Adhesive composition

A composition and adhesive technology, which is applied in the direction of adhesives, polymer adhesive additives, film/sheet adhesives, etc., can solve problems such as insufficient cohesive force, and achieve the effect of shortening the curing time

Active Publication Date: 2017-05-10
DOW GLOBAL TECH LLC
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the other hand, if the adhesive composition cures too slowly, there may be insufficient cohesion during the further processing steps of the bonded assembly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive composition
  • Adhesive composition
  • Adhesive composition

Examples

Experimental program
Comparison scheme
Effect test

example

[0198] 1. Preparation of PBPE

[0199] Two PBPEs were prepared using hafnium metal complexes of polyvalent aryloxyether catalysts.

[0200] Catalyst B is a hafnium metal complex of a polyvalent aryloxyether catalyst, which is [[2',2"'-[1,3-propanediylbis(oxyl-KO)]bis-{3-[ 9H-3,6-bis-(1,1-dimethylethyl)-carbazol-9-yl]}-5'-fluoro-5-(1,1,3,3-tetramethylbutyl )-[1,1'-biphenyl]-2-hydroxyl-KO]](2-)]dimethyl hafnium.

[0201] Table 1 below provides the name and structure of Catalyst B.

[0202] Table 1 - Hafnium metal complexes of polyvalent aryloxyether catalysts

[0203]

[0204]Each PBPE is made according to the following procedure. Catalyst B and co-catalyst component solutions were metered using pumps and mass flow meters and combined with the catalyst rinse solvent and introduced into the bottom of the reactor. The co-catalyst used is a long-chain alkyl ammonium borate approximately equal in stoichiometry to methyl di(octadecyl) ammonium tetrakis(pentafluorophenyl) bora...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
secant modulusaaaaaaaaaa
meltaaaaaaaaaa
meltaaaaaaaaaa
Login to View More

Abstract

The present disclosure provides an adhesive composition. The adhesive composition includes: A) a propylene based plastomer or elastomer (PBPE) comprising up to 15 wt % units derived from ethylene and having (i) a Koenig B-value less than 1.0; (ii) a total unsaturation per mole of propylene from 0.010% to 0.030%; (iii) a density from 0.860 g / cc to 0.890 g / cc; (iv) a melt viscosity at 177 DEG C from 1,000 mPa.s to 15,000 mPa.s; and (v) a weight average molecular weight from 20,000 to 50,000 g / mole.

Description

[0001] References to related applications [0002] This application claims priority to U.S. Provisional Application Serial No. 62 / 040,143, filed August 21, 2014, which is incorporated herein by reference to the extent the language does not conflict with the content of this application. Background technique [0003] Adhesive compositions have a curing temperature, which is a key parameter affecting the utility of the adhesive composition for a given application. If the adhesive composition cures too quickly, its ability to form an effective bond is compromised. On the other hand, if the adhesive composition cures too slowly, there may be insufficient cohesive force during the further steps of processing the bonded assembly. [0004] The art recognizes the need for adhesive compositions that have shorter cure times and can maintain suitable cohesion. Contents of the invention [0005] The present invention relates to an adhesive composition comprising PBPE (propylene based ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/16C09J11/08C09J7/21C09J7/30
CPCC09J11/08C09J123/16C08L2314/06C08L23/142C09J7/30C09J7/21C08F210/06C08F4/65908C08F4/65912C08F4/64193C08F2/06C08F210/16C08F2500/03C08F2500/02C08F2500/15C08F2500/17C08F2500/22C08F2500/27C08F2500/34C09J2301/312C08L23/16B32B5/022B32B7/12B32B2405/00C08F10/06C08F2500/08C08F2800/20C09J123/12C09J2400/263C09J2423/16
Inventor A·W·麦克林纳格罕金怡K·布朗
Owner DOW GLOBAL TECH LLC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com