Wicker curing agent and preparation method thereof

A curing agent and wicker technology, applied in the direction of manufacturing tools, reed/straw treatment, wood processing equipment, etc., can solve problems such as falling off, not waterproof, and imperfect connection, etc., to achieve enhanced strength, increased bending, and good use effect Effect

Inactive Publication Date: 2017-01-11
阜南县明强柳编工艺品有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing wicker handicrafts are often folded and discounted. The strength and toughness of wicker directly affect the aesthetics and durability of handicrafts. However, most of the existing curing agents are surface strengthening. Although the strength of the surface increases, it becomes more brittle and less tough. At the same time, the existing curing agent is coated with a layer on the surface, which is not waterproof. After a long time, it will fall off and be invalid. At the same time, the quality of the glue will affect the connection between wicker and wicker, and the wicker will warp later, and the connection is not perfect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1: wicker solidifying agent mainly comprises the following components by mass and is prepared from:

[0031] 100 parts of polyacrylamide, 2 parts of toluene, 3 parts of glycerin, 5 parts of liquid low molecular weight polyamide, 2 parts of ethylene thiourea, 15 parts of epoxy resin, 2 parts of thiuram tetrasulfide, 60 parts of polylactic acid, calcined 15 parts of kaolin, 12 parts of epichlorohydrin, 7 parts of pullulan, 13 parts of nano silicon dioxide, 15 parts of zinc stearate, 14 parts of carbon black, 12 parts of ethyl silicone oil, 13 parts of calcium carbonate, pentadiene 4 parts of aldehydes, 13 parts of stearyl alcohol, 20 parts of chloromethyl oxirane, 30 parts of silicone vulcanizing agent, 20 parts of modified epoxy resin, 25 parts of isoamyl alcohol, 20 parts of isobutanol, 8 parts of castor oil Polyoxyethylene ether, 6 parts of sodium dodecylbenzenesulfonate, 20 parts of ash, 12 parts of urea, 12 parts of potassium chloride, 100 parts of sucrose...

Embodiment 2

[0049] Embodiment 2: wicker solidifying agent mainly comprises the following components by mass and is prepared from:

[0050]110 parts of polyacrylamide, 3 parts of toluene, 5 parts of glycerin, 10 parts of liquid low molecular weight polyamide, 3 parts of ethylene thiourea, 20 parts of epoxy resin, 5 parts of thiuram tetrasulfide, 70 parts of polylactic acid, calcined 20 parts of kaolin, 18 parts of epichlorohydrin, 15 parts of pullulan, 16 parts of nano silicon dioxide, 20 parts of zinc stearate, 18 parts of carbon black, 17 parts of ethyl silicone oil, 15 parts of calcium carbonate, pentadiene 10 parts of aldehyde, 15 parts of stearyl alcohol, 30 parts of chloromethyl oxirane, 40 parts of silicone vulcanizing agent, 25 parts of modified epoxy resin, 30 parts of isoamyl alcohol, 25 parts of isobutanol, 10 parts of castor oil Polyoxyethylene ether, 8 parts of sodium dodecylbenzenesulfonate, 25 parts of ash, 15 parts of urea, 15 parts of potassium chloride, 110 parts of sucro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a wicker curing agent and a preparation method thereof. The wicker curing agent mainly comprises polyacrylamide, methylbenzene, glycerol, liquid-state low-molecular-weight polyamide, ethylene thiourea, epoxy resin, tetramethylammonium thiuram tetrasulfide, polylactic acid, calcined kaoline, epoxy chloropropane, pullulan, nanometer silicon dioxide, zinc stearate, carbon black, ethyl silicon oil, calcium carbonate, glutaraldehyde, octadecanol, chloromethyloxirane, silica gel vulcanized agents, modified epoxy resin, isoamyl alcohol, isobutyl alcohol, castor oil polyoxylethylene ether, sodium dodecylbenzene sulfonate, ash, urea, potassium chloride, sucrose, peanuts, dried mushroom, forage, fresh milk, cold water, boiled water, rhubarb, magnoliae officinalis cortex, fructus aurantii, titanium dioxide, radix aucklandiae, popcorns, maltose, pitted red dates, talcum powder and ginger juice. A reinforcing agent prepared through the method is good in reinforcing effect, free of corrosion and capable of enhancing the strength and toughness of softened parts.

Description

[0001] Technical field: [0002] The invention relates to the technical field of auxiliary materials for handicraft preparation, in particular to a wicker curing agent and a preparation method thereof. [0003] Background technique: [0004] The existing wicker handicrafts are often folded and discounted. The strength and toughness of wicker directly affect the aesthetics and durability of handicrafts. However, most of the existing curing agents are surface strengthening. Although the strength of the surface increases, it becomes more brittle and less tough. At the same time, the existing curing agent is coated with a layer on the surface, which is not waterproof. After a long time, it will fall off and be ineffective. [0005] Invention content: [0006] The technical problem to be solved by the present invention is to overcome the defects of the prior art and provide a wicker curing agent and a preparation method thereof. [0007] The technical problem to be solved by the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K3/52B27K9/00
CPCB27K3/52B27K9/002
Inventor 孙传庆宋迎宾宋标孙传标
Owner 阜南县明强柳编工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products