A kind of preparation method of wide-temperature acid-resistant and heat-resistant mastic

A production method, technology of heat-resistant glue, applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of ineffectiveness, environmental temperature changes, inconvenience, etc., and increase the operating rate of the construction site , wide temperature range, energy saving effect

Active Publication Date: 2018-03-20
JIANGXI PINGXIANG LONGFA ENTERPRISE
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when on-site deployment, the ambient temperature changes, and the effect is often not achieved. It is rarely used now, and a large amount of heating equipment can only be invested in construction. It is extremely inconvenient to use raw materials at low temperatures.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The cement material includes a mixture of the following components in a weight ratio: 50% of quartz, 15% of feldspar powder, 20% of cast stone essence, 5% of curing agent, and 10% of additives. The additives are additive type A, and the Additive type A includes the following components in weight ratio (wt%): Wangxianshi 20%, Jiaobao 33%, Xianqiaoshi 15%, Yichun raw material 20%, Datang sand 6%, Banshan mud 6%, the additive Each component is mixed and made into additive type A for use; then according to the following production method: a, after processing the dry material of each component of the mixture, put it into the mixer for dry mixing for 5 minutes, and the addition is 40% of the capacity of the mixer; b, After stirring evenly, add additive type A and stir evenly; c. Finally, mix the mixture obtained after stirring in step b with water glass.

Embodiment 2

[0024] The cement material includes a mixture of the following components in a weight ratio: 60% of quartz, 10% of feldspar powder, 10% of cast stone essence, 7% of curing agent, and 13% of additives. The additives are additive type A, and the Additive type A includes the following components in weight ratio (wt%): Wangxianshi 25%, Jiaobao 28%, Xianqiaoshi 10%, Yichun raw material 19%, Datang sand 8% and Banshan mud 10%, the additive Each component is mixed and made into additive type A for use; then follow the following production method; 30% of the capacity; b. After stirring evenly, add additive type A and stir evenly; c. Finally, mix the mixture obtained after stirring in step b with water glass to make cement.

Embodiment 3

[0026] The cement material includes a mixture of the following components in a weight ratio: 52% of quartz, 12% of feldspar powder, 16% of cast stone essence, 6% of curing agent, and 14% of additives. The additives are additive type B, and the Additive type B includes the following components in weight ratio (wt%): Wangxianshi 15%, Jiaobao 50%, Xianqiaoshi 5%, Yichun raw material 15%, Datang sand 12%, Banshan mud 3%, the additive Each component is mixed and made into additive type B for use; then according to the following production method; the production method is as follows: a, after processing the dry material of each component of the mixture, put it into the mixer for dry mixing for 3 minutes, and the addition amount is 1 / 2 of the capacity of the mixer 45%; b. After the mixture is stirred evenly, add additive type B and stir evenly; c. Finally, mix the mixture that has been stirred in step b with water glass.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for making wide-temperature acid-resistant and heat-resistant mastic. The mastic includes a mixture of the following components in weight ratio: 50-60% of quartz, 10-20% of feldspar powder, 15-20% of cast stone essence, Curing agent 5-7%, also includes additive 10-15%, and described additive is A type and includes following weight ratio: Wang Xianshi 15-25%, coke stone 28-35%, Xianqiao stone 10-15%, Yichun 18-25% of raw material, 1-8% of Datang sand, 3-10% of Banshan mud, or the additives are type B including the following weight ratios: Wangxianshi 10-15%, coke gemstone 40-50%, fairy Bridge stone 5-10%, Yichun raw material 10-20%, Datang sand 10-15%, Banshan mud 1-5%, the present invention is to add 1-2 kinds to the existing acid-resistant heat-resistant cement powder Additives for acid-resistant raw materials are convenient for construction at low temperatures, ensuring project progress and saving energy.

Description

technical field [0001] The invention relates to the technical field of making anti-corrosion engineering clay, in particular to a method for making wide-temperature acid-resistant and heat-resistant clay. Background technique [0002] Acid-resistant and heat-resistant cement is an acid-resistant material mixed with acid-resistant fillers and hardeners in an appropriate proportion. It is suitable for acid-resistant and anti-corrosion projects in chemical, petroleum, metallurgy, machinery, papermaking, textile and other industries. When in use, it can harden in the air after being stirred evenly with an appropriate amount of water glass solution, and has the ability to resist corrosion by most inorganic acids and organic acids. Its main components generally include quartz sand, quartz powder, cast stone powder, curing agent (fluorine Sodium silicate or polymer condensed aluminum phosphate), etc., and then prepare about 40% water glass for construction. [0003] According to t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B18/04C04B28/26
CPCY02W30/91
Inventor 罗德平朱陵辉赖志军
Owner JIANGXI PINGXIANG LONGFA ENTERPRISE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap