A kind of microsphere catalyst and its preparation method and application

A catalyst, zeolite catalyst technology, applied in molecular sieve catalysts, chemical instruments and methods, physical/chemical process catalysts, etc., can solve problems such as weak coke adsorption capacity, small specific surface area, and easy clogging of catalyst apertures. The effect of large coke adsorption capacity and convenience for large-scale production

Active Publication Date: 2018-04-27
BEIJING HUASHI UNITED ENERGY TECH & DEV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the defects in the prior art that the catalyst aperture is easy to block, the specific surface area is small, and the ability to adsorb coke is weak in the suspension bed hydrogenation process, and then provide a microsphere catalyst and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of microsphere catalyst and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1, preparation microsphere catalyst:

[0037] 1) Crush 1000g of zeolite powder to a particle size of 0.4μm, then add 1000g of ethanol to it, mix well, and stir at 30°C for 10h to obtain a slurry;

[0038] 2) Spray-dry the slurry in step 1), the temperature of spray-drying is 50°C, and the time is 5h; then, it is formed into catalyst microspheres by using a ball press machine, and then pressed at 200MPa for 5min to finalize the shape; then the finalized The catalyst microspheres are placed in a vacuum degumming furnace for degumming. The degumming temperature is 1200°C and the time is 10h;

[0039] 3) Fe(NO 3 ) 3 9H 2 O, Ni(NO 3 ) 2 ·6H 2 O and Co(NO 3 ) 2Dissolved in water to obtain a metal impregnation solution, the total mass fraction is 30%, so that the mass ratio of Fe, Ni and Na in the metal impregnation solution is 8:2:3; The catalyst microspheres were immersed in the metal impregnating solution for 1 hour, and the impregnated catalyst microsph...

Embodiment 2

[0040] Embodiment 2, preparation microsphere catalyst:

[0041] 1) Crush 1000g of zeolite powder to a particle size of 0.4μm, then add 1500g of ethanol to it, mix well, and stir at 40°C for 8h to obtain a slurry;

[0042] 2) Spray-dry the slurry in step 1), the temperature of the spray-drying is 60°C, and the time is 8h; then use a ball press to form catalyst microspheres, and then press at 300MPa for 5min to shape; then shape the The catalyst microspheres are placed in a vacuum degumming furnace for degumming. The degumming temperature is 1000°C and the time is 6h;

[0043] 3) Fe(NO 3 ) 3 9H 2 O, Ni(NO 3 ) 2 ·6H 2 O and Co(NO 3 ) 2 Dissolved in water to obtain a metal impregnation solution, the total mass fraction is 20%, so that the mass ratio of Fe, Ni and Na in the metal impregnation solution is 2:1:1; The catalyst microspheres were immersed in the metal impregnation solution for 2 hours, and the impregnated catalyst microspheres were dried at 90° C. for 4 hours t...

Embodiment 3

[0044] Embodiment 3, preparation microsphere catalyst:

[0045] 1) Crush 1000g of zeolite powder to a particle size of 0.4μm, then add 3000g of ethanol to it, mix well, and stir at 50°C for 5h to obtain a slurry;

[0046] 2) Spray-dry the slurry in step 1), the temperature of the spray-drying is 75°C, and the time is 10h; then use a ball press to form catalyst microspheres, and then press at 150MPa for 5min to shape; then shape the The catalyst microspheres are placed in a vacuum degumming furnace for degumming. The degumming temperature is 1100°C and the time is 8h;

[0047] 3) Fe(NO 3 ) 3 9H 2 O, Ni(NO 3 ) 2 ·6H 2 O and Co(NO 3 ) 2 Dissolved in water to obtain a metal impregnation solution, the total mass fraction is 60%, so that the mass ratio of Fe, Ni and Na in the metal impregnation solution is 5:1:5; The catalyst microspheres were immersed in the metal impregnating solution for 3 hours, and the impregnated catalyst microspheres were dried at 130° C. for 3 hours...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a microspherical catalyst as well as a preparation method and an application thereof. The preparation method comprises the following steps: 1) mixing and stirring zeolite powder and ethyl alcohol so as to obtain slurry; 2) sequentially drying, forming, setting and sintering the slurry obtained in the step 1), thereby obtaining zeolite catalyst microspheres; and 3) impregnating the zeolite catalyst microspheres obtained in the step 2) into a metal impregnation liquid, and then drying the impregnated zeolite catalyst microspheres so as to obtain the microspherical catalyst. The preparation method is simple and convenient to operate; the prepared microspherical catalyst has high cracking performance, high desulfuration, denitrification and deoxygenation performance, high hydrogenation performance, high demetalization performance and high coke adsorption performance, and can be widely applied to heavy oil slurry bed hydrocracking process.

Description

technical field [0001] The invention belongs to the field of catalyst preparation in the hydrogenation process of heavy oil suspended bed, in particular to a microsphere catalyst and its preparation method and application, in particular to a microsphere catalyst used in the hydrogenation process of heavy oil suspension bed and its preparation method and application . Background technique [0002] With the rapid development of our country's economy, the consumption of oil has increased rapidly. my country's energy pattern is short of oil, low in gas, and rich in coal. From the national energy strategy, oil and gas are needed. Therefore, the lightening of heavy oil has attracted more and more attention. Among them, the suspended bed process of heavy oil is one of the most effective processes for lightening heavy oil. In the process of lightening heavy oil, various processing Use of Hydrogen Catalysts. [0003] Common residual oil hydrogenation catalysts use alumina as the c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J29/072B01J35/08C10G45/12C10G45/16
CPCB01J29/072B01J35/08B01J2229/18C10G45/12C10G45/16C10G2300/205C10G2300/70
Inventor 李林林科李春桃
Owner BEIJING HUASHI UNITED ENERGY TECH & DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com