Wet processing method for mica iron oxide

A technology of mica iron oxide and processing method, which is applied in chemical instruments and methods, treatment of dyed macromolecular organic compounds, treatment of inorganic pigments, etc. problem, to achieve the effect of good flaky structure, narrow particle size range, and high content of flaky structure

Inactive Publication Date: 2017-02-15
安徽纽亚达科技有限责任公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current pulverization process of mica iron oxide is complex, the pulverization effect is not good, the particle size range is relatively wide, and the flake structure of mica iron oxide will be destroyed during the pulverization process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of mica iron oxide wet processing method, comprises the following steps:

[0018] (1) The micaceous iron oxide raw material is generally added in the ball mill, and water is added as the grinding medium, so that the solid content is 55%, and in terms of the weight percentage of the micaceous iron oxide, 5% of the grinding aid is added, and the grinding aid is polyethylene glycol 400;

[0019] (2) Then carry out ball milling by the ball mill described in step (1), the ball-to-material ratio is 10:1, the set speed is 300r / min, the ball milling time is 60min, and then dried in a vacuum oven at 40°C , Dispersed to produce ultra-fine mica iron oxide powder.

Embodiment 2

[0021] A kind of mica iron oxide wet processing method, comprises the following steps:

[0022] (1) The micaceous iron oxide raw material is generally added in the ball mill, and water is added as the grinding medium so that the solid content is at 60%. In terms of the weight percentage of the micaceous iron oxide, 8% of the grinding aid is added, and the grinding aid is polyethylene glycol 400;

[0023] (2) Then carry out ball milling by the ball mill described in step (1), the ball-to-material ratio is 8:1, the set speed is 500r / min, the ball milling time is 120min, and then dried in a vacuum oven at 30°C , Dispersed to produce ultra-fine mica iron oxide powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a wet processing method for mica iron oxide. The method comprises the following steps: (1) adding a mica iron oxide raw material into a ball mill, adding water as a grinding medium, wherein solid content is allowed to be 55 to 60% in terms of the weight percentage of mica iron oxide, and adding 5 to 8% of a grinding aid; and (2) carrying out ball milling by using the ball mill in the step (1), wherein a ball-material ratio is 8: 1 to 10: 1, a rotating speed is set to be 300 to 500 r/min and ball milling time is 60 to 120 min, then carrying out drying at 30 to 40 DEG C in a vacuum drying box and then carrying out dispersion so as to obtian ultrafine mica iron oxide powder. Through optimization of the operation parameters of the wet processing method for mica iron oxide, the prepared mica iron oxide has a great amount of flaky structures, finer average granularity and a narrower granularity scope.

Description

technical field [0001] The invention relates to the technical field of mica iron oxide processing, in particular to a wet processing method of mica iron oxide. Background technique [0002] Mica iron oxide is a special iron ore in nature with ferric oxide as the main chemical composition. Its crystallization state is similar to mica, and its structure is scale-like, gray-black, with metallic luster. Due to its unique scaly structure, iron oxide ash and iron oxide red prepared by crushing, ultra-fine processing, and sorting are mainly used as fillers for anti-corrosion coatings. The current pulverization process of mica iron oxide is complex, the pulverization effect is not good, the particle size range is relatively wide, and the flake structure of mica iron oxide will be destroyed during the pulverization process. Contents of the invention [0003] In view of the above-mentioned technical problems, the object of the present invention is to provide a mica iron oxide wet p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/24C09C3/04C09C3/10
CPCC09C1/24C09C3/006C09C3/041C09C3/043C09C3/10
Inventor 崔应武李卫诚陈正余
Owner 安徽纽亚达科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap