A kind of molecular sieve catalyst for the catalytic cracking of MTP by-product hydrocarbons and its preparation method

A technology of molecular sieves and catalysts, which is applied in the field of molecular sieve catalysts and their preparation, can solve problems such as separation difficulties, thermal stability and hydrothermal stability reduction of nano-molecular sieves, and achieve rich structural features, good catalytic cracking effect, and reduction of side effects such as aromatics. The effect of product formation

Active Publication Date: 2019-07-23
CHNA ENERGY INVESTMENT CORP LTD +2
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, nano-ZSM-5 molecular sieves are easy to aggregate and difficult to separate, and the thermal stability and hydrothermal stability of nano-molecular sieves will be greatly reduced.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of molecular sieve catalyst for the catalytic cracking of MTP by-product hydrocarbons and its preparation method
  • A kind of molecular sieve catalyst for the catalytic cracking of MTP by-product hydrocarbons and its preparation method
  • A kind of molecular sieve catalyst for the catalytic cracking of MTP by-product hydrocarbons and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-16

[0080] II. The hydrocarbon cracking catalytic performance evaluation of the modified ZSM-5 molecular sieve catalyst obtained in embodiment 1-16

[0081] The properties of the modified ZSM-5 molecular sieve catalysts obtained in Examples 1-16 were investigated by catalytic cracking of the model compound n-hexane. The catalytic cracking reaction was evaluated in a continuous small fixed-bed reactor. The reaction tube is a φ10mm×430mm quartz tube, the catalyst loading is 0.5-2.0g, the reaction temperature is 550-650°C, and the space velocity is 1-3.0h -1 , the system pressure is normal pressure. The SP-3420 gas chromatograph was used for on-line analysis, and the organic composition in the product was detected by a hydrogen flame ionization detector, and a small amount of dry gas generated during the reaction was ignored. Before the reaction starts, the catalyst is firstly activated under the condition that N 2 The molecular sieve bed was purged for 1 h at a flow rate of 50 L / ...

Embodiment 17

[0084] At normal pressure, the temperature is 625°C, the catalyst loading is 2.0g, and the space velocity is 3h -1 Under the condition, examine different TPXA among the embodiment 1-4 + The catalytic cracking performance of ZSM-5 molecular sieve synthesized by the added amount on n-hexane, and the evaluation results are shown in Table 5.

Embodiment 18

[0086] At normal pressure, the temperature is 625°C, the catalyst loading is 2.0g, and the space velocity is 3h -1 Under certain conditions, the catalytic cracking performance of ZSM-5 molecular sieves with different silicon-aluminum ratios in Examples 5-8 on MTP by-product hydrocarbons was investigated, and the evaluation results are shown in Table 6.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a molecular sieve catalyst for catalytic cracking of MTP (methanol to propylene) by-product hydrocarbons and a preparation method of the molecular sieve catalyst, and particularly relates to a preparation method of a modified ZSM-5 molecular sieve catalyst. The method comprises the steps as follows: a, preparing and synthesizing silica-alumina gel from a silicon source, an aluminum source, an organic templating agent, alkali and deionized water, performing hydrothermal crystallization on the silica-alumina gel in a closed reaction vessel to obtain a modified ZSM-5 molecular sieve precursor; b, adding an aqueous solution of organosilane ammonium salt TPXA+ to the obtained precursor and mixing the mixture uniformly; c, adjusting the pH of the system obtained in step b to be 10-12 and continuing crystallization at 150-180C; d, exchanging and calcining the product obtained in the step c to obtain a final product. The catalyst is used for catalytic cracking of MTP by-product hydrocarbons, and has the advantages of high selectivity of lower olefins, long service life and the like.

Description

technical field [0001] The invention belongs to the technical field of catalysts, and in particular relates to a molecular sieve catalyst used for catalytic cracking of MTP by-product hydrocarbons and a preparation method thereof. Background technique [0002] With the development of the global economy, the demand for low-carbon olefins is increasing, and oil resources are increasingly scarce. The recent implementation of the coal-based methanol-to-olefins (MTP) project can effectively alleviate the shortage of naphtha and low-carbon oil in my country. The degree of dependence of olefins on the international market. MTP technology uses coal as raw material to produce propylene through dehydration of methanol and dimethyl ether. It is currently the most mature and economical production technology to replace petroleum route to produce propylene. The by-products are gasoline, liquefied gas and a small amount of ethylene and other hydrocarbons. compound. [0003] As a new chemi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J29/40C07C4/06C07C11/04C07C11/06C07C11/08
CPCY02P20/52
Inventor 巩雁军
Owner CHNA ENERGY INVESTMENT CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap