Anti-bacterial polyvinyl chloride (PVC) material and preparation method thereof

The technology of polyvinyl chloride and inorganic antibacterial agent is applied in the field of antibacterial polyvinyl chloride material and its preparation, which can solve the problems of low antibacterial efficiency, waste of resources and high price, so as to improve the antibacterial effect, reduce the cost of raw materials, and improve the impact resistance performance. Effect

Inactive Publication Date: 2017-03-15
SHANGHAI ZHENTUO IND CO LTD
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Commonly used antibacterial modified materials are silver ion antibacterial agents. Although silver ion antibacterial agents have good antibacterial effects, their prices are relatively high, and their antibacterial efficiency during use is relatively low.
Moreover, after metallic silver is dispersed into plastic materials, it is difficult to recycle later, which is a great waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-bacterial polyvinyl chloride (PVC) material and preparation method thereof
  • Anti-bacterial polyvinyl chloride (PVC) material and preparation method thereof
  • Anti-bacterial polyvinyl chloride (PVC) material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] An antibacterial polyvinyl chloride material is made of the following components by weight:.

[0036]

[0037] Wherein, the viscosity of the polyvinyl chloride is 96; the stabilizer is dibasic lead phosphite; the compatibilizer is maleic anhydride grafted polyethylene; the coupling agent is γ- Glycidyl ether oxypropyltrimethoxysilane; Described plasticizer is cedarwood oil;

[0038] Described organic antibacterial agent is obtained according to the following method: 1g chloromethylstyrene-divinylbenzene-styrene copolymer is added in 50ml chloroform solvent, adds 1g benzyl dimethyl dodecyl ammonium chloride, Heat to 80°C and stir for 30 minutes, filter, wash and dry to obtain composite particles; weigh 5 parts of composite particles, 1 part of chitosan, and 0.2 part of potassium sorbate in parts by weight, and mix uniformly to obtain the antibacterial agent; wherein, the The chitosan is 2-hydroxypropyltrimethylammonium chloride chitosan.

[0039] The inorganic antib...

Embodiment 2

[0044] An antibacterial polyvinyl chloride material is made of the following components by weight:.

[0045]

[0046] Wherein, the viscosity of the polyvinyl chloride is 126; the stabilizer is tribasic lead phosphite; the compatibilizer is maleic anhydride grafted polyethylene. The coupling agent is N-(β aminoethyl)-γ-aminopropylmethyl-dimethoxysilane; the plasticizer is castor oil;

[0047] Described organic antibacterial agent is obtained according to the following method: 5g chloromethylstyrene-divinylbenzene-styrene copolymer is added in 50ml chloroform solvent, adds 5g benzyl dimethyl dodecyl ammonium chloride, Heat to 50°C and stir for 30 minutes, filter, wash and dry to obtain composite particles; weigh 5 parts of composite particles, 3 parts of chitosan, and 0.8 parts of potassium sorbate in parts by weight, and mix uniformly to obtain the antibacterial agent; wherein, the The chitosan is 2-hydroxypropyltrimethylammonium chloride chitosan.

[0048] The inorganic a...

Embodiment 3

[0053] An antibacterial polyvinyl chloride material is made of the following components by weight:.

[0054]

[0055]

[0056] Wherein, the viscosity of the polyvinyl chloride is 120; the stabilizer is dibasic lead phosphite; the compatibilizer is maleic anhydride grafted polyethylene; the coupling agent is 3- Aminopropyltrimethoxysilane; Described plasticizer is green mustard essential oil;

[0057] Described organic antibacterial agent is obtained according to the following method: 3g chloromethylstyrene-divinylbenzene-styrene copolymer is added in the 50ml chloroform solvent, adds 3g benzyl dimethyl dodecyl ammonium chloride, Heat to 50-860°C and stir for 20 minutes, filter, wash and dry to obtain composite particles; weigh 5 parts of composite particles, 2 parts of chitosan, and 0.6 parts of potassium sorbate in parts by weight, and mix uniformly to obtain the antibacterial agent; wherein, The chitosan is 2-hydroxypropyltrimethylammonium chloride chitosan.

[0058] T...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an anti-bacterial PVC material and a preparation method thereof. The anti-bacterial PVC material is prepared from, by weight, 100 parts of PVC, 2-5 parts of a stabilizer, 0.2-0.8 parts of a lubricant, 1-5 parts of a compatibilizer, 0.4-1.5 parts of a coupling agent, 2-8 parts of a plasticizer, 0.5-4 parts of an organic antibacterial agent and 8-25 parts of an inorganic antibacterial agent. In the design of the material, characters of the PVC material is fully considered, so that by means of the antibacterial plasticizer, with combination of the organic antibacterial agent and the inorganic antibacterial agent, mechanical performances of the PVC material is maintained and the antibacterial effect of the material is improved.

Description

technical field [0001] The invention belongs to the field of composite materials, and in particular relates to an antibacterial polyvinyl chloride material and a preparation method thereof. Background technique [0002] Polyvinyl chloride material is one of the most widely used general-purpose plastics. Polyvinyl chloride is polymerized by vinyl chloride under the action of an initiator, and the molecular weight of the polymer is generally between 50,000 and 120,000. Polyvinyl chloride material has good mechanical properties, good flame retardancy and dielectric properties. However, ordinary polyvinyl chloride materials lack high antibacterial properties. Therefore, there are certain performance defects when used in an environment with high antibacterial requirements. [0003] Commonly used antibacterial modified materials are added silver ion antibacterial agents. Although silver ion antibacterial agents have good antibacterial effects, their prices are relatively high, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/06C08L91/00C08L5/08C08L25/18C08K13/06C08K9/06C08K3/32C08K5/19C08K5/098C08K3/22C08K3/36C08K3/34C08K3/04
Inventor 万春霞
Owner SHANGHAI ZHENTUO IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com