Preparation method for aluminum alloy shell and aluminum alloy shell
An aluminum alloy, aluminum alloy-based technology, applied in coatings, surface reaction electrolytic coatings, electrolytic coatings, etc., can solve the problems of low brightness on the surface of aluminum alloy shells, and achieve good color effects, excellent appearance quality, and brightness high effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0016] The preparation method of the aluminum alloy casing provided by the present invention comprises the following steps:
[0017] S1. Perform sandblasting treatment on the surface of the aluminum alloy substrate; the pressure of the sandblasting treatment is 0.18-0.25MPa, and the particle size of the sand material is 80-205 mesh;
[0018] S2. Carrying out chemical polishing treatment on the surface of the sandblasted aluminum alloy substrate; the chemical polishing treatment method is: at 90-100° C., polishing with polishing solution for 15-20 s;
[0019] S3. Perform anodic oxidation treatment on the surface of the chemically polished aluminum alloy substrate; the anodic oxidation treatment method is: under the conditions of 18-20°C and a voltage of 13-16V, in the presence of 180-200g / L sulfuric acid In the anodic oxidation electrolyte, anodic oxidation treatment is performed to obtain an anodic oxidation film with a thickness of 10-20 μm;
[0020] S4, polishing the surfac...
Embodiment 1
[0043] This embodiment is used to illustrate the aluminum alloy casing disclosed in the present invention and the preparation method thereof.
[0044] Using sand with a particle size of 180 mesh, the surface of the aluminum alloy substrate was sandblasted under a pressure of 0.20 MPa. The distance between the spray gun and the surface of the aluminum alloy substrate was 15 cm, and the feed rate was 1 m / min.
[0045] Then, the aluminum alloy substrate was alkali-etched in a 50 g / L sodium hydroxide solution at 55 °C for 20 s. Then, at 25°C, neutralization treatment was carried out in a nitric acid solution with a concentration of 20ml / L for 30s.
[0046] The aluminum alloy substrate was chemically polished for 15s using a mixed polishing solution with a mass ratio of phosphoric acid and sulfuric acid at 100°C of 3:1.
[0047] Then, the aluminum alloy substrate was neutralized in a nitric acid solution with a concentration of 20 ml / L at 25° C. for 20 s.
[0048] The chemically ...
Embodiment 2
[0053] This embodiment is used to illustrate the aluminum alloy casing disclosed in the present invention and the preparation method thereof.
[0054] Using sand with a particle size of 205 mesh, the surface of the aluminum alloy substrate was sandblasted under a pressure of 0.20 MPa. The distance between the spray gun and the surface of the aluminum alloy substrate was 35 cm, and the feed rate was 1 m / min.
[0055] Then, the aluminum alloy substrate was alkali-etched in a 58 g / L sodium hydroxide solution at 55 °C for 10 s. Then, at 25°C, neutralization treatment was carried out in a 30ml / L nitric acid solution for 20s.
[0056] The aluminum alloy substrate was chemically polished for 20s using a mixed polishing solution with a mass ratio of phosphoric acid and sulfuric acid at 95°C of 3:1.
[0057] Then, the aluminum alloy substrate was neutralized in a 30ml / L nitric acid solution at 25°C for 10s.
[0058] The chemically polished aluminum alloy substrate was anodized for 40...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com