Supercapacitor electrode plate and preparation method thereof

A technology for supercapacitors and pole pieces, applied in the field of supercapacitor pole pieces and their preparation, can solve the problems of slurry dripping and hindering applications, achieve high production efficiency, increase energy density and power density, and reduce production costs

Inactive Publication Date: 2016-09-28
SHANDONG GOLDENCELL ELECTRONICS TECH
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to improve the energy density of supercapacitors, those skilled in the art have explored the use of metal collectors with holes to reduce the weight of the product, but the current collectors with holes will leak during the coating process, which hinders the application of this process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Supercapacitor electrode plate and preparation method thereof
  • Supercapacitor electrode plate and preparation method thereof
  • Supercapacitor electrode plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example

[0040] Example: a method for preparing a pole piece of a supercapacitor, the pole piece preparation comprises the following steps:

[0041] Ⅰ. Pulping, that is, putting 85% by weight of activated carbon, 10% of conductive carbon and 5% of binder into a planetary vacuum mixer and adding a solvent that is 4 times the weight of solid matter for stirring, dispersing and mixing to obtain a uniform supercapacitor slurry material.

[0042] II. Forming a film, using an extrusion coater to coat the uniform slurry obtained in step I on the polyimide film carrier 2 to prepare a carbon film 1

[0043] Ⅲ, drying, step Ⅱ The polyimide film 2 coated with the carbon film 1 is dried in a tunnel oven, the thickness of the carbon film 1 after drying is 200 μm, and the content of the solvent is controlled at 6%;

[0044] Ⅳ. Hot press molding, place the carbon film 1 dried in step Ⅲ on both sides of the aluminum current collector 3 with holes, and use 120°C and 200 tons of pressure to heat and ro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

A kind of supercapacitor pole piece and preparation method thereof, it is characterized in that comprising the following steps: 1, pulping, the active carbon of 60%~90% by weight, the conductive carbon of 5%~35% and the viscose of 5%~10% Put the binder into a planetary vacuum mixer and add a solvent 2 to 5 times the weight of the solid substance for stirring, dispersing and mixing to obtain a uniform supercapacitor slurry; The uniform slurry coated on the organic film carrier is prepared into a carbon film; Ⅲ, drying, step Ⅱ The organic film coated with the carbon film is dried in a tunnel oven, so that the content of the solvent in the carbon film is controlled at 5% to 10 Between %; Ⅳ, hot press forming, place the carbon film dried in step Ⅲ on both sides of the metal current collector, and combine the carbon film and the metal current collector by heating and rolling to form a supercapacitor pole piece.

Description

technical field [0001] The invention belongs to the technical field of supercapacitors, and in particular relates to a pole piece of a supercapacitor with high energy density, high power density and good stability and a preparation method thereof. Background technique [0002] Supercapacitor is a new type of energy storage device between traditional capacitors and secondary batteries that has emerged in recent years. While retaining the characteristics of high power density of traditional capacitors, it has an electrostatic capacity of up to farads or even tens of thousands of farads. , so it has the characteristics of high energy density. At the same time, it also has the advantages of fast charging and discharging, high energy conversion efficiency, good temperature characteristics (-40 ° C ~ 70 ° C), long cycle life and environmental protection, so its technology has been widely valued by countries all over the world and can be widely used. Wind power, solar power, digit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01G11/86H01G11/32
CPCY02E60/13H01G11/86H01G11/32
Inventor 王勇张敬捧李涛关成善宗继月
Owner SHANDONG GOLDENCELL ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com