A kind of solar double-glass photovoltaic module lamination edge sealing tape and preparation method thereof

A double-glass photovoltaic and module layer technology, applied in coatings, adhesives, pressure-sensitive films/sheets, etc., to achieve good adhesion and compliance

Active Publication Date: 2019-02-26
YANTAI DARBOND TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the shortcomings of the existing double-glass photovoltaic module sealing tape, the present invention provides a solar double-glass photovoltaic module lamination edge sealing tape and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of solar double-glass photovoltaic module lamination edge sealing tape and preparation method thereof
  • A kind of solar double-glass photovoltaic module lamination edge sealing tape and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] The principles and features of the present invention are described below in conjunction with examples, which are only used to explain the present invention and are not intended to limit the scope of the present invention.

[0027] The used raw materials of embodiment 1-5 are as shown in table 1:

[0028] Table 1: The kind of raw material that embodiment 1-5 uses

[0029]

[0030] Table 2: Performance test data of the edge banding tape obtained in Examples 1-5

[0031] Glue viscosity / mPas

3450

4400

2350

3742

5820

Tape thickness / μm

30

30

30

30

30

Peel strength / N / mm

0.75

1.10

0.60

0.58

0.62

Holding power / h

＞72

＞72

＞72

＞72

＞72

Heat resistance / min, 150℃

＞60

＞60

＞60

＞60

＞60

air permeability

OK

OK

OK

OK

OK

[0032] The preparation method of the edge sealing tape of embodiment 1-5 is as follows:

[0033] First, 10wt% of the total a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a solar double-glass photovoltaic module lamination edge sealing tape, which comprises a base material layer and a pressure-sensitive adhesive layer located thereon, and the pressure-sensitive adhesive comprises the following components in parts by weight: 70-90 parts of soft monomer , 1-20 parts of hard monomer, 0.5-5 parts of polymerization initiator, 1-2 parts of crosslinking agent, 0.1-0.5 parts of antioxidant, 1-5 parts of baking porogen. The edge-sealing adhesive tape of the present invention has good adhesiveness and compliance to the glass substrate, and the presence of the baking porogen makes it possible to use the volatilization of water vapor to produce uniform through holes on the colloid during baking, thereby realizing the breathable function and solving the problem of The problems caused by the physical method of ordinary high-temperature tape drilling; after using this edge-sealing tape, there is no need to cut the edge, and the tape is torn off directly after lamination, and the overflowing polymer is taken away at the same time, reducing the labor intensity of workers and reducing the existing seal. Reduce the cost of edge tape, solve appearance problems such as burrs, and achieve the requirement of uniform edge thickness of double-glass modules.

Description

technical field [0001] The invention relates to an edge-sealing tape, in particular to a solar double-glass photovoltaic module lamination edge-sealing tape and a preparation method thereof, belonging to the technical field of solar double-glass photovoltaic modules. Background technique [0002] In the production process of photovoltaic cell modules, the edge protection is generally realized by aluminum alloy frames, and the sealing is done by silica gel or adhesive tape. With prominent performance advantages, it has gradually become a mainstream product in the photovoltaic market. Compared with traditional modules, ultra-thin double-glass modules use glass backplanes, which have the advantages of light weight, long life, reduced potential-induced degradation (PID) cracks, no snail marks, and high fire protection rating. In the current lamination process of solar double-glass photovoltaic modules, crystalline silicon cells are stacked in the module. After the lamination op...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J7/04C08J7/02C09J133/08C09J11/08C08F220/18C08F220/28C08F220/06
CPCC09J7/21C09J7/22C09J7/38C09J11/08C09J133/08C08F220/18C08F220/1804C08L51/02C08F220/281C08F220/06
Inventor 薛兴旺王建斌陈田安解海华
Owner YANTAI DARBOND TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap