Blended fabric and making method

A technology for fabrics and products, applied in the field of blended fabrics and preparations, can solve the problems of low added value, single function, and poor comfort, and achieve the effects of novel functional design, skin protection, and high added value

Inactive Publication Date: 2017-01-04
北京三五零一服装厂有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional fabrics in the prior art have single function, low grade, poor comfort and low added value, which cannot meet people's needs for clothing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blended fabric and making method
  • Blended fabric and making method
  • Blended fabric and making method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1: a kind of blended fabric, obtains by the raw material blending of following weight ratio:

[0034]

[0035] A method for preparing a blended fabric, comprising the steps of:

[0036] Step 1), blending bamboo fiber, hemp fiber, flax fiber, modal fiber, polylactic acid fiber, jute fiber and apocynum fiber according to the ratio in the formula, to obtain a blended product;

[0037] Step 2), soak the blended product in the chitosan solution for 15-20 minutes, take it out and dry it;

[0038] Step 3), soak the blended product in the compound enzyme preparation, the dosage is 0.8-1.2% owf, the pH is 7.8, the temperature is 45°C, keep warm for 40 minutes, raise the temperature to 90°C, keep warm for 10 minutes, inactivate the enzyme, rinse , cooling to obtain the finished product of the blended product;

[0039] Step 4), blanching the bamboo fiber fabric in hot water at a temperature of 90-100°C for 20-30 minutes, taking it out, and rinsing it with normal te...

Embodiment 2

[0044] Embodiment 2: a kind of blended cloth, obtains by the raw material blending of following weight ratio:

[0045]

[0046] A method for preparing a blended fabric, comprising the steps of:

[0047] Step 1), blending bamboo fiber, hemp fiber, flax fiber, modal fiber, polylactic acid fiber, jute fiber and apocynum fiber according to the ratio in the formula, to obtain a blended product;

[0048] Step 2), soak the blended product in the chitosan solution for 15-20 minutes, take it out and dry it;

[0049] Step 3), soak the blended product in the compound enzyme preparation, the dosage is 0.8-1.2% owf, the pH is 7.8, the temperature is 45°C, keep warm for 40 minutes, raise the temperature to 90°C, keep warm for 10 minutes, inactivate the enzyme, rinse , cooling to obtain the finished product of the blended product;

[0050] Step 4), blanching the bamboo fiber fabric in hot water at a temperature of 90-100°C for 20-30 minutes, taking it out, and rinsing it with normal tem...

Embodiment 3

[0055] Embodiment 3: a kind of blended cloth, obtains by the raw material blending of following weight ratio:

[0056]

[0057] A method for preparing a blended fabric, comprising the steps of:

[0058] Step 1), blending bamboo fiber, hemp fiber, flax fiber, modal fiber, polylactic acid fiber, jute fiber and apocynum fiber according to the ratio in the formula, to obtain a blended product;

[0059] Step 2), soak the blended product in the chitosan solution for 15-20 minutes, take it out and dry it;

[0060] Step 3), soak the blended product in the compound enzyme preparation, the dosage is 0.8-1.2% owf, the pH is 7.8, the temperature is 45°C, keep warm for 40 minutes, raise the temperature to 90°C, keep warm for 10 minutes, inactivate the enzyme, rinse , cooling to obtain the finished product of the blended product;

[0061] Step 4), blanching the bamboo fiber fabric in hot water at a temperature of 90-100°C for 20-30 minutes, taking it out, and rinsing it with normal tem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a blended fabric and a making method and belongs to the field of textile technologies. The making method of the blended fabric is characterized by including the following steps that bamboo fibers, hemp fibers, flax fibers, modal fibers, polylactic acid fibers, jute fibers and apocynum venetum fibers are blended according to the ratio in the formula, so that a blended product is obtained; the blended product is soaked for 15-20 minutes in a chitosan solution and taken out to be dried; the blended product is soaked in a complex enzyme preparation, the usage amount of the complex enzyme preparation is 0.8%-1.2% owf, pH is 7.8, temperature is 45 DEG C, and is kept for 40 minutes and increased to 90 DEG C, then temperature is kept for 10 minutes, in this way, enzyme is inactivated, and the blended finished product is obtained through rinsing and cooling. The blended fabric is good in antibacterial activity, protects the skin and further has the advantages of being resistant to ultraviolet, abrasion and shrinkage and smooth, and having moisture permeability.

Description

technical field [0001] The invention relates to a blended fabric and a preparation method thereof, belonging to the technical field of textiles. Background technique [0002] The traditional cloth of the prior art has single function, low grade, poor comfort and low added value, and cannot meet people's needs for clothing. Contents of the invention [0003] In order to overcome the deficiencies of the prior art, the invention provides a blended fabric and a preparation method. [0004] A blended fabric obtained by blending raw materials in the following weight ratios: [0005] Bamboo fiber 30-46; [0006] Hemp fiber 20-32; [0007] Flax fiber 3-19; [0008] Jute fiber 5-12; [0009] Apocynum fiber 5-9; [0010] Modal fiber 16-23; [0011] Polylactic acid fiber 9-26; [0012] A method for preparing a blended fabric, comprising the steps of: [0013] Step 1), blending bamboo fiber, hemp fiber, flax fiber, modal fiber, polylactic acid fiber, jute fiber and apocynum f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A41D31/00D02G3/04D06B3/10D06M15/03D06M16/00D06L3/00D06P3/85D06P1/34D06P5/02D06M101/04D06M101/06D06M101/32
CPCA41D31/00D02G3/04D06B3/10D06M15/03D06M16/003D06M2101/04D06M2101/06D06M2101/32D06P1/34D06P3/8228D06P5/02D10B2201/01D10B2201/04D10B2201/06D10B2201/10D10B2201/22D10B2331/04
Inventor 侯秀廷
Owner 北京三五零一服装厂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com