Preparation method of porous carbon nanotube

A technology of carbon nanotubes and nanotubes, applied in the field of preparation of porous carbon nanotubes, which can solve the problems of small specific surface area, limited application range, and easy aggregation of carbon nanotubes

Active Publication Date: 2017-05-17
TAIYUAN UNIV OF TECH
View PDF1 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional carbon nanotubes are easy to agglomerate, have poor dispersion, and small specific surface area, which limits their application range; carbon nanotubes are porous, can maintain high chemical stability, electrical conductivity, have large specific surface area, and rich pore structure. It is difficult to prepare and is under scientific research

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of porous carbon nanotube
  • Preparation method of porous carbon nanotube
  • Preparation method of porous carbon nanotube

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0097] The present invention will be further described below in conjunction with accompanying drawing:

[0098] figure 1 As shown in Fig. 1 , it is a state diagram for the preparation of porous carbon nanotubes. The position and connection relationship of each part must be correct, the ratio should be proportioned, and the operations should be performed in sequence.

[0099] The preparation of porous carbon nanotubes is carried out in a three-necked flask, and is completed under water bath, stirring, water circulation condensation, and argon protection; its preparation state is: the three-necked flask 3 is placed on the water bathtub 2, and the water bathtub 2 is placed on the On the electric heating stirrer 1, display screen 4, indicator light 5, power switch 6, stirrer controller 19 are arranged on the electric heating stirrer 1; Water bath water 16 is in the water bathtub 2; Argon tube 9, stirring Device 10, water circulation condensing pipe 11; Argon gas pipe 9 connects a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a porous carbon nanotube, and aims to solve the problems of easiness in agglomeration, poor dispersity and small specific surface area of a carbon nanotube. The porous carbon nanotube is prepared from a carbon nanotube serving as a raw material through solution preparation, ultrasonic dispersion treatment, acid oxidation, freeze drying, vacuum sintering, acid soaking, washing-suction filtration and drying in vacuum. The preparation method has the advantages of advanced and rapid process, and accurate and abundant data; a product is black powder with the particle diameter of less than or equal to 60nm; pores are uniformly distributed in the surface of the carbon nanotube, and the pore diameters are less than or equal to 10nm; the product purity is up to 99.5 percent, and the specific surface area is increased by 520 percent; the method is an advanced method for preparing the porous nanotube tube.

Description

technical field [0001] The invention relates to a method for preparing porous carbon nanotubes, which belongs to the technical field of preparation and application of organic carbon materials. Background technique [0002] Carbon nanotubes have excellent mechanical, electrical and chemical properties, and show broad application prospects in energy storage, lithium batteries and other fields. [0003] Traditional carbon nanotubes are easy to agglomerate, have poor dispersion, and small specific surface area, which limits their application range; carbon nanotubes are porous, can maintain high chemical stability, electrical conductivity, have large specific surface area, and rich pore structure. It is difficult to prepare and is under scientific research. Contents of the invention [0004] purpose of invention [0005] The purpose of the present invention is aimed at the situation of background technology, with carbon nanotube as raw material, through preparation solution, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B32/168
CPCC01P2004/64C01P2006/16C01P2006/80
Inventor 刘伟峰刘旭光杨永珍郭俊杰许并社
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com