A kind of determination method of bulk method ABS solid content

A determination method and technology of solid content, which can be applied in the direction of removing a certain component and weighing, etc., to solve problems such as affecting the test results.

Active Publication Date: 2018-10-02
NORTH HUAJIN CHEM IND CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is the problem that residual monomers and a small amount of initiator in sample processing affect the test results in the existing ABS solid content analysis and testing technology, and a new method for measuring the solid content of ABS by bulk method is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of determination method of bulk method ABS solid content

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Weigh 1 g of a sample with a solid content of 30%, and add 10.1 g of a mixed solvent (5 g of toluene, 5 g of methyl ethyl ketone, and 0.1 g of hydroquinone) under stirring conditions. After the sample is completely dissolved, add the sample solution dropwise to 100 g of methanol liquid under strong stirring conditions. Mix well and then separate into layers, separate the polymer phase through a filter, then put the polymer phase and the filter together in an oven, place it at 100°C for 1 hour, then cool to room temperature, weigh the polymer mass, and calculate This gives a solids content of 30.5%.

Embodiment 2

[0029] Weigh 1 g of a sample with a solid content of 50%, and add 10.1 g of a mixed solvent (5 g of toluene, 5 g of methyl ethyl ketone, and 0.1 g of hydroquinone) under stirring conditions. After the sample is completely dissolved, add the sample solution dropwise to 100 g of methanol liquid under strong stirring conditions. Mix well and then separate into layers, separate the polymer phase through a filter, then put the polymer phase and the filter together in an oven, place it at 100°C for 1 hour, then cool to room temperature, weigh the polymer mass, and calculate This gives a solids content of 50.4%.

Embodiment 3

[0031] Weigh 4 g of a sample with a solid content of 70%, and add 50.1 g of a mixed solvent (25 g of toluene, 25 g of methyl ethyl ketone, and 0.1 g of hydroquinone) under stirring conditions. After the sample was completely dissolved, the sample solution was added dropwise to 500 g of methanol liquid under strong stirring conditions. Mix well and then separate into layers, separate the polymer phase through a filter, then put the polymer phase and the filter together in an oven, place it at 100°C for 1 hour, then cool to room temperature, weigh the polymer mass, and calculate This gives a solids content of 71.1%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for determining solid content of ABS by continuous bulk polymerization process. A sample is added into a certain amount of a mixed solvent with stirring, in order to dissolve more fully, a micro amount of hydroquinone or TBC (p-tert-Butylcatechol) is added; after the sample is completely dissolved with strong stirring, and the sample is added into a methanol solution drop by drop; the sample is allowed to stand after fully mixing for demixing, and a polymer phase is separated by filtering; the polymer and a filter are placed into a baking oven for drying, and the polymer and the filter are placed in a dryer for natural cooling at room temperature; mass of solids is weighed, and solid content of the sample is calculated. The method can effectively prevent the problem that monomers and a few initiators are remained after treatment of the sample, which can influence the test results.

Description

technical field [0001] The invention relates to the technical field of ABS production, in particular to a method for measuring the solid content of ABS by a bulk method, which can accurately measure the solid content of the bulk ABS. Background technique [0002] ABS resin refers to the graft copolymer of polybutadiene rubber, styrene and acrylonitrile. It has a complex two-phase structure, in which the matrix resin SAN is used as the continuous phase, and rubber is dispersed in the matrix resin in the form of particles as the dispersed phase. Due to the existence of the rubber phase, the performance of ABS resin has been significantly improved, and its own impact resistance can be increased several times or even ten times. With the characteristics of high impact resistance, high surface hardness, stable size, heat resistance, chemical resistance and good electrical properties, ABS resin is easy to form and has excellent machining performance. Products and other fields hav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N5/04
CPCG01N5/04
Inventor 王益波袁博胡世秋郝春波刘万胜吕天一周川李耀波范铁军李新杰聂中方张延涛王楠韩丽君朱勇飞魏尧
Owner NORTH HUAJIN CHEM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com