Manufacturing method for novel solid wood composite plate special for door pocket

A technology of solid wood composite and production method, which is applied to the jointing of wooden veneers, chemical instruments and methods, manufacturing tools, etc., which can solve the problems of poor nail holding force, poor flatness, and environmental protection, and achieve cool insulation Effect, good waterproof performance, and prolonging the service life

Inactive Publication Date: 2016-02-10
HARBIN SHENGSHI HUALIN TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims at the current door cover panels made of solid wood boards, solid wood splicing panels, finger-jointed panels, and door cover panels made of wood-based panels that are not environmentally friendly and have nail-holding power. Not good, not moisture-proof, poor flatness, deformation, warping, cracking and other problems, the production method of a new type of special board for solid wood composite door covers is provided, which can better solve the above problems, using scientific and technological production methods and unique The structure took the lead in breaking through the above technical problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method for novel solid wood composite plate special for door pocket
  • Manufacturing method for novel solid wood composite plate special for door pocket
  • Manufacturing method for novel solid wood composite plate special for door pocket

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A method for making a special board for a novel solid wood composite door cover, characterized in that it includes the following steps:

[0041] The first step: First, the logs are cooked and softened, and the wood pulp is physically treated;

[0042] The second step: miniaturize the logs and cut them into thin boards;

[0043] The third step: veneer drying;

[0044] Step 4: Trim the edges of the thin wood boards and splice them into a whole board with a patchwork machine, then grade the whole board again, separate the panels and core materials, and all layers are thin wood boards with longitudinal grain, arranged into multi-layer boards, Apply glue on the surface that needs to be bonded; Ordinary plywood can be arranged vertically and horizontally according to needs; It can also be arranged with more vertical and less horizontal structures according to needs;

[0045] Step 5: Press the multi-layer veneer with a hot press through high temperature and high ...

Embodiment 2

[0052] In the first step, the first step is to soften the logs by cooking and softening the logs. First, soak the logs in water at 25-35°C for 6-10 hours, and then steam the water with steam at 1.5-3 atmospheres; The second step is to carry out miniaturization treatment to make thin wood boards, which is to slice or peel the logs into thin boards. Firstly, put the logs on the planer or rotary cutter, adjust the speed, adjust the thickness to 1.8-2mm, and cut the logs into thin boards. 1.8-2mm thin wood board.

Embodiment 3

[0054] In the third step, the veneer is dried by a special process, and the selected veneer is dried by a hot-press drying method; In the press, after heating and pressing, the pressure is adjusted to 1mpa, the temperature is adjusted to be within 100°C, and the pressure is reset to zero after 30-60 seconds of pressing. Repeat several times to stabilize the moisture content of the veneer at 6-12 %within.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method for a novel solid wood composite plate special for a door pocket. The manufacturing method comprises the following steps: performing softening physical treatment on raw wood; performing miniaturizing treatment on the raw wood to make the raw wood into thin wood plates; drying the thin wood plates with a special process; splicing the thin wood plates into an integrated plate, forming panels and core materials, arranging the panels and the core materials into all-longitudinal multi-layer plate structures, and printing glue; pressing the all-longitudinal multi-layer plate structures into an all-longitudinal multi-layer plate by using a hot press, and optimizing the wood material by adopting scientific pressure, compression ratio and compression time; enabling the all-longitudinal multi-layer plate to experience a unique curing period so that the solid wood multi-layer plate is more stable and non-deformable; cutting the four edges of the solid wood multi-layer plate, sanding the solid wood multi-layer plate by using a sanding machine, and fixing the thickness; sawing the longitudinal solid wood multi-layer plate into multi-layer plate strips, wherein the widths of the multi-layer plate strips are determined as required and are consistent with the thickness of an anti-deformation solid wood multi-layer laminated plate; coating the natural texture surfaces of the multi-layer plate strips with the glue, enabling the multi-layer plate strips coated with the glue to be perpendicular to a work surface, and placing the multi-layer plate strips coated with the glue into an automatic plate splicing machine (namely, the multi-layer plate strips are used vertically); pressurizing, performing high-frequency treatment, heating automatically, and performing one-time forming to form an anti-deformation solid wood multi-layer laminated plate; sawing the four edges, sanding, and fixing the thickness, wherein the overall surface of the spliced anti-deformation solid wood multi-layer laminated plate is the cross section of the multi-layer plate; adhering density plates to the two surfaces of the anti-deformation solid wood multi-layer laminated plate. According to the technology, anti-deformation deepening treatment is further performed on the basis of the anti-deformation solid wood multi-layer laminated plate, so that the internal stress of the wood material is eliminated to the greatest extent, and the difficult problems of deformation, crack and warpage of the wood material are really solved.

Description

technical field [0001] The invention relates to a method for producing a door cover board, in particular to a method for making a new type of special board for a solid wood composite door cover. Background technique [0002] Solid wood door cover panels have natural defects, color difference, stammering, deformation, cracking and other phenomena. In this field, industries, colleges, experts, scholars, and wood processing factories have conducted in-depth research and development, and invented solid wood splicing panels and finger joints. Although the problem of stuttering and deformation has been better solved, the deformation and cracking have not been solved because of the high price caused by the lack of resources in our country; blockboard, MDF, particle board, plywood and other products; so far they are still not environmentally friendly and grippy. Nail strength is not good, not moisture-proof, flatness is not good, deformation, warping, cracking are very serious, it c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B27D1/08B27D1/10B32B37/12B32B37/06B32B37/10
Inventor 张福贵
Owner HARBIN SHENGSHI HUALIN TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products