Fluorescent inflaming-retarding multifunctional double-layer fabric and preparing method thereof

A double-layer fabric, multi-functional technology, applied in dyeing method, multi-strand fabric, textile and other directions, can solve the problems of difficult to meet safety protective clothing, single function, etc., achieve anti-splash of molten metal, simple preparation method, and promote development Effect

Active Publication Date: 2016-04-13
SHAANXI YUANFENG TEXTILE TECH RES
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a fluorescent flame-retardant multifunctional double-layer fabric, the surface of which can be dyed into fluorescent colors, and has the functions of flame retardancy, high temperature resistance, molten metal splash prevention, antistatic, high strength wear resistance, and pilling resistance and other high performance, which solves the problem that the existing fabric has a single function and is difficult to meet the needs of safety protective clothing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorescent inflaming-retarding multifunctional double-layer fabric and preparing method thereof
  • Fluorescent inflaming-retarding multifunctional double-layer fabric and preparing method thereof
  • Fluorescent inflaming-retarding multifunctional double-layer fabric and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Preparation of fluorescent flame-retardant multifunctional double-layer fabric:

[0053] Step 1, select the raw material fiber: select dyeable flame-retardant polyester filament with a yarn count of 150D for the surface layer, accounting for 40%, and use infusible aramid blended yarn for the inner layer, accounting for 60%. The specific proportion of the inner layer is 93% of aramid fiber 1313, 5% of aramid fiber 1414, and 2% of conductive fiber.

[0054] After fully mixing the fibers required for the inner layer above, pretreatment, cotton cleaning, carding, drawing, roving, spun yarn, and winding are sequentially performed to obtain a yarn count of 55 S / 2 Aramid 1313 / 1414 / Conductive Fiber 93 / 5 / 2 blended yarn. Among them, the cylinder speed is 330r / min, the licker-in speed is 750r / min, and the doffer speed is 38r / min. The total draft of the pre-merging is 6.8 times, and the draft of the back zone is 1.97 times; the total draft of the blending is 8.6 times, and the d...

Embodiment 2

[0060] Preparation of fluorescent flame-retardant multifunctional double-layer fabric:

[0061] Step 1, select the raw material fiber: the surface layer is made of 175D dyeable flame-retardant polyester filament, accounting for 46%, and the inner layer is made of infusible aramid blended yarn, accounting for 54%. The specific proportion of the inner layer is 90% of aramid fiber 1313, 8% of aramid fiber 1414, and 2% of conductive fiber.

[0062] After fully mixing the raw materials required for the above inner layer, pretreatment, cotton cleaning, carding, drawing, roving, spun yarn, and winding are sequentially performed to obtain a yarn count of 40 S / 2 Aramid 1313 / 1414 / Conductive Fiber 90 / 8 / 2 blended yarn. Among them, the cylinder speed is 330r / min, the licker-in speed is 750r / min, and the doffer speed is 38r / min. The total draft of the pre-merging is 6.8 times, and the draft of the back zone is 1.97 times; the total draft of the blending is 8.6 times, and the draft of the...

Embodiment 3

[0068] Preparation of fluorescent flame-retardant multifunctional double-layer fabric:

[0069] Step 1, select raw material fibers: use 200D dyeable flame-retardant polyester filaments for the surface layer, accounting for 42%, and use infusible aramid blended yarns for the inner layer, accounting for 58%. The specific proportion of the inner layer is 88% of aramid fiber 1313, 9% of aramid fiber 1414, and 3% of conductive fiber.

[0070] After fully mixing the fibers required for the inner layer above, pretreatment, cotton cleaning, carding, drawing, roving, spun yarn, and winding are sequentially performed to obtain a yarn count of 25 S / 2 Aramid 1313 / 1414 / Conductive Fiber 88 / 9 / 3 blended yarn. Among them, the cylinder speed is 330r / min, the licker-in speed is 750r / min, and the doffer speed is 38r / min. The total draft of the pre-merging is 6.8 times, and the draft of the back zone is 1.97 times; the total draft of the blending is 8.6 times, and the draft of the back zone is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fluorescent inflaming-retarding multifunctional double-layer fabric. The surface layer of the fabric is woven from inflaming-retarding yarn capable of being dyed with fluorescence color, and the inner layer of the fabric is woven from non-melting inflaming-retarding yarn incapable of being dyed with fluorescence color. The warps of the inner layer are lifted to be interwoven with the wefts of the surface layer to form a binding texture so that the two layers can be connected. The fabric is prepared in the way that the warps of the inner layer are lifted to be interwoven with the wefts of the surface layer to form the binding texture so that the two layers can be connected, and then dyeing treatment is conducted to generate the fluorescent inflaming-retarding multifunctional double-layer fabric. Specifically, the two layers of the fabric are connected in the way that when surface wefts are put in for surface layer weaving, all inner warps must sink to the space below a shed and can not be interwoven with surface wefts; when inner wefts are put in for inner layer weaving, all surface warps must be lifted and can not be interwoven with inner wefts. The double-layer fabric can have different spaces and can be used for making protection garments in a plurality of fields.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a fluorescent flame-retardant multifunctional double-layer fabric, and also relates to a preparation method of the fluorescent flame-retardant multifunctional double-layer fabric. Background technique [0002] With the continuous breakthrough of new materials and new technologies in my country, the safety technology of industrial textiles is developing towards internationalization, serialization, and comprehensive and multiple performance requirements. The development of safety protective clothing must realize the protection from a single risk factor to The comprehensive protection of multiple risk factors, therefore, the development of protective fabrics with multiple functions conforms to the development of my country's economy, and is of great significance to improving the personal safety protection capabilities of our country. [0003] For some special working env...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D11/00D03D15/12D03D13/00D06M15/333D06M13/224D06P1/16D06P3/54D06M101/32D06M101/36D03D15/283D03D15/47D03D15/513D03D15/533D03D15/547
CPCD03D11/00D03D13/008D06M13/2246D06M15/333D06P1/16D06P3/004D06P3/54D06M2200/40D06M2101/32D06M2101/36D10B2331/021D03D15/513
Inventor 丁小瑞樊争科常金赵雷
Owner SHAANXI YUANFENG TEXTILE TECH RES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com