A high-brightness and high-stiffness reflective film and its preparation method

A high-stiffness, reflective film technology, applied in the direction of instruments, optics, optical components, etc., can solve the problems of scratching the light guide plate and low stiffness of the reflective film, achieve uniform luminance of reflected light, improve luminance and its uniformity , a wide range of effects

Active Publication Date: 2018-08-03
NINGBO CHANGYANG TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that the stiffness of the reflective film in the existing display is not high and the light guide plate will be scratched during use, the present invention provides a reflective film with high luminance and high stiffness and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-brightness and high-stiffness reflective film and its preparation method
  • A high-brightness and high-stiffness reflective film and its preparation method
  • A high-brightness and high-stiffness reflective film and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0062] A preparation method of a high-brightness and high-stiffness reflective film provided by the present invention comprises the following steps:

[0063] (1) Prepare inorganic particle resin masterbatch, mix and granulate inorganic particles and carrier resin materials to obtain inorganic particle resin masterbatch; use three-layer co-extrusion for casting, longitudinal stretching, transverse stretching, heat setting, cooling , traction, winding and slitting to obtain the reflective thin layer.

[0064] (2) Coat one side of the reflective layer with a hardened layer online, and dry in an oven at 100°C-120°C for 1min-2min.

[0065] (3) Wet coating method is used to coat the prepared coating solution containing scattering particles on the other side of the reflective layer, and use a high-pressure mercury lamp to 2 Radiation curing.

[0066] The reflective film prepared by the present invention is tested according to the following method:

[0067] Reflectance: According t...

Embodiment 1

[0072] The high-brightness and high-stiffness reflective film provided by the present invention is composed of a reflective layer, a hardened layer, and a coated particle layer; the upper surface of the reflective layer is coated with a coated particle layer , the lower surface of the reflective layer is coated with a hardened layer; the coating particle layer includes adhesive resin and diffusion particles, and the diffusion particles are bonded to the surface of the reflective layer through the adhesive resin; the diffusion particles include large Particles and small particles. Wherein, the thickness of the hardened layer is 15 μm, the thickness of the reflective layer is 170 μm, and the total thickness of the reflective film is 225 μm.

[0073] The polyester resin in the reflective layer is PET with a content of 70%, the incompatible carrier resin is polyolefin with a content of 15%, and the inorganic particles are rutile titanium dioxide with a content of 15%;

[0074] Th...

Embodiment 2

[0081] High-brightness high-stiffness reflective film as provided in Example 1, wherein,

[0082] The thickness of the hardened layer is 15 μm, the thickness of the reflection layer is 170 μm, and the total thickness of the reflection film is 225 μm.

[0083] The polyester resin in the reflective layer is PET with a content of 70%, the incompatible carrier resin is polyolefin with a content of 15%, and the inorganic particles are rutile titanium dioxide with a content of 15%;

[0084] The reflective layer is an ABA three-layer co-extruded structure, wherein the thickness of the A layer accounts for 10% of the total thickness of the reflective layer, and the thickness of the B layer accounts for 90% of the total thickness of the reflective layer.

[0085] The hardened layer comprises a UV-curable resin glue and a UV curing agent, the UV-curable resin glue is selected from acrylic resin with a content of 75%, and the UV curing agent is selected from an epoxy resin curing agent w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of optical thin films, in particular to a high-brightness and high-stiffness reflective film for a backlight module and a preparation method thereof. In order to solve the problem that the stiffness of the reflective film in the existing display is not high and the light guide plate will be scratched during use, the present invention provides a reflective film with high luminance and high stiffness and a preparation method thereof. The high-brightness and high-stiffness reflective film is composed of a reflective layer, a hardened layer, and a coated particle layer; the upper surface of the reflective layer is coated with a coated particle layer, and the lower surface of the reflective layer is coated with a hardened layer ; The coating particle layer includes adhesive resin and diffusion particles, and the diffusion particles are bonded on the surface of the reflective layer through the adhesive resin; the diffusion particles include large particles and small particles, and the particle size of the small particles is 1-10 μm; the particle size of the large particles is 30-60 μm. The reflective film provided by the invention has high stiffness, does not adhere to the light guide plate, and does not scratch the light guide plate.

Description

technical field [0001] The invention relates to the technical field of optical thin films, in particular to a high-brightness and high-stiffness reflective film for a backlight module and a preparation method thereof. Background technique [0002] The backlight module for display includes light source, light guide plate, reflective film, brightness enhancement film, diffusion film, etc. The function of the reflective film is to reflect the light leaked from the bottom of the light guide plate back into the system as efficiently as possible, thereby improving the utilization rate of light ,Reduce energy consumption. [0003] For the rapidly developing reflective film for liquid crystal display, it is required to improve the reflective properties of the reflective film while reducing the cost. If the brightness of the backlight can be increased by improving the reflective properties of the reflective film, the cost can be reduced. Due to the internal foam structure, the trad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02B1/10G02F1/1335
CPCG02B1/10G02F1/133605
Inventor 金亚东裴旺
Owner NINGBO CHANGYANG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com