Permeation type dyeing auxiliary for dyeing aramid fiber and preparation method of permeation type dyeing auxiliary

A technology of penetrating and dyeing aids, applied in the field of penetrating dyeing aids, can solve the problems of difficult dyeing of aramid fiber, and achieve the effect of easy dyeing and fiber protection

Active Publication Date: 2016-07-13
厦门谢田守望新材料有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of permeable dyeing aid for aramid fiber dyeing, this dyeing aid can effectively improve the dye uptake rate of aramid fiber, solve the problem that aramid fiber is difficult to dye, the dyeing effect is good, and to The structure of aramid fiber is not damaged, and the fiber after dyeing is soft and comfortable, with bright color and good gloss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Permeation type dyeing auxiliary for dyeing aramid fiber and preparation method of permeation type dyeing auxiliary

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A kind of penetrating dyeing aid for aramid fiber dyeing, in parts by weight, comprises the following components:

[0043] 5 parts of malic acid, 5 parts of sodium acetate,

[0044] 6 parts cysteine, 2 parts guar gum,

[0045] 10 parts of sodium alginate, 3 parts of dipropylene glycol dibenzoate,

[0046] 2 parts of castor oil polyoxyethylene ether, 1 part of pH regulator,

[0047] 2 parts of emulsifier, 10 parts of deionized water.

[0048] Its preparation method comprises the following steps:

[0049] (1) Mix and stir malic acid, sodium acetate, cysteine, sodium alginate and deionized water evenly to obtain mixed solution A;

[0050] (2) Mix and stir guar gum, dipropylene glycol dibenzoate, castor oil polyoxyethylene ether and deionized water evenly, add an emulsifier, and ultrasonicate for 2 hours at a power of 500W to obtain a mixed solution B;

[0051] (3) Mix the mixed solution A obtained in step (1) and the mixed solution B obtained in step (2) uniformly, ad...

Embodiment 2

[0053] A kind of penetrating dyeing aid for aramid fiber dyeing, in parts by weight, comprises the following components:

[0054] 12 parts of malic acid, 10 parts of sodium acetate,

[0055] 11 parts of cysteine, 6 parts of guar gum,

[0056] 15 parts of sodium alginate, 7 parts of dipropylene glycol dibenzoate,

[0057] 4 parts of castor oil polyoxyethylene ether, 2 parts of pH regulator,

[0058] 3 parts of emulsifier, 15 parts of deionized water.

[0059] Its preparation method comprises the following steps:

[0060] (1) Mix and stir malic acid, sodium acetate, cysteine, sodium alginate and deionized water evenly to obtain mixed solution A;

[0061] (2) Mix and stir guar gum, dipropylene glycol dibenzoate, castor oil polyoxyethylene ether and deionized water evenly, add an emulsifier, and ultrasonicate for 3 hours at a power of 800W to obtain a mixed solution B;

[0062] (3) Mix the mixed solution A obtained in step (1) and the mixed solution B obtained in step (2) uni...

Embodiment 3

[0064] A kind of penetrating dyeing aid for aramid fiber dyeing, in parts by weight, comprises the following components:

[0065] 10 parts of malic acid, 8 parts of sodium acetate,

[0066] 7 parts of cysteine, 2-6 parts of guar gum,

[0067] 12 parts of sodium alginate, 5 parts of dipropylene glycol dibenzoate,

[0068] 3.5 parts of castor oil polyoxyethylene ether,

[0069] 1.5 parts of pH regulator, 2 parts of emulsifier, 15 parts of deionized water.

[0070] Its preparation method comprises the following steps:

[0071] (1) Mix and stir malic acid, sodium acetate, cysteine, sodium alginate and deionized water evenly to obtain mixed solution A;

[0072] (2) Mix and stir guar gum, dipropylene glycol dibenzoate, castor oil polyoxyethylene ether and deionized water evenly, add an emulsifier, and ultrasonicate for 2.2 hours at a power of 600W to obtain a mixed solution B;

[0073] (3) Mix the mixed solution A obtained in step (1) and the mixed solution B obtained in step (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a permeation type dyeing auxiliary for dyeing aramid fiber. The permeation type dyeing auxiliary comprises the following components in parts by weight: 5-12 parts of malic acid, 5-10 parts of sodium acetate, 6-11 parts of cysteine, 2-6 parts of guar gum, 10-15 parts of sodium alginate, 3-7 parts of dipropylene glycol dibenzoate, 2-4 parts of castor oil polyoxyethylene ether, 1-2 parts of a pH adjusting agent, 2-3 parts of an emulsifier and 10-15 parts of deionized water. The invention further discloses a preparation method of the permeation type dyeing auxiliary. By adopting the permeation type dyeing auxiliary for dyeing aramid fiber, the dyeing rate of aramid fiber can be effectively increased, the problem that the aramid fiber is hard to dye is solved, the dyeing effect is good, the fiber structure of aramid fiber is not damaged, and the dyed fiber is soft and comfortable, bright in color and good in gloss. The preparation method is simple and the cost is low.

Description

Technical field: [0001] The invention relates to the field of dye auxiliaries, in particular to a penetrating dye auxiliaries for aramid fiber dyeing. Background technique: [0002] At present, the most widely used new type of special fiber is aramid fiber, a high-tech fiber invented and put into production by DuPont in the 1970s. Its macromolecules are generally long chains connected by amide groups and benzene rings, endowed with a stable skeleton structure; the fiber has excellent chemical stability, thermal stability, high strength and high modulus and other characteristics. Aramid Nomex fiber has a compact macromolecular structure, high crystallinity, high glass flower temperature, and no affinity group. Aramid fiber is dyed by conventional dyeing methods, and the dye is basically not dyed, so dyeing is very difficult. [0003] At present, the following two methods are mainly used to dye aramid fibers: one is to add dyes during spinning to directly produce excellent fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06P1/653D06P1/48D06P1/655D06P1/613D06P3/24
CPCD06P1/48D06P1/6136D06P1/6533D06P1/6553D06P3/24
Inventor 魏天堂
Owner 厦门谢田守望新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com