (2) Take out and clean the bamboo in February of the next year, then break the bamboo into bamboo strips, soak the bamboo strips in fresh bamboo leaf juice, and dry them with a dryer at 50°C after soaking for a week. Send it into a pressure vessel of 3.5MPa and pressurize it for 2 hours;

[0035] (3) handle finishes and bamboo stick is easily soaked with the ethyl acetate of 3.5% concentration;

[0036] (4) After soaking for 1 hour, the bamboo strips were pulled out and then soaked in dilute sulfuric acid solution with a concentration of 3.2%, and the bamboo strips were fumigated with ethanol steam for 10 minutes after soa...

Embodiment 3

[0044] An anti-fracture treatment process for bamboo strips in a plastic rattan seat, comprising the following steps:

[0045] (1) felling the fresh bamboo between 5-6 months, then covering the bamboo with the pond silt that has settled for 2-3 years, and then covering the surface of the pond silt with yellow soil and burying it underground;

[0046] (2) Take out and clean the bamboo in February of the next year, then break the bamboo into bamboo strips, soak the bamboo strips in fresh bamboo leaf juice, and dry them with a dryer at 60°C after soaking for a week. Send it into a pressure vessel of 4.5MPa and pressurize it for 2 hours;

[0047] (3) handle finishes and bamboo stick is easily soaked with the ethyl acetate of 3.5% concentration;

[0048] (4) After soaking for 1 hour, the bamboo strips were pulled out and then soaked in dilute sulfuric acid solution with a concentration of 3.2%, and the bamboo strips were fumigated with ethanol steam for 10 minutes after soaking; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a bamboo cane anti-breakage treatment technology for a plastic rattan seat. The technology comprises the following steps that bamboo is covered with pond sludge deposited for 2-3 years, then the surface of the pond sludge is covered with yellow soil, and then the bamboo is buried underground; the bamboo is broken into bamboo canes, and the bamboo canes are immersed through fresh bamboo leaf juice and sent into a pressure container of 3.5-4.5 MPa to be pressurized for 2 h; treatment is over, the bamboo canes are easily immersed through ethyl acetate with the concentration being 3.5%; after immersing is conducted for 1 h, the bamboo canes are fished out and then immersed through a dilute sulfuric acid solution with the concentration being 3.2%; the bamboo canes are taken out and placed in a high-pressure chamber, and the pull force of 0.4-0.6 MPa is exerted on the bamboo canes in the high-pressure chamber; and glacial acetic acid is used for continuous cleaning, and airing is conducted. The treated bamboo canes are resistant to bending and scratching, the edges of the bamboo canes cannot be cracked, meanwhile, the treated bamboo canes are bright in color, bamboo cane fiber connection is tighter, the bamboo canes cannot contract under immersion of strong brine, and black spots cannot be generated under roast smoking of local flames with the temperature ranging from 300 DEG C to 350 DEG C.

Description

technical field [0001] The invention relates to the technical field of bamboo treatment, in particular to an anti-breakage treatment process for bamboo strips in a plastic rattan seat. Background technique [0002] Bamboo is a perennial lignified plant with aboveground stems (bamboo stems) and underground stems (bamboo whips). Bamboo stems are often cylindrical, rarely quadrangular, connected by internodes and nodes, internodes are often hollow, a few are solid, and nodes are composed of sheath rings and rod rings. Branches at each node. There are two kinds of leaves, one is cauline leaves, commonly known as sheath leaves; the other is vegetative leaves, lanceolate, and the size varies with varieties. Bamboo flowers are composed of scales, stamens and pistils. The fruit is mostly caryopsis. In the whole life of bamboo, most of the time is the vegetative growth stage, and once the flowers and fruits are set, all the bushes will die and complete a life cycle. [0003] Bec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27K9/00B27K5/00B27K3/52B27K3/08B27K3/34B27K3/16B27K3/12
CPCB27K9/002B27K3/08B27K3/12B27K3/16B27K3/34B27K3/52B27K5/00B27K5/007B27K5/0085
Inventor 王刚
Owner 安徽持家汉家居工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products