Surface chrome-plating process for minisize worm

A surface chrome plating and worm technology, which is applied in metal material coating process, sputtering plating, ion implantation plating, etc., can solve the problem that the gear cannot rotate the worm, etc., achieve smooth resistance, increase density, and chrome plating thickness increased effect

Inactive Publication Date: 2017-06-20
桥运精密部件(苏州)有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The worm gear and the worm are equivalent to the gear and the rack in their middle plane, and the worm is similar in shape to the screw. The worm can easily rotate the gear, but the gear cannot rotate the worm

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A surface chrome plating process for a miniature worm, comprising the steps of:

[0017] (a) Grinding burrs: Use water abrasive paper to polish the surface of the worm, especially the sharp edges and corners, so that no burrs are seen or the feel of no thorns is wiped with the thumb;

[0018] (b) Cleaning and degreasing: clean the worm after step (a) in clear water, then soak in 50% alcohol liquid for 5 minutes and drain;

[0019] (c) Surface treatment: place the worm treated in step (b) on the workpiece rack in the vacuum equipment, and adjust the vacuum degree in the vacuum equipment to 7-8X10 -3 After Pa, open the throttle valve, and make the workpiece holder rotate slowly, the rotation speed is 4r / min, then open the inert gas, use cathode magnetron sputtering for 4min, finally close the inert gas, and carry out 6min ionization under high vacuum conditions. Bombarded in chrome.

[0020] (d) Inspection: Take out the worm after the treatment in step (c), rinse it wit...

Embodiment 2

[0022] 1, a kind of surface chrome plating process of miniature worm, it is characterized in that: comprise the steps:

[0023] (a) Grinding burrs: Use water abrasive paper to polish the surface of the worm, especially the sharp edges and corners, so that no burrs are seen or the feel of no thorns is wiped with the thumb;

[0024] (b) cleaning and degreasing: clean the worm after step (a) in clear water, then soak in 80% alcohol liquid for 10 minutes and drain;

[0025] (c) Surface treatment: place the worm treated in step (b) on the workpiece rack in the vacuum equipment, adjust the vacuum degree in the vacuum equipment to 7-8X10-3Pa, open the throttle valve, and use The workpiece holder rotates slowly at a rotation speed of 5r / min, then turns on the inert gas, and uses cathode magnetron sputtering for 10 minutes, and finally turns off the inert gas, and conducts 10 minutes of ion bombardment chromium plating under high vacuum conditions;

[0026] (d) Inspection: Take out th...

Embodiment 3

[0028] 1, a kind of surface chrome plating process of miniature worm, it is characterized in that: comprise the steps:

[0029] (a) Grinding burrs: Use water abrasive paper to polish the surface of the worm, especially the sharp edges and corners, so that no burrs are seen or the feel of no thorns is wiped with the thumb;

[0030] (b) Cleaning and degreasing: After cleaning the worm treated in step (a) in clear water, place it in 60% alcohol liquid for 6 minutes and then drain it;

[0031] (c) Surface treatment: place the worm treated in step (b) on the workpiece rack in the vacuum equipment, adjust the vacuum degree in the vacuum equipment to 7-8X10-3Pa, open the throttle valve, and use The workpiece holder rotates slowly at a rotation speed of 5r / min, then turns on the inert gas, and uses cathode magnetron sputtering for 6 minutes, and finally turns off the inert gas, and conducts 8 minutes of ion bombardment chromium plating under high vacuum conditions;

[0032] (d) Inspe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A surface chrome plating process of a micro worm, comprising the following steps: (a) grinding burrs (b) cleaning and degreasing (c) surface treatment (d) inspection, the present invention adopts the vacuum chrome plating method to increase the density and stability of the chrome plating layer on the surface of the worm Chemical properties ensure the smooth surface of the worm with low resistance. Secondly, the thickness of the chrome plating layer increases, the wear resistance is good, and the service life of the worm is extended. At the same time, the chrome plating method has low pollution, and there is no chrome plating waste liquid, and there is no heavy metal chromium flowing into the environment. High economic and ecological benefits.

Description

technical field [0001] The invention relates to a chrome plating process for worms, in particular to a vacuum chrome plating process for micro worms. Background technique [0002] Worm gears are commonly used to transmit motion and power between two interleaved shafts. The worm gear and the worm are equivalent to the gear and the rack in the middle plane, and the worm is similar to the screw in shape. The worm can easily rotate the gear, but the gear cannot rotate the worm. This is because the lugs on the screw are so shallow that friction between the gear and the screw keeps the screw in place when the gear tries to turn it. As one of the commonly used components in electronic products, the micro worm is very easy to further reduce the diameter of the tooth groove or appear at the tooth groove due to long-term friction due to its small diameter and further reduction in the diameter of the tooth groove. Bending, so it is necessary to chrome-plate the outer surface of the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/16C23C14/35
CPCC23C14/35C23C14/165
Inventor 俞雅勤
Owner 桥运精密部件(苏州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com