Anti-cracking putty powder for interior walls

A technology of putty powder and interior walls, applied in the direction of filling slurry, etc., can solve the problems of mildew, easy yellowing, cracking, etc., and achieve the effects of strong adhesion, good leveling, and good water resistance

Inactive Publication Date: 2016-11-30
CHANGSHU QIYUE NEW BUILDING MATERIAL TECH CO LTD
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing crack-resistant putty powder for interior walls needs to be improved in leveling, adhesion, water resistance, strength, abrasion resistance, acid and alkali corrosion resistance, high and low temperature resistance, and mildew resistance. After being damp, it is prone to hollowing, peeling, cracking, and shedding, and it is prone to yellowing, mold, and black spots

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] The anti-cracking putty powder for interior walls consists of the following components by weight:

[0054] 1-2 parts polyoxyethylene oleate,

[0055] 1.8 parts polyvinylpyrrolidone,

[0056] 1.6 parts of sodium alpha-olefin sulfonate,

[0057] 0.9 parts lauryltrimethylammonium chloride,

[0058] 1.4 parts of sodium oleamide ethanesulfonate,

[0059] 0.8 parts magnesium aluminum silicate,

[0060] 3.4 parts carbon fiber filaments,

[0061] 14 parts marble flour,

[0062] 24 parts white latex,

[0063] 46 parts gray calcium.

Embodiment 2

[0065] The anti-cracking putty powder for interior walls consists of the following components by weight:

[0066] 1 part polyoxyethylene oleate,

[0067] 1.8 parts polyvinylpyrrolidone,

[0068] 1.6 parts of sodium alpha-olefin sulfonate,

[0069] 0.9 parts lauryltrimethylammonium chloride,

[0070] 1.4 parts of sodium oleamide ethanesulfonate,

[0071] 0.8 parts magnesium aluminum silicate,

[0072] 3.4 parts carbon fiber filaments,

[0073] 14 parts marble flour,

[0074] 24 parts white latex,

[0075] 46 parts gray calcium.

Embodiment 3

[0077] The anti-cracking putty powder for interior walls consists of the following components by weight:

[0078] 2 parts polyoxyethylene oleate,

[0079] 1.8 parts polyvinylpyrrolidone,

[0080] 1.6 parts of sodium alpha-olefin sulfonate,

[0081] 0.9 parts lauryltrimethylammonium chloride,

[0082] 1.4 parts of sodium oleamide ethanesulfonate,

[0083] 0.8 parts magnesium aluminum silicate,

[0084] 3.4 parts carbon fiber filaments,

[0085] 14 parts marble flour,

[0086] 24 parts white latex,

[0087] 46 parts gray calcium.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses anti-cracking putty powder for interior walls. The anti-cracking putty powder comprises, by weight, 1-2 parts of oleic acid polyoxyethylene ester, 1.8 parts of polyvinylpyrrolidone, 1.6 parts of alpha-olefin sulfonate, 0.9 part of dodecyltrimethylammonium chloride, 1.4 parts of oleoyl methylamine sodium diethylsulfonate, 0.8 part of magnesium aluminium silicate, 3.4 parts of carbon fiber yarn, 14 parts of marble powder, 24 parts of white latex and 46 parts of ash calcium. The anti-cracking putty powder for interior walls is good in levelling property, strong in adhesive force, good in water proofness, high in strength, good in sanding property, resistant to acid and alkali corrosion, resistant to high and low temperature changes and resistant to mildew, is free of hollowing, peeling, crazing and stripping after being exposed to water and damp, and is also free of yellowing, mildewing and black spot formation.

Description

technical field [0001] The invention relates to an anti-cracking putty powder for interior walls. Background technique [0002] The existing crack-resistant putty powder for interior walls needs to be improved in leveling, adhesion, water resistance, strength, abrasion resistance, acid and alkali corrosion resistance, high and low temperature resistance, and mildew resistance. After being damp, it is prone to hollowing, peeling, cracking, and shedding, and it is also prone to yellowing, mold, and black spots. Contents of the invention [0003] The object of the present invention is to provide an anti-cracking putty powder for interior walls, which has good leveling property, strong adhesion, good water resistance, high strength, abrasion resistance, acid and alkali corrosion resistance, high and low temperature resistance, and mildew resistance , No hollowing, peeling, cracking, shedding after being exposed to water and damp, and no yellowing, mildew, or black spots. [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 范毓明
Owner CHANGSHU QIYUE NEW BUILDING MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com