Luminescent glass

A technology of luminescent glass and raw materials, applied in the field of glass, can solve the problems of low luminous efficiency and achieve the effects of high brightness, simple formula and high transparency

Inactive Publication Date: 2017-05-10
QINZHOU ZHONGBO GLASS CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the luminous efficiency of the current luminescent glass is still low under the excitation of cathode rays

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A luminescent glass is made of the following raw materials in parts by weight: 70 parts of silicon dioxide, 10 parts of aluminum oxide, 8 parts of sodium oxide, 3 parts of sodium phosphate, 0.7 part of thulium oxide, 0.2 part of samarium oxide, and 0.21 part of neodymium oxide.

[0020] The above-mentioned preparation method of luminescent glass comprises the following preparation steps:

[0021] 1) Weigh the raw materials according to the following parts by weight (the purity of all the raw materials is 99%), add absolute ethanol, use agate as the medium, and ball mill for 18 hours,

[0022] 2) Dry, pass through a 115-mesh sieve, and heat at 1200°C for 30 minutes to melt into a uniform glass liquid;

[0023] 3) The molten glass is quickly poured into shape, and then kept in an annealing furnace at 650° C. for 2 hours and then cooled to room temperature to obtain a luminescent glass.

[0024] Performance parameters: Applicable environment -35 ℃ ~ 90 ℃; light transmissi...

Embodiment 2

[0026] A luminescent glass is made of the following raw materials in parts by weight: 65 parts of silicon dioxide, 12 parts of aluminum oxide, 7 parts of sodium oxide, 4 parts of sodium phosphate, 0.6 part of thulium oxide, 0.4 part of samarium oxide, and 0.18 part of neodymium oxide.

[0027] The above-mentioned preparation method of luminescent glass comprises the following preparation steps:

[0028] 1) Weigh the raw materials according to the following parts by weight (the purity of all the raw materials is 99%), add absolute ethanol, use agate as the medium, and ball mill for 19 hours,

[0029] 2) Dry, pass through a 130-mesh sieve, and heat at 1210°C for 50 minutes to melt into a uniform glass liquid;

[0030] 3) The molten glass is rapidly poured into shape, and then kept in an annealing furnace at 660° C. for 3 hours and then cooled to room temperature to obtain a luminescent glass.

[0031] Performance parameters: Applicable environment -35 ℃ ~ 90 ℃; light transmissi...

Embodiment 3

[0033] A luminescent glass is made of the following raw materials in parts by weight: 60 parts of silicon dioxide, 14 parts of aluminum oxide, 6 parts of sodium oxide, 5 parts of sodium phosphate, 0.5 part of thulium oxide, 0.6 part of samarium oxide, and 0.15 part of neodymium oxide.

[0034] The above-mentioned preparation method of luminescent glass comprises the following preparation steps:

[0035] 1) Weigh the raw materials according to the following parts by weight (the purity of all the raw materials is 99%), add absolute ethanol, use agate as the medium, and ball mill for 20 hours,

[0036] 2) Dry, pass through a 140-mesh sieve, and heat at 1220°C for 60 minutes to melt into a uniform molten glass;

[0037] 3) The molten glass is quickly poured into shape, then kept in an annealing furnace at 670° C. for 2 hours, and then cooled to room temperature to obtain a luminescent glass.

[0038] Performance parameters: Applicable environment -30 ℃ ~ 90 ℃; light transmission ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of glass, and particularly relates to luminescent glass. The luminescent glass is prepared from the following raw materials in parts by weight: 40 to 70 parts of silicon dioxide, 10 to 22 parts of aluminum oxide, 2 to 8 parts of sodium oxide, 3 to 9 parts of sodium phosphate, 0.1 to 0.7 part of thulium oxide, 0.2 to 1.4 parts of samarium oxide and 0.03 to 0.21 part of neodymium oxide. The luminescent glass disclosed by the invention is high in transparency and high in light efficiency; light rays are uniform, stable, and high in brightness.

Description

technical field [0001] The invention belongs to the technical field of glass, in particular to a luminescent glass. Background technique [0002] As far as the applicant knows, some of the luminous glass currently on the market are embedded with LED lights in the glass, and some are made of hollow glass, and then the LED lights are placed in the hollow layer; the luminous glass products designed by these technical solutions are more dazzling. The light-emitting surface is not uniform enough, there are obvious dark areas, it is not beautiful enough, and maintenance is very troublesome. [0003] In traditional light-emitting devices, the light-emitting materials used generally include phosphors, nanocrystals, and glass. At present, low-voltage phosphors are mainly used as luminescent materials. However, phosphors need to be crushed and washed before coating, and necessary heat treatment is required after coating, which leads to a decrease in the luminescent performance of pho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C4/12C03C6/04C03C4/08
CPCC03C4/12C03C1/00C03C4/0092C03C4/082C03C4/085
Inventor 庞会军
Owner QINZHOU ZHONGBO GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap