Alloy steel surface coating cladding method

A surface coating, alloy steel technology, applied in metal material coating process, coating, melt spraying and other directions, can solve the problem of insufficient bonding strength between coating and substrate, complex coating cladding process, coating shape distortion, etc. problems, to achieve the effect of easy selection of temperature range, high thermal energy utilization rate, and small axial temperature gradient

Active Publication Date: 2016-11-30
CHENGDU PLASMAJET SCI & TECH
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention solves the problems of cracks or pores in the cladding layer, insufficient bonding strength between the coating and the substrate, distortion of the coating shape and serious coating dilution in the prior art, and solves the problems of complex coating cladding process and harsh conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A method for alloy steel surface coating cladding, comprising the steps of:

[0033] A. Configure alloy powder

[0034] Alloy powder, including the following raw materials by mass percentage: 30% ferro-titanium, 14% ferrochromium, 14% ferromolybdenum, 20% graphite and the balance are powders of pure iron, mixed together in proportion;

[0035] B. Using laminar plasma coating cladding equipment

[0036]Coating cladding equipment includes a laminar plasma generator, which provides a heat source with laminar plasma. Setting parameters, input power voltage 340, rated input capacity 30KVA, output voltage 60V, working voltage 25V, output current 450A, scanning speed 600mm / min, powder feeder airflow 1.5m 3 / h, ion gas flow rate 1.5m 3 / h, shielding gas flow rate 1.5 m 3 / h;

[0037] C. Pre-treatment of coating cladding

[0038] Derust, decontaminate and remove the fatigue layer on the surface of the substrate, and preheat the laminar plasma generator;

[0039] D. Coat...

Embodiment 2

[0044] A method for alloy steel surface coating cladding, comprising the steps of:

[0045] A. Configure alloy powder

[0046] Alloy powder, including the following raw materials by mass percentage: 35% ferro-titanium, 16% ferrochromium, 16% ferromolybdenum, 25% graphite and the balance are powders of pure iron, mixed together in proportion;

[0047] B. Using laminar plasma coating cladding equipment

[0048] Coating cladding equipment includes a laminar plasma generator, which provides a heat source with laminar plasma. Setting parameters, input power voltage 400, rated input capacity 30KVA, output voltage 60V, working voltage 25V, output current 500A, scanning speed 650mm / min, powder feeder airflow 2.0m 3 / h, ion gas flow rate 2.0 m 3 / h, protective gas flow rate 2.3 m 3 / h;

[0049] C. Pre-treatment of coating cladding

[0050] Derust, decontaminate and remove the fatigue layer on the surface of the substrate, and preheat the laminar plasma generator;

[0051] D. C...

Embodiment 3

[0056] A method for alloy steel surface coating cladding, comprising the steps of:

[0057] A. Configure alloy powder

[0058] Alloy powder, including the following raw materials by mass percentage: 33% ferro-titanium, 15% ferrochromium, 15% ferromolybdenum, 22% graphite and the balance are powders of pure iron, mixed together in proportion;

[0059] B. Using laminar plasma coating cladding equipment

[0060] Coating cladding equipment includes a laminar plasma generator, which provides a heat source with laminar plasma. Setting parameters, input power voltage 370, rated input capacity 30KVA, output voltage 60V, working voltage 25V, output current 470A, scanning speed 620mm / min, powder feeder airflow 1.8m 3 / h, ion gas flow rate 1.8 m 3 / h, protective gas flow rate 2.1 m 3 / h;

[0061] C. Pre-treatment of coating cladding

[0062] Derust, decontaminate and remove the fatigue layer on the surface of the substrate, and preheat the laminar plasma generator;

[0063] D. C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
microhardnessaaaaaaaaaa
microhardnessaaaaaaaaaa
microhardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an alloy steel surface coating cladding method. A surface coating comprises, by mass, 30 to 35% of ferrotitanium, 14 to 16% of ferrochromium, 14 to 16% of ferromolybdenum, 20 to 25% of graphite, and the balance pure iron powder. According to the alloy steel surface coating cladding method, alloy steel surface coating cladding is realized via following steps: alloy powder configuration is carried out, laminar plasma jet coating cladding equipment setting is carried out, coating cladding pretreatment is carried out, coating cladding treatment is carried out, coating cladding aftertreatment is carried out, and a heat source is provided by a laminar plasma generator under certain parameter setting. According to the alloy steel surface coating cladding method, the special heat source is provided by laminar plasma beam, and special setting of technological conditions and parameters are carried out, so that the alloy steel surface coating cladding method is simple, an obtained alloy steel surface cladding coating possesses wear resistance, high compactness, and alloy steel surface modification quality is improved.

Description

technical field [0001] The invention relates to a metal surface treatment method, in particular to an alloy steel surface coating cladding method, which belongs to the technical field of metal surface treatment. Background technique [0002] At present and in the foreseeable future, alloy steel is still an important material required for social and economic development. The new alloy steel must meet the requirements of social development for energy saving, resource conservation, and environmental protection in the production, processing, use and recycling of steel. For this reason, alloy steel will develop in the direction of high performance and variety. Alloy steel (alloy steel) in addition to iron, carbon, there are other alloying elements added. An iron-carbon alloy formed by adding an appropriate amount of one or more alloying elements to ordinary carbon steel. According to the different elements added and appropriate processing technology, special properties such as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C4/134C23C4/06
CPCC23C4/06
Inventor 李向阳陈千智何泽李露
Owner CHENGDU PLASMAJET SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com