High-strength and low-temperature-resistant plastic bucket and preparation method thereof

A plastic barrel, low temperature resistant technology, applied in the field of packaging materials, can solve the problem of impact strength of boring barrels and other problems, and achieve the effect of high strength

Inactive Publication Date: 2017-05-31
苏州纳贝通环境科技有限公司
View PDF7 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Technical problem to be solved: the purpose of this invention is to provide a high-strength low-temperature resistant plastic barrel, which can overcome the impact strength problem of existing boring barrels, and has good low-temperature toughness, good rigidity and tensile strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A high-strength and low-temperature-resistant plastic bucket, prepared from the following ingredients by weight: 100 parts of polyethylene, 10 parts of aramid fiber, 15 parts of basalt fiber, 0.1 part of dibenzylidene sorbitol, and 0.5 parts of ultraviolet absorber UV-326 0.4 parts of antioxidant 1010, 0.8 parts of antioxidant 168, 0.5 parts of oxidized polyethylene wax, 8 parts of active quartz powder, 10 parts of nano-modified epoxy resin, and 12 parts of glass fiber reinforced vinyl ester resin.

[0020] The preparation method of the above-mentioned high-strength and low-temperature-resistant plastic barrel is as follows: (1) Put polyethylene, nano-modified epoxy resin, and glass fiber-reinforced vinyl ester resin in a mixer, and stir for 40 minutes at a temperature of 125°C, and mix (2) Then add aramid fiber, basalt fiber, dibenzylidene sorbitol, ultraviolet absorber UV-326, antioxidant 1010, antioxidant 168, oxidized polyethylene wax, active quartz powder, and stir ...

Embodiment 2

[0022] A high-strength and low-temperature-resistant plastic bucket, prepared from the following ingredients in parts by weight: 80 parts of polyethylene, 20 parts of aramid fiber, 5 parts of basalt fiber, 0.4 part of dibenzylidene sorbitol, and 1.5 parts of ultraviolet absorber UV-326 parts, 0.8 parts of antioxidant 1010, 0.4 parts of antioxidant 168, 1.2 parts of oxidized polyethylene wax, 14 parts of active quartz powder, 18 parts of nano-modified epoxy resin, and 5 parts of glass fiber reinforced vinyl ester resin.

[0023] The preparation method of the above-mentioned high-strength and low-temperature-resistant plastic barrel is as follows: (1) Put polyethylene, nano-modified epoxy resin, and glass fiber-reinforced vinyl ester resin in a mixer, and stir for 20 minutes at a temperature of 100°C, and mix (2) Then add aramid fiber, basalt fiber, dibenzylidene sorbitol, ultraviolet absorber UV-326, antioxidant 1010, antioxidant 168, oxidized polyethylene wax, active quartz pow...

Embodiment 3

[0025] A high-strength and low-temperature-resistant plastic bucket, prepared from the following ingredients by weight: 88 parts of polyethylene, 18 parts of aramid fiber, 8 parts of basalt fiber, 0.2 part of dibenzylidene sorbitol, and 0.8 part of ultraviolet absorber UV-326 parts, 0.5 parts of antioxidant 1010, 0.7 parts of antioxidant 168, 0.8 parts of oxidized polyethylene wax, 10 parts of active quartz powder, 14 parts of nano-modified epoxy resin, and 8 parts of glass fiber reinforced vinyl ester resin.

[0026] The preparation method of the above-mentioned high-strength and low-temperature-resistant plastic bucket is as follows: (1) Put polyethylene, nano-modified epoxy resin, and glass fiber-reinforced vinyl ester resin in a mixer, and stir for 25 minutes at a temperature of 110°C, and mix (2) Then add aramid fiber, basalt fiber, dibenzylidene sorbitol, ultraviolet absorber UV-326, antioxidant 1010, antioxidant 168, oxidized polyethylene wax, active quartz powder, and s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-strength and low-temperature-resistant plastic bucket and a preparation method thereof. The preparation method comprises the following steps: (1) putting polyethylene, nano-modified epoxy resin and glass-fiber-reinforced vinyl ester resin into a mixer, and evenly stirring and mixing at certain temperature; (2) sequentially adding aramid fibers, basalt fibers, dibenzylidene sorbitol, an ultraviolet light absorber UV-326, an antioxidant 1010, an antioxidant 168, oxidized polyethlene wax and activated quartz powder into the mixer, and evenly stirring and mixing; (3) heating an obtained mixture, putting the heated mixture into a double-screw extruder and extruding plastic particles; (4) putting the plastic particles into an extrusion hollow blow molding machine, and extruding a tubular blank material; (5) putting the tubular blank material into a mould of the extrusion hollow blow molding machine, controlling the temperature of the mould and the pressure of the compressed air, and carrying out hollow blowing to obtain the plastic bucket. The plastic bucket provided by the invention is good in low temperature impact resistance and tensile strength, is non-toxic and harmless, and simple and practicable in technology.

Description

technical field [0001] The invention relates to the field of packaging materials, in particular to a high-strength and low-temperature resistant plastic bucket and a preparation method thereof. Background technique [0002] Plastic barrels are mostly used for the storage and transportation of various liquids, and have good characteristics for special dangerous goods packaging. They are not fragile, rust-free, light in weight, etc., and are resistant to oil and strong corrosion. They are mostly used for heat preservation and moisture-proof , pressure-resistant and corrosion-resistant dangerous goods packaging. Plastic barrels are mostly made of polyethylene, polypropylene, polyester and other plastic blow molding, injection molding, blister molding, and rotational molding. They are mostly used to hold liquid and solid items in industries such as chemicals, pesticides, medicine, food, hardware, electronics, and electromechanical industries. . The main raw material for the pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L77/06C08L23/30C08L63/00C08L63/10C08K13/04C08K7/10C08K5/134C08K5/526C08K3/36C08K7/14
CPCC08L23/06C08L2205/035C08L77/06C08L23/30C08L63/00C08L63/10C08K13/04C08K7/10C08K5/1345C08K5/526C08K3/36C08K7/14
Inventor 潘明华
Owner 苏州纳贝通环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com