Water-resistant net-flavor waterborne ceramic simulating coating and preparation method thereof

A porcelain-like coating, water-based technology, applied in the field of coatings, can solve the problems of adsorption capacity occupation, unable to meet the requirements of air purification, and small adsorption capacity of activated carbon, and achieve the effect of large adsorption capacity, good air purification effect and long purification time

Active Publication Date: 2016-07-20
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still many disadvantages in the current coatings that use activated carbon as the main air purification component: 1. The adsorption capacity of activated carbon is small, and the general effective duration of adsorption is 1 year, while the release of harmful gases is long-term, so it cannot meet the long-term requirements. Air purification requirements; 2. Activated carbon has good hygroscopicity. While adsorbing harmful gases, it will also absorb a large amount of water, resulting in its limited adsorption capacity being occupied

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A water-resistant and odor-cleaning water-based enamel paint, comprising the following components by mass:

[0039] 15 parts of calcite powder, 15 parts of Shuangfei powder, 10 parts of calcium carbonate, 3 parts of bletilla striata powder, 2 parts of corn starch, 1 part of carboxymethyl cellulose, 1 part of phenolic resin, 1 part of glutaraldehyde, 2 parts of air purification particles , 50 parts of water.

[0040] The preparation steps of the water-resistant and odor-cleaning water-based imitation porcelain coating of the present embodiment are:

[0041] 1) Preparation of composite carbon sol: furfural, water-soluble phenolic resin, carbon nanotubes, carboxymethyl cellulose, brucite fiber, sodium bicarbonate and water in a mass ratio of 4:1:0.4:0.15:0.04: Mix 0.02:100, stir evenly to obtain the first mixed solution, add ammonia water with a concentration of 0.5mol / L to the first mixed solution at a rate of 15mL / min under stirring conditions, so that the first mixed s...

Embodiment 2

[0048] A water-resistant and odor-cleaning water-based enamel paint, comprising the following components by mass:

[0049] 10 parts of calcite powder, 20 parts of Shuangfei powder, 8 parts of calcium carbonate, 4 parts of bletilla striata powder, 3 parts of corn starch, 0.5 parts of carboxymethyl cellulose, 0.5 parts of phenolic resin, 0.5 parts of glutaraldehyde, 1 part of air purification particles , 52.5 parts of water.

[0050] The preparation steps of the water-resistant and odor-cleaning water-based imitation porcelain coating of the present embodiment are:

[0051] 1), the preparation of composite carbon sol: furfural, water-soluble phenolic resin, carbon nanotubes, carboxymethyl cellulose, brucite fiber, sodium bicarbonate and water in a mass ratio of 3:1:0.3:0.1:0.03: Mix 0.01:100, stir evenly to obtain the first mixed solution, add ammonia water with a concentration of 0.25mol / L to the first mixed solution at a rate of 10mL / min under stirring conditions, so that the...

Embodiment 3

[0058] A water-resistant and odor-cleaning water-based enamel paint, comprising the following components by mass:

[0059] 20 parts of calcite powder, 10 parts of double fly powder, 12 parts of calcium carbonate, 2 parts of bletilla striata powder, 1 part of corn starch, 1.5 parts of carboxymethyl cellulose, 1.5 parts of phenolic resin, 1.5 parts of glutaraldehyde, 3 parts of air purification particles , 47.5 parts of water.

[0060] The preparation steps of the water-resistant and odor-cleaning water-based imitation porcelain coating of the present embodiment are:

[0061] 1) Preparation of composite carbon sol: furfural, water-soluble phenolic resin, carbon nanotubes, carboxymethyl cellulose, brucite fiber, sodium bicarbonate and water in a mass ratio of 5:1:0.5:0.2:0.05: Mix 0.03:100, stir evenly to obtain the first mixed solution, add ammonia water with a concentration of 0.75mol / L to the first mixed solution at a rate of 20mL / min under stirring conditions, so that the fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of coating and discloses a water-resistant net-flavor waterborne ceramic simulating coating and a preparation method thereof. The coating comprises the following components in parts by mass: 10-20 parts of calcite powder, 10-20 parts of heavy calcium carbonate powder, 8-12 parts of calcium carbonate, 2-4 parts of bletilla striata powder, 1-3 parts of corn starch, 0.5-1.5 parts of carboxymethyl cellulose, 0.5-1.5 parts of phenoxy resin, 0.5-1.5 parts of glutaraldehyde, 1-3 parts of air purifying particles and 45-55 parts of water. The water-resistant net-flavor waterborne ceramic simulating coating provided by the invention has the advantages of relatively good water resistance, air purifying function, large adsorption capacity, long purifying time and good air purifying effect.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a water-resistant and deodorizing water-based imitation porcelain coating and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, people pay more and more attention to their own health. In recent years, reports on the relationship between newly renovated indoor air pollution and the incidence of leukemia have also been seen in the media. Therefore, people pay more and more attention to the environmental protection of decoration materials when decorating. [0003] In the process of interior decoration, harmful substances such as formaldehyde and benzene series are more or less contained in wood boards, glue, wall paint, and furniture, which will gradually emit in the years or even decades after the decoration, thus affecting the health of the human body. healthy. Water-based imitation porcelain paints currently on the market are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D103/02C09D105/02C09D101/28C09D7/12
CPCC08K2201/014C08L2205/025C08L2205/035C09D7/61C09D7/62C09D7/63C09D7/65C09D103/02C09D105/02C08L3/02C08L5/02C08L1/286C08L71/00C08K13/06C08K9/06C08K3/04C08K2003/265C08K5/07
Inventor 杨谋森
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com