Peanut hull plant fiber synthetic resin and preparation technology thereof

A plant fiber and synthetic resin technology, applied in the field of peanut shell plant fiber synthetic resin and its preparation process, can solve the problems of unfavorable degradation, damage to soil water permeability, high cost, etc., to alleviate the shortage of resources, increase farmers' income, and have a long service life Effect

Inactive Publication Date: 2016-09-28
安徽科邦树脂科技有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing tableware, furniture, kitchen utensils and other daily necessities on the market are all made of wood, bamboo, ordinary plastics and other products. Pollution" destroys the water permeability of the soil, while wood and bamboo products require deforestation and waste water pollution during the manufacturing process, so they are not very good environmental protection materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A peanut shell plant fiber synthetic resin, comprising the following raw materials in parts by weight: 30 parts of peanut shell powder, 5 parts of polyanionic cellulose, 15 parts of algin, 3 parts of aliphatic polycarbonate, 15 parts of tapioca starch, 3 parts of glycerin , 3 parts acacia powder, 5 parts calcium carbonate, 10 parts polylactic acid fiber;

[0021] The preparation process includes the following steps:

[0022] (1) The peanut shells are subjected to ultra-fine grinding processing to obtain fine-particle peanut shell powder;

[0023] (2) Put the glycerin and aliphatic polycarbonate into the high-speed mixer, and at the same time add the polyanionic cellulose and stir evenly to obtain the initial mixed material;

[0024] (3) Put the peanut shell powder of step (1) into the high-speed mixer and mix with the initial mixing material of step (2), and at the same time add tapioca starch and stir evenly, then cool to room temperature, and smash after solidifying into a bl...

Embodiment 2

[0031] A peanut shell plant fiber synthetic resin comprising the following raw materials by weight: 60 parts of peanut shell powder, 10 parts of polyanionic cellulose, 40 parts of alginate, 8 parts of aliphatic polycarbonate, 40 parts of tapioca starch, 8 parts of glycerin , 8 parts of gum arabic powder, 10 parts of calcium carbonate, 20 parts of polylactic acid fiber;

[0032] The preparation process includes the following steps:

[0033] (1) The peanut shells are subjected to ultra-fine grinding processing to obtain fine-particle peanut shell powder;

[0034] (2) Put the glycerin and aliphatic polycarbonate into the high-speed mixer, and at the same time add the polyanionic cellulose and stir evenly to obtain the initial mixed material;

[0035] (3) Put the peanut shell powder of step (1) into the high-speed mixer and mix with the initial mixing material of step (2), and at the same time add tapioca starch and stir evenly, then cool to room temperature, and smash after solidifying i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of chemical materials, in particular to peanut hull plant fiber synthetic resin and a preparation technology thereof. The resin is prepared from peanut hull powder, polyanionic cellulose, alginate, aliphatic polycarbonate, cassava starch, glycerinum, Arabic gum powder, calcium carbonate and polylactic acid fiber. The preparation method includes the following steps that firstly, fine granular peanut hull powder is prepared; secondly, a primarily mixed material is prepared; thirdly, peanut hull fiber powder is prepared; fourthly, a mixed additive is prepared; fifthly, the mixed additive and polylactic acid fiber are stirred evenly, mixed and extruded, injection molding is conducted, and the peanut hull plant fiber synthetic resin is obtained. The resin and the method aim to prevent crop waste and other resources from being wasted, fully use the resources and reduce environment pollution. Production cost is low, application range is wide, rural resource advantages can be achieved, and an effective method and a means are provided for reasonable utilization of waste crops.

Description

Technical field [0001] The invention relates to the field of chemical materials, in particular to a peanut shell plant fiber synthetic resin and a preparation process thereof. Background technique [0002] As a large agricultural country, with the successive bumper harvests of agriculture, the output of crop straw and other waste materials has also risen sharply. The output of light straw and other waste materials is about 650 million tons per year. The disposal of crop waste materials and straw has become a social problem. In addition to the development and utilization of feed and fertilizer, most of them are burned, which not only wastes resources, but also seriously harms the natural ecological environment. Therefore, the comprehensive utilization of abandoned crops is of great significance. While mankind is creating modern civilization, it also brings a negative impact-white pollution. Disposable tableware, disposable plastic products, and agricultural mulch are difficult to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L1/02C08L69/00C08L3/02C08L5/04C08L5/00C08L67/04C08K5/053C08K3/26
CPCC08L97/02C08L2201/06C08L2201/08C08L2205/02C08L2205/035C08L2205/16C08L1/02C08L69/00C08L3/02C08L5/04C08L5/00C08L67/04C08K5/053C08K2003/265
Inventor 袁振洲
Owner 安徽科邦树脂科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com