Novel electronic buffer packaging material and preparation method thereof
A packaging material and electronic cushioning technology, which is applied in the field of new electronic cushioning packaging materials and its preparation, can solve the problems of large manpower and material resources, poor polystyrene degradation ability, environmental pollution, etc., and achieve the effect of good elasticity and excellent cushioning performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0051] (1) Mix 20 parts of polyvinyl alcohol and 80 parts of water, and stir with a magnetic stirrer at a speed of 70r / min for 10 minutes;
[0052] (2) Add 20 parts of corn starch, 20 parts of potato starch, 20 parts of tapioca starch, 5 parts of ramie fiber and 2 parts of coconut shell fiber, and continue to stir at a speed of 70r / min for 5 minutes;
[0053] (3) Add 1 part of phosphatidylcholine, 0.1 part of potassium sorbate, 1 part of sodium bicarbonate, 4 parts of azodicarbonamide, 5 parts of epoxy soybean oil, 2 parts of dioctyl phthalate, glycerine 20 parts of alcohol and 1 part of ethanol were stirred for 10 minutes with a stirrer at a speed of 400r / min;
[0054] (4) Pour into the mold for pre-compression;
[0055] (5) Carry out cold pressing at a pressure of 10MPa by a cold press, and keep the pressure for 30 minutes;
[0056] (6) After drying, put it into a hot press and press it at a temperature of 170 ° C and a pressure of 2 MPa;
[0057] (7) Put it into a cold p...
Embodiment 2
[0059] (1) Mix 30 parts of polyvinyl alcohol and 90 parts of water, and stir for 15 minutes with a magnetic stirrer at a speed of 80 r / min;
[0060] (2) Add 22 parts of corn starch, 23 parts of potato starch, 22 parts of tapioca starch, 6 parts of ramie fiber and 3 parts of coconut shell fiber, and continue stirring at a speed of 80r / min for 10 minutes;
[0061] (3) Add 1.2 parts of phosphatidylcholine, 0.15 parts of potassium sorbate, 1.5 parts of sodium bicarbonate, 5 parts of azodicarbonamide, 6 parts of epoxy soybean oil, 3 parts of dioctyl phthalate, glycerine 25 parts of alcohol and 1.3 parts of ethanol were stirred for 15 minutes with a stirrer at a speed of 450 r / min;
[0062] (4) Pour into the mold for pre-compression;
[0063] (5) Carry out cold pressing at a pressure of 15 MPa by a cold pressing machine, and keep the pressure for 40 minutes;
[0064] (6) After drying, put it into a hot press and press it at a temperature of 180 ° C and a pressure of 3 MPa;
[006...
Embodiment 3
[0067] (1) Mix 35 parts of polyvinyl alcohol and 100 parts of water, and stir for 17 minutes with a magnetic stirrer at a speed of 85 r / min;
[0068] (2) Add 25 parts of corn starch, 25 parts of potato starch, 25 parts of tapioca starch, 7.5 parts of ramie fiber and 3.5 parts of coconut shell fiber, and continue to stir at a speed of 85r / min for 12 minutes;
[0069] (3) Add 1.5 parts of phosphatidylcholine, 0.2 parts of potassium sorbate, 2 parts of sodium bicarbonate, 6 parts of azodicarbonamide, 7.5 parts of epoxy soybean oil, 3.5 parts of dioctyl phthalate, glycerine 30 parts of alcohol and 1.5 parts of ethanol were stirred for 20 minutes with a stirrer at a rotating speed of 500r / min;
[0070] (4) Pour into the mold for pre-compression;
[0071] (5) Carry out cold pressing at a pressure of 15 MPa by a cold pressing machine, and keep the pressure for 45 minutes;
[0072] (6) After drying, put it into a hot press and press it at a temperature of 185 ° C and a pressure of 3...
PUM
Property | Measurement | Unit |
---|---|---|
Density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap