Preparation method of nitrogen-phosphorus co-doped carbon nanosheet and application of preparation method

A carbon nanosheet, co-doping technology, applied in nanotechnology, nanotechnology, nanotechnology for materials and surface science, etc., can solve problems such as unfavorable large-scale application, high price, poor stability, etc., and achieve good The effect of methanol resistance, high current density and high stability

Active Publication Date: 2016-07-13
QINGDAO UNIV
View PDF3 Cites 48 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of these metal catalysts have disadvantages such as high price and poor stability, which are not conducive to large-scale commercial application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of nitrogen-phosphorus co-doped carbon nanosheet and application of preparation method
  • Preparation method of nitrogen-phosphorus co-doped carbon nanosheet and application of preparation method
  • Preparation method of nitrogen-phosphorus co-doped carbon nanosheet and application of preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of nitrogen and phosphorus co-doped carbon nanosheets, comprising the following steps:

[0031] 1) Preparation of self-assembled melamine precursor: Weigh 6mmol melamine and add it to 10ml deionized water, stir evenly, add 910uL phytic acid dropwise, stir fully and stand still to obtain a white hydrogel, freeze-dry the product to obtain a white fluffy powder.

[0032] 2) Preparation of nitrogen-phosphorus co-doped carbon nanosheet material (N-P / CNS): put the self-assembled melamine precursor prepared in step 1) into a tube furnace, and heat it at 2 °C min under an argon atmosphere -1 The heating rate was raised to 700-1100°C and roasted for 2 hours to prepare nitrogen-phosphorus co-doped carbon nanosheets named N-P / CNS-700~N-P / CNS-1100, respectively.

Embodiment 2

[0034] A preparation method of nitrogen and phosphorus co-doped carbon nanosheets, comprising the following steps:

[0035] 1) Preparation of self-assembled melamine precursor: weigh melamine and add it to deionized water, stir evenly, add phytic acid dropwise, stir fully and stand still to obtain a white hydrogel, and freeze-dry the product to obtain a white fluffy powder. Wherein, the molar ratio of the melamine, phytic acid and water is 6:1:500.

[0036] 2) Preparation of nitrogen-phosphorus co-doped carbon nanosheet material (N-P / CNS): put the self-assembled melamine precursor prepared in step 1) into a tube furnace, -1 The heating rate was increased to 1000°C for 1.5h to prepare nitrogen and phosphorus co-doped carbon nanosheets.

Embodiment 3

[0038] A preparation method of nitrogen and phosphorus co-doped carbon nanosheets, comprising the following steps:

[0039] 1) Preparation of self-assembled melamine precursor: weigh melamine and add it to deionized water, stir evenly, add phytic acid dropwise, stir fully and stand still to obtain a white hydrogel, and freeze-dry the product to obtain a white fluffy powder. Wherein, the molar ratio of the melamine, phytic acid and water is 6:3:600.

[0040] 2) Preparation of nitrogen-phosphorus co-doped carbon nanosheet material (N-P / CNS): put the self-assembled melamine precursor prepared in step 1) into a tube furnace, -1 The heating rate was increased to 700°C for 2.5h to prepare nitrogen and phosphorus co-doped carbon nanosheets.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lattice spacingaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a nitrogen-phosphorus co-doped carbon nanosheet and application of the preparation method.Nitrogen-phosphorus co-doped carbon nanosheet catalyst material is prepared by: calcining at high temperature, template-free one-step self-assembled precursors: melamine and phytic acid.Oxygen reduction tests show that prepared N-P / CNS-1000 shows corrected initial potential and higher current density, represents four-electron transfer reaction, can match with commercial Pt / C and shows both excellent ethanol resistance and long-range stability in alkali solutions.

Description

technical field [0001] The invention belongs to the technical field of fuel cells, and in particular relates to a preparation method and application of nitrogen and phosphorus co-doped carbon nanosheets. Background technique [0002] Most of the oxygen reduction catalysts widely used in fuel cells are platinum-based noble metal or non-noble metal catalysts. Most of these metal catalysts have disadvantages such as high price and poor stability, which are not conducive to large-scale commercial application. Therefore, the development of inexpensive metal-free catalysts with high activity and high stability is one of the goals of researchers. Carbon nanomaterials are an ideal metal-free catalyst material because of their low cost, simple preparation, environmental friendliness, high activity and high stability, and easy modification. In recent years, a large number of documents have reported that the catalytic activity of carbon nanomaterials can be increased by means of hete...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/90B82Y30/00
CPCB82Y30/00H01M4/9083H01M8/1011Y02E60/50
Inventor 王宗花王晓涵夏建飞赵凯
Owner QINGDAO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More