Composite nanofiltration membrane and preparation method thereof

A composite nanofiltration membrane and combined technology, applied in chemical instruments and methods, membrane technology, semi-permeable membrane separation, etc., can solve the problem that nanofiltration membranes do not have antibacterial properties

Active Publication Date: 2016-03-30
CHINA PETROLEUM & CHEM CORP +1
View PDF10 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the defect that existing nanofiltration membranes do not possess antibacterial properties, and provide a composite nanofiltration membrane and a preparation method thereof, as well as the composite nanofiltration membrane and the composite nanofiltration membrane prepared by the method Application in the field of water treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite nanofiltration membrane and preparation method thereof
  • Composite nanofiltration membrane and preparation method thereof
  • Composite nanofiltration membrane and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The present invention also provides a kind of preparation method of composite nanofiltration membrane, and this method comprises the following steps:

[0032] (1) dissolving a hydroxyl-containing polymer and a silane coupling agent containing a structure shown in formula (I) in a solvent to prepare a coating solution;

[0033] (2) coating the coating solution on the support layer to form an initial film;

[0034] (3) immerse the supporting layer formed with the initial film in step (2) into a solution containing a crosslinking agent and a crosslinking catalyst to carry out a crosslinking reaction to obtain a crosslinked network structure comprising the supporting layer and the surface of the supporting layer Composite nanofiltration membrane;

[0035]

[0036] Among them, Y is a linear or branched alkyl group containing C1-C20, and the end of the linear or branched alkyl group is a quaternary amine group; X is Cl, methoxy (OMe), ethoxy (OEt), OC 2 h 4 OCH 3 , OS...

Embodiment 1

[0064] This embodiment is used to illustrate the composite nanofiltration membrane provided by the present invention and its preparation method.

[0065] Dissolve 1.0g of polyvinyl alcohol (PVA), 0.8g of dimethyloctadecyl [3-(trimethoxysilyl) propyl]ammonium chloride in 100g of deionized water, and then drop into 1mol / L of dilute hydrochloric acid to adjust the pH of the solution to 1. At room temperature, after stirring for 24 hours, filter to obtain a clear coating solution;

[0066] After coating the dilute coating solution evenly on the polysulfone bottom membrane, put it into an oven at 60°C and heat it for 30 minutes to ensure that the solvent is completely evaporated; , 10 g of formaldehyde and 15 g of sodium sulfate, heated at 60° C. for 30 min, took out the composite nanofiltration membrane, washed it with water, and soaked it in deionized water.

[0067] After soaking the obtained composite nanofiltration membrane in water for 24 hours, the water flux and desalina...

Embodiment 2

[0071] This embodiment is used to illustrate the composite nanofiltration membrane provided by the present invention and its preparation method.

[0072] Dissolve 1.0 g of chitosan and 1.0 g of dimethyloctadecyl [3-(trimethoxysilyl) propyl] ammonium chloride in 100 g of deionized water, and then drop into 1 mol / L dilute hydrochloric acid to adjust the pH of the solution to 1. At room temperature, after stirring for 24 hours, filter to obtain a clear coating solution;

[0073] After coating the dilute coating solution evenly on the polysulfone bottom membrane, put it into an oven at 60°C and heat it for 30 minutes to ensure that the solvent is completely evaporated; , 10g of formaldehyde and 15g of sodium sulfate, heated at 50°C for 30min, then took out the composite nanofiltration membrane, washed it with water and soaked it in deionized water.

[0074] After soaking the obtained composite nanofiltration membrane in water for 24 hours, the water flux and desalination rate we...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a composite nanofiltration membrane and a preparation method thereof and application of the composite nanofiltration membrane prepared by the preparation method in the field of water treatment. The composite nanofiltration membrane comprises a support layer and a separation layer which are stacked together, wherein the separation layer is a cross-linked net structure formed by dissolving of a polymer containing a hydroxyl group and a silane coupling agent containing a structure as shown in formula (I) in a solvent for sol-gel and thermal crosslinking reaction, the cross-linked net structure is located on the surface of the support layer, Y is a C2-C10 linear or branched chain alkyl group, the terminal end of the C2-C10 linear or branched chain alkyl group is quaternary ammonium group, and X is one or more of Cl, OMe, OEt, OC2H4OCH3, OSiMe3 and OAc. The composite nanofiltration membrane has a high salt removing rate and water permeability (water flux), also has strong antibacterial property, is simple in preparation method, and has great prospects for industrial application.

Description

technical field [0001] The invention relates to a composite nanofiltration membrane and a preparation method thereof. Background technique [0002] Nanofiltration is a pressure-driven membrane separation process between reverse osmosis and ultrafiltration. The pore size of the nanofiltration membrane is in the range of several nanometers. Or multivalent ions and organic matter with a molecular weight between 200 and 500 have a higher removal rate. It can be widely used in fresh water softening, seawater softening, drinking water purification, water quality improvement, oil-water separation, waste water treatment and recycling, as well as the classification, purification and concentration of chemical products such as dyes, antibiotics, polypeptides and polysaccharides. [0003] The separation characteristics of nanofiltration membranes cannot be replaced by reverse osmosis membranes and ultrafiltration membranes, and they also have the characteristics of high efficiency and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D71/70B01D69/12B01D67/00C02F1/44
Inventor 张杨刘轶群潘国元严昊郭敏
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com