Method for manufacturing antiskid bamboo-wood composite boards
A manufacturing method and technology of composite boards, which are applied in the jointing of wooden veneers, manufacturing tools, and humidity-adjusting wood, etc., can solve the problems of lower raw material utilization, high cost, and single materials, so as to enhance self-adjusting ability and overcome Unstable size, scientific and reasonable structure
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031] A kind of manufacture method of antiskid bamboo-wood composite board, comprises the following steps:
[0032] (1) Material selection: Bamboo materials can be selected from moso bamboo, miscellaneous bamboo, small-caliber bamboo or processed bamboo scraps, and wood can be selected from poplar, willow or wood processed scraps;
[0033] (2) Drying: first put the raw material on a natural drying site, and when it is air-dried to a moisture content of 35%, it is sent into a drying kiln for forced drying. The humidity in the drying kiln is controlled to be 80%, and the time is 5 to 6 days. The temperature of the day is 50°C-60°C, and maintain a daily temperature increase rate of 10°C until the temperature reaches 100°C to reduce the moisture content to 10%;
[0034] (3) rolling: the bamboo after step (2) is degreened, the wood is peeled, and mechanically rolled into bamboo and wood blanks;
[0035] (4) Drying again: the bamboo and wooden blanks after mechanical rolling are p...
Embodiment 2
[0040] A kind of manufacture method of antiskid bamboo-wood composite board, comprises the following steps:
[0041] (1) Material selection: Bamboo materials can be selected from moso bamboo, miscellaneous bamboo, small-caliber bamboo or processed bamboo scraps, and wood can be selected from poplar, willow or wood processed scraps;
[0042] (2) Drying: first put the raw material on a natural drying place, and when it is air-dried to a moisture content of 35%, it is sent into a drying kiln for forced drying. The humidity in the drying kiln is controlled to be 90%, and the time is 5 to 6 days. The temperature of the day is 50°C to 60°C, and maintain a daily temperature increase rate of 10°C until the temperature reaches 100°C, reducing the moisture content to 11%;
[0043] (3) rolling: the bamboo after step (2) is degreened, the wood is peeled, and mechanically rolled into bamboo and wood blanks;
[0044] (4) Drying again: the bamboo and wooden blanks after mechanical rolling a...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com