High-efficiency ABC dry powder extinguishing agent
A dry powder fire extinguishing agent, high-efficiency technology, applied in fire prevention equipment, etc., can solve the problems of low monoammonium phosphate content, poor fire extinguishing effect, low fire extinguishing efficiency, etc., achieve high monoammonium phosphate content, good fire extinguishing effect, and improve sports performance Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0026] The raw material of the main components adopts 820 kilograms of monoammonium phosphate with a purity of 92.71% produced by our company, wherein the content of ammonium sulfate is 2.62%, and other components are purchased from the market. The converted formula is as follows:
[0027] Monoammonium Phosphate
Silica
Quartz sand
silicone oil
activated clay
iron yellow
760kg
152kg
13kg
11kg
6kg
11kg
11kg
0.02kg
[0028] Break the monoammonium phosphate and ammonium sulfate separately; add all the raw materials into the silicification machine (except silicone oil) according to the formula; stir and heat to 60-70°C; spray the emulsion of silicone oil and water; The temperature of the reaction material is 110-115°C; the siliconized reaction material is cooled to below 60°C, screened, and packaged to obtain a high-efficiency ABC dry powder fire extinguishing agent product.
[0029] T...
Embodiment 2
[0033] The raw material of the main components adopts 810 kilograms of monoammonium phosphate with a purity of 96.43% produced by our company, wherein the content of ammonium sulfate is 1.08%, and other components are purchased from the market. The converted formula is as follows:
[0034] Monoammonium Phosphate
ammonium sulfate
Silica
Quartz sand
activated clay
iron yellow
781kg
153kg
25kg
12kg
9kg
25kg
12kg
0.01kg
[0035] Break the monoammonium phosphate and ammonium sulfate separately; add all raw materials into the siliconization machine (except silicone oil) according to the formula; stir and heat to 65-75°C; spray the emulsion of silicone oil and water; siliconization reaction for 2.5 hours, siliconization The temperature of the reaction material is 90-95°C; the siliconized reaction material is cooled to below 60°C, screened and packaged to obtain a high-efficiency ABC dry powd...
Embodiment 3
[0040] The raw material of the main components adopts 816 kilograms of monoammonium phosphate with a purity of 94.39% produced by our company, wherein the content of ammonium sulfate is 3.12%, and other components are purchased from the market. The formula after conversion is as follows:
[0041] Monoammonium Phosphate
ammonium sulfate
Silica
Quartz sand
silicone oil
activated clay
lead chrome yellow
770kg
156kg
10kg
26kg
5kg
15kg
21kg
0.01kg
[0042] Break the monoammonium phosphate and ammonium sulfate separately; add all raw materials into the siliconization machine (except silicone oil) according to the formula; stir and heat to 75-85°C; spray the emulsion of silicone oil and water; siliconization reaction for 2 hours, siliconization The temperature of the reaction material is 105-110°C; the siliconized reaction material is cooled to below 60°C, screened, and packaged to obtain a high-efficien...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com