Rare earth-contained high-manganese cold-rolled steel plate and manufacturing method thereof

A technology of cold-rolled steel sheet and high manganese, which is applied to the field of rare earth-containing high-manganese cold-rolled steel sheet and its manufacturing, can solve the problems of low yield strength and tensile strength, unfavorable cost control, and high Mn content, and achieves good manufacturability, The effect of good product performance uniformity and high production efficiency

Inactive Publication Date: 2017-01-11
BAOSHAN IRON & STEEL CO LTD
View PDF10 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The performance of the invention steel is superior, but the Mn content is relatively high, and the cost control is relatively unfavorable
[0009] Chinese patent 200810239893.X discloses a P-strengthened TWIP steel and its preparation process, its composition is: C: 0.01-0.08, Mn: 15-35%, Si≤1-6%, Al: 1-6%, P: 0.062-0.2%, the remainder is Fe and impurities. The tensile strength of the steel in this invention is 610-915MPa, the yield strength is 225-610MPa, and the elongation is 45-85.5%. The formability of the steel is superior, but the yield strength and tensile strength The strength is low, it is difficult to meet the requirements of ultra-high-strength steel for future automobiles
In addition, high-strength steel reinforced with P also has great difficulties in welding with other steel types.
[0010] Rare earth elements are generally used in iron and steel metallurgy to improve the shape of inclusions and purify steel. They are hydrogen storage materials with excellent performance. They have a good curing effect on H elements. Adding rare earth elements to improve the delayed cracking resistance of high manganese steel Not yet reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rare earth-contained high-manganese cold-rolled steel plate and manufacturing method thereof
  • Rare earth-contained high-manganese cold-rolled steel plate and manufacturing method thereof
  • Rare earth-contained high-manganese cold-rolled steel plate and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0043] The present invention will be further described below in conjunction with specific examples.

[0044] The composition of the embodiment of the present invention is obtained after smelting, hot rolling, cold rolling, annealing and smoothing, wherein the composition is as shown in Table 1, and the annealing process and mechanical properties are as shown in Table 2. figure 1 It is the elongation change data of Example 7 of the present invention and Comparative Example 2 under cold rolling deformation conditions.

[0045] As can be seen from Table 1, the microstructure of the rare earth-containing high manganese cold-rolled steel plate obtained by the present invention is 100% austenite at room temperature through appropriate composition design and process coordination; the recrystallization fraction is 80% to 95%; the yield strength is 450% ~650MPa, tensile strength 950~1100MPa, elongation over 50%, ultra-high-strength cold-rolled steel plate with good delayed cracking per...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rare earth-contained high-manganese cold-rolled steel plate and a manufacturing method thereof. The steel plate comprises the following components in percentage by weight: 0.4-0.8% of C,14-20% of Mn, 0.05-0.15% of RE, P not more than 0.020%, S not more than 0.012%, 1.0-2.0% of Al, 0.01-0.03% of N, and the balance of Fe and inevitable impurities; and the steel plate satisfies the conditions that: Mn+20*C not less than 30% and Al+5*RE not less than 1.8%. The steel plate is produced by a cold rolling-continuous annealing process to obtain austenite with 100% of room-temperature microstructure, reaches the recrystallization fraction of 80-95%, the yield strength of 450-650 MPa, the tensile strength of 950-1100 MPa and the ductility of above 50%, is excellent in splitting delay performance, is ultrahigh in strength, and is suitable for a vehicle structural part and a safety part with complex shapes.

Description

technical field [0001] The invention belongs to the field of high-manganese cold-rolled steel, and in particular relates to a rare-earth-containing high-manganese cold-rolled steel plate and a manufacturing method thereof. It has good cracking performance and is suitable for automotive structural parts and safety parts with complex shapes, as well as other related fields. Background technique [0002] Increasing the strength of the steel plate to reduce the thickness of the steel plate is a development trend of the steel plate in recent years. A large number of ultra-high-strength steel plates with a strength of 780MPa or more are used to replace traditional automotive steel, which is the key to achieving "weight reduction, energy saving, safety and The optimal material solution for reducing manufacturing costs is of great significance to building a low-carbon society. Every 10% reduction in vehicle weight can save fuel consumption by 5% to 8%, and at the same time reduce C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/06C22C38/04C21D8/02
Inventor 钟勇王利
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products